Abstract: Tires using high tensile reinforcement with value of at least 1240 N(280 lbs) for U+T type cord and at least 2000 N(450 lbs) for bunched type cord.

Abstract: Steel reinforcing cords (36) having four or more filaments (38, 40, 42 and 44) in two groups, one twisted and the other untwisted with a filament tensile strength TS equal to K.sub.1 -K.sub.2 D where K.sub.1 =4080N/mm.sup.2, and D is a filament diameter in mm to form cords with a break load equal to N(720.40D.sup.2 -352.6D.sup.3 ; CE is the cord efficiency, D is the filament diameter in millimeters and N is the number of filaments.

Abstract: The present process comprising the steps of:(1) heating a steel wire to a temperature which is within the range of approximately 850.degree. C. to about 1050.degree. C. for a period of at least about 2 seconds; wherein said steel wire is comprised of a microalloyed high carbon steel which consists essentially of about 97.03 to about 98.925 weight percent iron, from about 0.72 to about 0.92 weight percent carbon, from about 0.3 to about 0.8 weight percent manganese, from about 0.05 to about 0.4 weight percent silicon, and from about 0.005 to about 0.85 weight percent of at least one member selected from the group consisting of chromium, vanadium, nickel, and boron, with the proviso that the total amount of silicon, manganese, chromium, vanadium, nickel, and boron in the microalloyed high carbon steel is within the range of about 0.7 to 0.9 weight percent;(2) continuously cooling the steel wire at a cooling rate of less than 100.degree. C.

Abstract: Tires using high tensile reinforcement with values of at least 1240 N (280 lbs) for U+T type cord and at least 2000 N (450 lbs) for bunched type cord.