Abstract: A tooth whitening composition includes a whitening component; a metal ion chelator; water; and polyalcohol, the weight ratio of the water and the polyalcohol being, water:polyalcohol=3.5:1 to 20:1, and also, the total amount of the water and the polyalcohol, in the composition, being greater than or equal to 50 wt. % and less than or equal to 85 wt. %.

Abstract: According to one aspect of the present invention, a hardenable putty used for impression taking includes an inorganic filler at 60% by mass or greater and 85% by mass or less, wherein consistency of the hardenable putty is greater than or equal to 35, and wherein a median diameter of the inorganic filler is greater than or equal to 5 ?m and less than or equal to 50 ?m on a weight basis.

Abstract: A tooth whitening composition includes a whitening component; a metal ion chelator; water; and polyalcohol, the weight ratio of the water and the polyalcohol being, water:polyalcohol=3.5:1 to 20:1, and also, the total amount of the water and the polyalcohol, in the composition, being greater than or equal to 50 wt. % and less than or equal to 85 wt. %.

Abstract: Provided is a filler for dental glass ionomer cements, the filler to a surface of which a compound(s) having a carboxyl group(s) is/are bound via a silicon atom, for the purpose of providing: a filler suitable for dental glass ionomer cements that can provide a hardened cement having a high strength by being mixed with a dental glass ionomer cement composition, the filler that can be easily manufactured from a general inorganic powder as a raw material; and a manufacturing method of the filler for dental glass ionomer cements. The manufacturing method includes binding a carboxylic acid having an unsaturated double bond(s) exclusive of a (meth)acrylate compound to an inorganic powder whose surface is treated with a silane coupling agent having an unsaturated double bond(s).

Abstract: Provided is a fluoroaluminosilicate glass powder that can provide a dental glass ionomer cement hardened body excellent in acid resistance, the glass powder including sodium and potassium which have an effect of lowering the reflective index of glass. A mass ratio of potassium to sodium in the component is in the range of from 1.2 to 1.9 in terms of oxide.

Abstract: Provided is a fluoroaluminosilicate glass powder that can provide a dental glass ionomer cement hardened body excellent in acid resistance, the glass powder including sodium and potassium which have an effect of lowering the reflective index of glass. A mass ratio of potassium to sodium in the component is in the range of from 1.2 to 1.9 in terms of oxide.

Abstract: Provided is a dental glass ionomer cement composition whose hardened cement has a high strength, despite not including a (meth)acrylate monomer. The dental glass ionomer cement composition includes a filler in which a compound(s) having a carboxyl group(s) is/are bound to a surface of an inorganic powder via a silicon atom, the composition not including a (meth)acrylate monomer.

Abstract: Provided is a filler for dental glass ionomer cements, the filler to a surface of which a compound(s) having a carboxyl group(s) is/are bound via a silicon atom, for the purpose of providing: a filler suitable for dental glass ionomer cements that can provide a hardened cement having a high strength by being mixed with a dental glass ionomer cement composition, the filler that can be easily manufactured from a general inorganic powder as a raw material; and a manufacturing method of the filler for dental glass ionomer cements. The manufacturing method includes binding a carboxylic acid having an unsaturated double bond(s) exclusive of a (meth)acrylate compound to an inorganic powder whose surface is treated with a silane coupling agent having an unsaturated double bond(s).

Abstract: [Problems to be Solved] To provide fluoroaluminosilicate glass powder enabling to improve acid resistance of dental glass ionomor cement and a production method thereof. [Solution] A lanthanum compound eluted in the presence of polycarboxylic acid and water exists only in a surface layer of a fluoroaluminosilicate glass powder. An amount of the fluoroaluminosilicate glass powder is preferably 1 to 5% by weight in terms of oxide. The fluoroaluminosilicate glass powder is produced by mixing an aqueous solution of a lanthanum compound and a fluoroaluminosilicate glass powder not containing lanthanum, and heating them. The aqueous solution of lanthanum compound is an aqueous solution of a water solvable lanthanum compound, preferably an aqueous solution of lanthanum nitrite and/or an aqueous solution of lanthanum chloride.

Abstract: A polymerizable composition that comprises a first component comprising a (meth)acrylate and an organic peroxide as an oxidizing agent and a second component comprising a (meth)acrylate and a cysteine as a reducing agent which has a partial structure represented by the following structural formula, the first component and/or the second component further comprising a polymerization promoter:

Abstract: [Problems to be Solved] To provide fluoroaluminosilicate glass powder enabling to improve acid resistance of dental glass ionomor cement and a production method thereof. [Solution] A lanthanum compound eluted in the presence of polycarboxylic acid and water exists only in a surface layer of a fluoroaluminosilicate glass powder. An amount of the fluoroaluminosilicate glass powder is preferably 1 to 5% by weight in terms of oxide. The fluoroaluminosilicate glass powder is produced by mixing an aqueous solution of a lanthanum compound and a fluoroaluminosilicate glass powder not containing lanthanum, and heating them. The aqueous solution of lanthanum compound is an aqueous solution of a water solvable lanthanum compound, preferably an aqueous solution of lanthanum nitrite and/or an aqueous solution of lanthanum chloride.

Abstract: A polymerizable composition that comprises a first component comprising a (meth)acrylate and an organic peroxide as an oxidizing agent and a second component comprising a (meth)acrylate and a cysteine as a reducing agent which has a partial structure represented by the following structural formula, the first component and/or the second component further comprising a polymerization promoter:

Abstract: To provide an organic and inorganic composite filler which gives excellent surface smoothness similar to that of a natural tooth, low polymerization shrinkage, high X-ray imaging property and high mechanical strength to a dental restoration material composite, an organic and inorganic composite filler used for a dental restoration material is produced by curing and pulverizing a (meth)acrylate compound including 50 to 80% by weight of a glass powder having a maximum particle diameter of 5 ?m or less, an average particle diameter from 0.05 to 2 ?m, and X-ray imaging property, and 10 to 40% by weight of a metal compound having an average particle diameter from 0.005 to 0.3 ?m and X-ray imaging property at the maximum of 90% by weight in total, where the organic and inorganic composite filler has preferably an average particle diameter from 10 to 30 ?m.

Abstract: To provide a dental restorative material composition using an organic-inorganic composite filler having excellent surface smoothness like a natural tooth, low polymerization shrinkage, excellent X-ray contrast imaging property, similar transparency to that of a natural tooth, and no variation of transparency before and after the composition is hardened, the dental restorative material composition includes (a) a (meth)acrylate monomer, (b) an organic-inorganic composite filler having an average particle diameter of 5 to 50 ?m which is made by mixing a (meth)acrylate monomer and a fine particle filler having an average primary particle diameter of 0.005 to 0.3 ?m and having X-ray impermeability, (c) a fine particle filler having an average primary particle diameter of 0.005 to 0.04 ?m, and (d) a photopolymerization initiator.

Abstract: To provide a dental restorative material composition using an organic-inorganic composite filler having excellent surface smoothness like a natural tooth, low polymerization shrinkage, excellent X-ray contrast imaging property, similar transparency to that of a natural tooth, and no variation of transparency before and after the composition is hardened, the dental restorative material composition includes (a) a (meth)acrylate monomer, (b) an organic-inorganic composite filler having an average particle diameter of 5 to 50 ?m which is made by mixing a (meth)acrylate monomer and a fine particle filler having an average primary particle diameter of 0.005 to 0.3 ?m and having X-ray impermeability, (c) a fine particle filler having an average primary particle diameter of 0.005 to 0.04 ?m, and (d) a photopolymerization initiator.

Abstract: To provide a base material for a prosthesis having abrasion resistance and aesthetic appreciation more than equivalent to those of a conventional artificial tooth and to make a bridge and an artificial tooth for a partial denture easily in a short time without cutting adjacent teeth, the base material is made of a resin material, and comprises only a part having a form approximating to a lingual side surface part of the teeth being at the oral cavity side from a mucous of a dental cervix, two to four teeth may be connected, a thickness of the lingual side surface part is 0.5 mm or more from the lingual side surface and less than 0.5 mm from a labial surface of a teeth form being made finally, a surface contacting with a mucous surface of the dental cervix is formed and an engaging part connecting with a resin material built on a labial side surface is formed.

Abstract: To provide a prosthesis like an artificial tooth capable of forming the bridge directly and having abrasion resistance and aesthetic equivalent to or more than those of a conventional artificial tooth in a short time and without cutting proximal teeth, said prosthesis is made of a resin material and comprises one tooth or teeth connected two to four teeth, which are approximating to the teeth at the oral cavity side from a mucous of a dental cervix part, and recessed parts are formed at proximal surfaces of its both sides, and further, a part where some at the labial surface side is deleted in the thickness almost corresponding to the thickness of an enamel in a natural tooth and a part where some at the occlusal surface side is deleted in the thickness almost corresponding to the thickness of an enamel in a natural tooth, may be formed.

Abstract: A crown prosthesis having a wear resistance and an aesthetic property that are equivalent to those of the conventional hard resin, and being able to be fixed inside the oral cavity in a short time to form a dental prosthesis, without necessity of careful formation of an abutment tooth under consideration of the shape and the structure of the dental prosthesis to be produced later. It also offers no necessity of indirect production of the dental prosthesis outside the oral cavity, the crown prosthesis comprising a polymer of a mixture of a polymerizable compound having an unsaturated double bond, a filler and a polymerization initiator, and having an outer shape resembling a tooth and a space to be filled with a dental composite resin between an inner surface thereof and an abutment tooth, preferably having a thickness of 0.1 to 2 mm, and having, in its inside space, a protrusion having a slot or a hole, for engaging or inserting a post implanted on a tooth root of a remaining tooth.

Abstract: A light irradiation apparatus for a dental photo polymerization composite resin of multi-purpose type which can efficiently and completely polymerize and cure the dental photo polymerization composite resin using a combination of the camphor quinone and the tertiary amine as the photo polymerization catalyst, and can also polymerize and cure the dental photo polymerization composite resin using the acylphosphine oxide as the newly developed photo polymerization initiator. with a structure such that there are arranged a blue ray radiation LED 5 having luminous wavelengths peaked at a wavelength of 450 nm or more but not more than 490 nm, and a near ultraviolet rays and/or violet rays radiation LED 6 having luminous wavelengths peaked at a wavelength of 370 nm or more but less than 410 nm, and there is provided a circuit changing switch 7 at least for simultaneously turning on these two kinds of LEDs 5, 6 and for turning on only the near ultraviolet rays and/or violet rays radiation LED 6.

Abstract: A prosthesis for a tooth surface, which requires neither careful formation of an abutment tooth nor indirect production of the dental prosthesis outside the oral cavity, and can be fixed inside the oral cavity in a time, the prosthesis having a shape resembling a labial side surface of an anterior tooth, a buccal side surface and an approximal surface or an occlusal surface of a molar tooth, or a buccal surface or an approximal surface and an occlusal surface of a molar tooth, a back surface thereof being attached to a lingual side tooth formed by constructing with a lingual side tooth forming resin material on an abutment tooth, and comprising a polymer of a mixture of a polymerizable compound having an unsaturated double bond, a filler and a polymerization initiator. The prosthesis may be a veneering type having a thickness of 0.