Abstract: The invention concerns a composition comprising a mixture of zinc sulphide (ZnS) and molybdenum sulphide (MoSx), in which the Mo/Zn molar ratio is in the range 0.01 to 1.9. The invention also pertains to a process for its preparation as well as to its application in photocatalysis and more particularly to its application in photocatalysis for the production of dihydrogen from water (H2O) and/or hydrogen sulphide (H2S) and/or any other source of protons in the presence of a source emitting in the ultraviolet and/or visible spectrum.

Abstract: The invention concerns a composition comprising a mixture of zinc sulphide (ZnS) and molybdenum sulphide (MoSx), in which the Mo/Zn molar ratio is in the range 0.01 to 1.9. The invention also pertains to a process for its preparation as well as to its application in photocatalysis and more particularly to its application in photocatalysis for the production of dihydrogen from water (H2O) and/or hydrogen sulphide (H2S) and/or any other source of protons in the presence of a source emitting in the ultraviolet and/or visible spectrum.

Abstract: The invention concerns a process for preparing metallic nanoparticles with an anisotropic nature by using two different reducing agents, preferably with different reducing powers, on a source of a metal selected from columns 8, 9 or 10 of the periodic table of the elements.

Abstract: The invention concerns a process for preparing metallic nanoparticles with an anisotropic nature by using two different reducing agents, preferably with different reducing powers, on a source of a metal selected from columns 8, 9 or 10 of the periodic table of the elements.

Abstract: The invention relates to a process for preparation of anisotropic metallic nanoparticles comprising at least: a) One stage that is brought into contact with an aqueous solution that comprises at least one source of a metal that is selected from the columns 8, 9 or 10 of the periodic table and at least one soluble surfactant, b) One stage for formation of anisotropic metallic nanoparticles of at least one of said metals, by adding at least one reducing agent to the solution that is obtained in stage a), c) Said particles are: c1) separated from liquid and optionally dried, or c2) deposited on a substrate by impregnation with the suspension obtained in stage b) or after resuspension of the nanoparticles that are obtained at the end of stage c1), whereby the substrate is an oxide of unordered texture, and after separation of the possible residual liquid, the material that is obtained is dried at a temperature that is less than or equal to 120° C.