Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The foundry binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3) until a foundry mix is to be created, where said parts by weight are based upon 100 parts of the binder system.

Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3) until a foundry mix is to be created, where said parts by weight are based upon 100 parts of the binder system.

Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3) until a foundry mix is to be created, where said parts by weight are based upon 100 parts of the binder system.

Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.

Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.

Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.

Abstract: A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.