Abstract: The invention encompasses the process for the preparation of a cross-linked aramid polymer comprising the step of heating a non-crosslinked polymer comprising the repeating unit of formula (I) at a temperature comprised of from 150 to 400° C. for a period of time comprised of from 1 second to 20 minutes, wherein A and B are independently selected from meta-phenylene and para-phenylene, and R1 and R2 are independently selected from H and N3, with the proviso that at least one of R1 and R2 is N3 and R1 and R2 are attached to any of the positions 1, 2, 3, or 4 in para-phenylene and 1, 2, 3 in meta-phenylene; and the obtained cross-linked aramid polymer.

Abstract: The invention encompasses the process for the preparation of a cross-linked aramid polymer comprising the step of heating a non-crosslinked polymer comprising the repeating unit of formula (I) at a temperature comprised of from 150 to 400° C. for a period of time comprised of from 1 second to 20 minutes, wherein A and B are independently selected from meta-phenylene and para-phenylene, and R1 and R2 are independently selected from H and N3, with the proviso that at least one of R1 and R2 is N3 and R1 and R2 are attached to any of the positions 1, 2, 3, or 4 in para-phenylene and 1, 2, 3 in meta-phenylene; and the obtained cross-linked aramid polymer.

Abstract: A process for obtaining a hydroxy-ended glycidyl azide polymer (GAP). The process consists in reacting polyepichlorohydrin (PECH) with a metallic azide in the presence of an organic solvent having a parameter of solubility comprised between 21 and 23.5 (MPa).sup.1/2 such as DMA or NMP. The use of any of the solvents mentioned sharply reduces the reaction time needed for substituting azide groups for the chlorine present in the PECH. Said reaction times can be less than 4 hours when NMP is used or less than 6 hours when DMA is used. The GAP thus obtained having a functionality equal to or above 2 can be used as energetic bonding agent in the formulation of solid propellants for rockets.