Abstract: A process for the preparation of an ethylene polymer including the step of polymerizing ethylene or copolymerizing ethylene and one or more other olefins in the presence of a Phillips-type chromium catalyst in a gas-phase polymerization reactor containing a reactor bed of particulate polymer, wherein the gas-phase polymerization reactor is equipped with a cycle gas line, wherein the reactor gas returned to the polymerization reactor through the cycle gas line has been condensed in part and the amount of liquid in the returned reactor gas is from 0.5 wt. % to 10 wt. % based upon the total weight of the reactor gas/liquid composition, the polymerization is carried out at from 108° C. to 125° C., and an aluminum alkyl is fed into the polymerization reactor in an amount in the range of from 0.0025 mole to 0.1 mole per ton of dosed ethylene.

Abstract: The invention relates to a polyethylene molding composition having a multimodal molar mass distribution particularly suitable for blow molding films having a thickness in the range from 8 to 200 ?m. The molding composition has a density at a temperature of 23° C. in the range from 0.953 to 0.960 g/cm3 and an MFR190/5 of the final product after extrusion in the range from 0.10 to 0.50 dg/min. The composition comprises from 30 to 60% by weight of a first ethylene polymer fraction made of a homopolymer A having a first molecular weight, from 22 to 40% by weight of a second ethylene polymer fraction made of a further homopolymer or first copolymer B of ethylene and at least one first comonomer from the group of olefins having from 4 to 8 carbon atoms, the first copolymer B having a second molecular weight higher than the first molecular weight, and from 10 to 30% by weight of a third ethylene polymer fraction made of a second copolymer C having a third molecular weight higher than the second molecular weight.

Abstract: A polyethylene composition having the following features: 1) density from about 0.945 to about 0.955 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from about 23 to about 40; 3) MIF from about 8.5 to about 18 g/10 min.; 4) HMWcopo index from about 3.5 to about 20; and 5) long-chain branching index, LCBI, equal to or greater than about 0.45. The polyethylene composition can be used to produce pipes and films.

Abstract: A polyethylene composition made from or containing a polyethylene, having the following features: 1) a density from about 0.930 to about 0.945 g/cm3, determined according to ISO 1183 at 23° C.; 2) a ratio of MIF/MIP from about 10 to less than about 30; 3) a MIF from about 3 to about 25 g/10 min.; 4) a Mz equal to or greater than about 1,500,000 g/mol; and 5) a long-chain branching index, LCBI, equal to or lower than about 0.55, wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having the about same molecular weight of 1,000,000 g/mol.

Abstract: The present disclosure provides a gas-phase polymerization process for preparing polyethylene, wherein halogenated alcohols in combination with a Ti based catalyst component and aluminum alkyls as co-catalyst suppress ethane formation or increase polymerization activity.

Abstract: A polyethylene composition having the following features: 1) density from about 0.945 to about 0.951 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from about 25 to about 43; 3) MIF from about 3.5 to less than about 8.5 g/10 min.; 4) HMWcopo index from about 1 to about 40; and 5) long-chain branching index, LCBI, equal to or greater than about 0.83. The polyethylene composition can be used to produce pipes.

Abstract: A slurry polymerization process for the preparation of polyethylene in a reactor cascade of two or more polymerization reactors including the steps of feeding to a polymerization reactor amounts of ethylene, of a Ziegler catalyst, of fresh aluminum alkyl and of a diluent; feeding the slurry product withdrawn from the polymerization reactor to a second polymerization reactor; and feeding additional amounts of ethylene and of diluent wherein the ethylene is first passed through an ethylene purification unit, which reduces at least the concentration of carbon monoxide, carbon dioxide, oxygen, acetylene and water contained in the ethylene, before it is fed to the two or more polymerization reactors of the reactor cascade.

Abstract: A process for starting a multizone circulating reactor containing no polyolefin particles, comprising the steps of conveying gas through the reactor and the gas recycle line, feeding a particulate material comprising a polymerization catalyst and optionally polyolefin into the reactor, controlling the gas flow in a vertical reactor zone equipped with a throttling valve at the bottom so that the upwards gas velocity in the bottom part of this reaction zone is lower than the terminal free-fall velocity of the particulate material fed into the reactor, and, after the weight of the particulate polyolefin in this reactor zone is higher than the drag force of the upward moving gas, controlling the circulation rate of the polymer particles within the multizone circulating reactor by adjusting the opening of the throttling valve and adjusting the flow rate of a dosing gas.

Abstract: A polyethylene composition having the following features: 1) density from about 0.945 to about 0.958 g/cm3, determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from about 20 to about 43; 3) MIF from about 4.0 to less than about 8.5 g/10 min.; 4) HMWcopo index from about 3.5 to about 20; and 5) long-chain branching index, LCBI, equal to or lower than about 0.82. The polyethylene composition can be used to produce blown films.

Abstract: Polyethylene composition with improved balance of impact resistance at low temperatures and Environmental Stress Cracking Resistance (ESCR), particularly suited for producing protective coatings on metal pipes, said composition having the following features: 1) density from 0.938 to 0.948 g/cm3; 2) ratio MIF/MIP from 15 to 25; 3) MIF from 30 to 45 g/10 min.; 4) Mz equal to or greater than 1000000 g/mol; 5) LCBI equal to or greater than 0.55.

Abstract: A process for preparing a polyolefin, including polymerizing olefins in the presence of an antistatic agent made from or containing an alkylene oxide derived polymer made from or containing in average from about 10 to about 200 repeating units —(CH2—CHR—O)— with R being hydrogen or an alkyl group having from 1 to 6 carbon atoms, wherein the alkylene oxide derived polymer is a random copolymer of ethylene oxide and other alkylene oxides and a ratio of n:m is in the range of from 6:1 to 1:1, wherein (n) is the average number of repeating units —(CH2—CH2—O)— derived from ethylene oxide and (m) is the average number of repeating units —(CH2—CHR?—O)— derived from the other alkylene oxides with R? being an alkyl group having from 1 to 6 carbon atoms, and the end groups of the alkylene oxide derived polymer are —OH groups.

Abstract: The present disclosure relates to a continuous process for the preparation of ethylene homopolymers or ethylene copolymers comprising polymerizing ethylene or copolymerizing ethylene and one or more other olefins in the presence of a chromium catalyst in a gas-phase polymerization reactor which is equipped with a cycle gas line for withdrawing reactor gas from the reactor, leading the reactor gas through a heat-exchanger for cooling and feeding the reactor gas back to the reactor, wherein the polymerization is carried out at a temperature from 30° C. to 130° C. and a pressure of from 0.1 to 10 MPa and an aliphatic carboxylic acid ester having from 8 to 24 carbon atoms is added.

Abstract: A process for preparing a polyolefin, including polymerizing olefins in the presence of an antistatic agent made from or containing an alkylene oxide derived polymer made from or containing in average from about 10 to about 200 repeating units —(CH2—CHR—O)— with R being hydrogen or an alkyl group having from 1 to 6 carbon atoms, wherein the alkylene oxide derived polymer is a random copolymer of ethylene oxide and other alkylene oxides and a ratio of n:m is in the range of from 6:1 to 1:1, wherein (n) is the average number of repeating units —(CH2—CH2—O)— derived from ethylene oxide and (m) is the average number of repeating units —(CH2—CHR?—O)— derived from the other alkylene oxides with R? being an alkyl group having from 1 to 6 carbon atoms, and the end groups of the alkylene oxide derived polymer are —OH groups.

Abstract: The present disclosure generally relates to a slurry polymerization process for the preparation of polyethylene in the presence of a Ziegler catalyst and aluminum alkyl co-catalyst in at least one polymerization reactor, in which process suspension medium comprising a concentration of aluminum alkyl co-catalyst is recycled to the polymerization, the concentration of aluminum alkyl co-catalyst in the recycled suspension medium is determined; and the amount of fresh aluminum alkyl co-catalyst fed to the polymerization is adjusted to maintain a targeted aluminum alkyl co-catalyst concentration in the recycled suspension medium.

Abstract: A polyethylene composition made from or containing a polyethylene, having the following features: 1) a density from about 0.930 to about 0.945 g/cm3, determined according to ISO 1183 at 23° C.; 2) a ratio of MIF/MIP from about 30 to about 55; 3) a MIF from about 3 to about 25 g/10 min.; 4) a Mz equal to or greater than about 1,500,000 g/mol; and 5) a long-chain branching index, LCBI, equal to or lower than about 0.55, wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having about the same molecular weight of 1,000,000 g/mol.

Abstract: A slurry polymerization process for the preparation of polyethylene in a reactor cascade of two or more polymerization reactors including the steps of feeding to a polymerization reactor amounts of ethylene, of a Ziegler catalyst, of fresh aluminum alkyl and of a diluent; feeding the slurry product withdrawn from the polymerization reactor to a second polymerization reactor; and feeding additional amounts of ethylene and of diluent wherein the ethylene is first passed through an ethylene purification unit, which reduces at least the concentration of carbon monoxide, carbon dioxide, oxygen, acetylene and water contained in the ethylene, before it is fed to the two or more polymerization reactors of the reactor cascade.

Abstract: A process for the gas-phase polymerization of ethylene or a mixture of ethylene and one or more 1 olefins in the presence of a polymerization catalyst system comprising the steps a) feeding a solid catalyst component, which was obtained by contacting at least a magnesium compound and a titanium compound, to a continuously operated apparatus and contacting the solid catalyst component with an aluminum alkyl compound at a temperature of from 0° C. to 70° C. in a way that the mean residence time of the solid catalyst component in contact with the aluminum alkyl compound is from 5 to 300 minutes; b) transferring the catalyst component formed in step a) into another continuously operated apparatus and prepolymerizing it with ethylene or a mixture of ethylene and one or more 1 olefins in suspension at a temperature of from 10° C. to 80° forming polymer in an amount of from 0.

Abstract: A process for the preparation of polyolefins by polymerizing olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst and an antistatically acting composition in a polymerization reactor, wherein the antistatically acting composition is a mixture comprising an oil-soluble surfactant and water and the use of an antistatically acting composition comprising an oil-soluble surfactant and water as antistatic agent for the polymerization of olefins at temperatures of from 20 to 200° C. and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst.

Abstract: A polyethylene composition made from or containing a polyethylene, having the following features: 1) a density from about 0.930 to about 0.945 g/cm3, determined according to ISO 1183 at 23° C.; 2) a ratio of MIF/MIP from about 30 to about 55; 3) a MIF from about 3 to about 25 g/10 min.; 4) a Mz equal to or greater than about 1,500,000 g/mol; and 5) a long-chain branching index, LCBI, equal to or lower than about 0.55, wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having about the same molecular weight of 1,000,000 g/mol.

Abstract: A polyethylene composition made from or containing a polyethylene, having the following features: 1) a density from about 0.930 to about 0.945 g/cm3, determined according to ISO 1183 at 23° C.; 2) a ratio of MIF/MIP from about 10 to less than about 30; 3) a MIF from about 3 to about 25 g/10 min.; 4) a Mz equal to or greater than about 1,500,000 g/mol; and 5) a long-chain branching index, LCBI, equal to or lower than about 0.55, wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having the about same molecular weight of 1,000,000 g/mol.