Abstract: A hot-rolled wire rod excelling in wire drawability is provided, in which breakage can be suppressed even in heavy work from a large diameter. A hot-rolled wire rod contains C: 0.35 to 0.65% (percent by mass, hereinafter expressed as well), Si: 1.4 to 3.0%, Mn: 0.10 to 1.0%, Cr: 0.1 to 2.0%, P: 0.025% or less (exclusive of 0%), S: 0.025% or less (exclusive of 0%), N: 0.006% or less (exclusive of 0%), Al: 0.1% or less (exclusive of 0%), and O: 0.0030% or less (exclusive of 0%), with the remnant consisting of Fe and inevitable impurities; wherein the content of hydrogen in steel is 2.50 ppm (ppm by mass, hereinafter expressed as well) or less, and hardness (HV) is 460×C00.1 or less (C0 indicates the content of C (percent by mass) in a position of depth of D/4 (D: diameter of the wire rod)).

Abstract: The steel wire material for a spring of the invention contains; C: 0.37-0.54%, Si: 1.7-2.30%, Mn: 0.1-1.30%, Cr: 0.15-1.1%, Cu: 0.15-0.6%, Ti: 0.010-0.1%, Al: 0.003-0.05%, and the balance including iron with inevitable impurities, wherein ferrite decarburized layer depth is 0.01 mm or less, whole decarburized layer depth is 0.20 mm or less, and fracture reduction of area is 25% or more. It alternately may contain; C: 0.38-0.47%, Si: 1.9-2.5%, Mn: 0.6-1.3%, Ti: 0.05-0.15%, Al: 0.003-0.1%, and the balance including iron with inevitable impurities, wherein ferrite decarburized layer depth is 0.01 mm or less.

Abstract: The steel wire material for a spring of the invention contains; C: 0.37-0.54%, Si: 1.7-2.30%, Mn: 0.1-1.30%, Cr: 0.15-1.1%, Cu: 0.15-0.6%, Ti: 0.010-0.1%, Al: 0.003-0.05%, and the balance including iron with inevitable impurities, wherein ferrite decarburized layer depth is 0.01 mm or less, whole decarburized layer depth is 0.20 mm or less, and fracture reduction of area is 25% or more. It alternately may contain; C: 0.38-0.47%, Si: 1.9-2.5%, Mn: 0.6-1.3%, Ti: 0.05-0.15%, Al: 0.003-0.1%, and the balance including iron with inevitable impurities, wherein ferrite decarburized layer depth is 0.01 mm or less, Ceq1 in the equation (1) below is 0.580 or more, Ceq2 in the equation (2) below is 0.49 or less, and Ceq3 in the equation (3) below is 0.570 or less. Ceq1=[C]+0.11[Si]?0.07[Mn]?0.05[Ni]+0.02[Cr]??(1) Ceq2=[C]+0.30[Cr]?0.15[Ni]?0.70[Cu]??(2) Ceq3=[C]?0.04[Si]+0.24[Mn]+0.10[Ni]+0.20[Cr]?0.89[Ti]?1.92[Nb]??(3) (In the above equations, [ ] shows the content (mass %) of each element in steel.

Abstract: The steel wire material for a spring of the invention contains; C: 0.37-0.54%, Si: 1.7-2.30%, Mn: 0.1-1.30%, Cr: 0.15-1.1%, Cu: 0.15-0.6%, Ti: 0.010-0.1%, Al: 0.003-0.05%, and the balance including iron with inevitable impurities, wherein ferrite decarburized layer depth is 0.01 mm or less, whole decarburized layer depth is 0.20 mm or less, and fracture reduction of area is 25% or more. It alternately may contain; C: 0.38-0.47%, Si: 1.9-2.5%, Mn: 0.6-1.3%, Ti: 0.05-0.15%, Al: 0.003-0.1%, and the balance including iron with inevitable impurities, wherein ferrite decarburized layer depth is 0.01 mm or less, Ceq1 in the equation (1) below is 0.580 or more, Ceq2 in the equation (2) below is 0.49 or less, and Ceq3 in the equation (3) below is 0.570 or less. Ceq1=[C]+0.11[Si]?0.07[Mn]?0.05[Ni]+0.02[Cr]??(1) Ceq2=[C]+0.30[Cr]?0.15[Ni]?0.70[Cu]??(2) Ceq3=[C]?0.04[Si]+0.24[Mn]+0.10[Ni]+0.20[Cr]?0.89[Ti]?1.92[Nb]??(3) (In the above equations, [ ] shows the content (mass %) of each element in steel.

Abstract: A hot-rolled wire rod excelling in wire drawability is provided, in which breakage can be suppressed even in heavy work from a large diameter. A hot-rolled wire rod contains C: 0.35 to 0.65% (percent by mass, hereinafter expressed as well), Si: 1.4 to 3.0%, Mn: 0.10 to 1.0%, Cr: 0.1 to 2.0%, P: 0.025% or less (exclusive of 0%), S: 0.025% or less (exclusive of 0%), N: 0.006% or less (exclusive of 0%), Al: 0.1% or less (exclusive of 0%), and O: 0.0030% or less (exclusive of 0%), with the remnant consisting of Fe and inevitable impurities; wherein the content of hydrogen in steel is 2.50 ppm (ppm by mass, hereinafter expressed as well) or less, and hardness (HV) is 460×C00.1 or less (C0 indicates the content of C (percent by mass) in a position of depth of D/4 (D: diameter of the wire rod)).

Abstract: A spring steel wire rod according to the present invention is a spring steel wire rod wherein: the spring steel wire rod contains C: 0.35% to 0.7% (by mass, the same is hereunder applied), Si: 1.5% to 2.50%, Mn: 0.05% to 1.0%, Cr: 0.05% to 1.9%, Cu: 0.05% to 0.7%, Ni: 0.15% to 0.8%, P: 0.02% or less (excluding 0%), S: 0.02% or less (excluding 0%); and the balance being Fe and unavoidable impurities, wherein the ratio of Si to Cu (Si/Cu) is in the range of 4 or more; and the difference between the concentration of Cu in the surface layer and the concentration of Cu in the steel is 0.50% or less and the difference between the concentration of Ni in the surface layer and the concentration of Ni in the steel is 1.00% or less. The present invention makes it possible to improve pickling performance in a spring steel wire rod containing Si abundantly and further Cr, Cu, and Ni.