Abstract: The invention provides a process for the heat treatment of steel products, in particular of steel strips or sheets, in which the product is brought from a starting temperature to a target temperature in a booster zone having at least one burner; the burner is operated with a fuel, in particular a fuel gas, and an oxygen-containing gas which contains more than 21% oxygen; and the product is brought into direct contact with the flame generated by the burner, the air ratio ? within the flame being set as a function of the starting temperature and/or the target temperature.

Abstract: A method for hot dip coating a flat stainless steel product with more than 5 wt. % Cr with a protective metallic coating by: heating the flat steel product under an oxygen-free heating atmosphere to 100° C.-600° C. within 1-30 seconds; continuing heating to a holding temperature of 750° C.-950° C., by heating to 550° C.-800° C. under an inert or reducing atmosphere, holding within this temperature window for 1 to 15 seconds under an oxidizing atmosphere, and continuing heating under an inert or reducing atmosphere, until the holding temperature is reached; holding at the holding temperature for 10-120 seconds under a reducing atmosphere; and passing the flat steel product through a nozzle area under an inert or reducing atmosphere at 430°-780° C. and into a molten bath in which the flat steel product is coated with the metallic coating.

Abstract: A method for hot dip coating a flat stainless steel product with more than 5 wt. % Cr with a protective metallic coating by: heating the flat steel product under an oxygen-free heating atmosphere to 100° C.-600° C. within 1-30 seconds; continuing heating to a holding temperature of 750° C.-950° C., by heating to 550° C.-800° C. under an inert or reducing atmosphere, holding within this temperature window for 1 to 15 seconds under an oxidising atmosphere, and continuing heating under an inert or reducing atmosphere, until the holding temperature is reached; holding at the holding temperature for 10-120 seconds under a reducing atmosphere; and passing the flat steel product through a nozzle area under an inert or reducing atmosphere at 430°-780° C. and into a molten bath in which the flat steel product is coated with the metallic coating.

Abstract: The invention provides a process for the heat treatment of steel products, in particular of steel strips or sheets, in which the product is brought from a starting temperature to a target temperature in a booster zone having at least one burner; the burner is operated with a fuel, in particular a fuel gas, and an oxygen-containing gas which contains more than 21% oxygen; and the product is brought into direct contact with the flame generated by the burner, the air ratio ? within the flame being set as a function of the starting temperature and/or the target temperature.

Abstract: A thin sheet is coated by hot dip galvanization with a zinc based alloy comprising 3.5% to 15% by weight of aluminum. Immediately after solidification of the coating, the thin sheet is heated for 2 to 10 seconds to a temperature 20 to 100° C. above the melting point of the coating. The thin sheet is then cooled to room temperature.

Abstract: The invention relates to a device for blowing off excessive coating material, especially fluid zinc or aluminium, in the coating of metal bands. The device comprises a blowing off jet impinged on compressed air, of which the jet bodies 3,4 are fixed at a base body 1. The jet lips 3,4 adjustable against each other form a jet slit 10 extending in transverse direction of the metal band. For optimizing an adaption of the slit thickness respectively the pressure of the blowing off medium along the band width it is provided to build the blowing off jet as a jet row, providing in transverse direction of the band at least two partial jets 2 to impinge seperately on a blowing off medium, especially compressed air, sealed against each other, of which the respective partial slits are adjacent forming a continuous jet slit (10).