Abstract: A para-aramid fibrid film is disclosed that has at least 95% of the bonds of the polymer are para-oriented. A method for making said para-aramid fibrid film by (a) polymerizing a para-oriented aromatic diamine and a para-oriented aromatic dicarboxylic acid halide to an aramid polymer having only para-oriented bonds in a mixture of solvents consisting of N-methylpyrrolidone or dimethylacetamide and calcium chloride or lithium chloride to obtain a dope wherein the polymer is dissolved in the mixture of solvents and the polymer concentration is 2 to 6 wt. %, and (b) converting the dope to para-aramid fibrid film is also described.

Abstract: Aramid fibrils having in the wet phase a Canadian Standard Freeness (CSF) value less than 100 ml, after drying a specific surface area (SSA) less than 7 m2/g, and a weight weighted length for particles having a length >250 ?m (WL 0.25) less than 1.2 mm, are described. A method of preparing the fibrils includes the steps (a) polymerizing an aromatic diamine and an aromatic dicarboxylic acid halide to an aramid polymer, in a mixture of N-methylpyrrolidone or dimethylacetamide and calcium chloride or lithium chloride to obtain a dope wherein the polymer is dissolved in the mixture and the polymer concentration is 2 to 6 wt. %, (b) converting the dope to fibrils by using a jet spin nozzle under a gas stream, and (c) coagulating the fibrils using a coagulation jet.

Abstract: A para-aramid fibrid film is disclosed that has at least 95% of the bonds of the polymer are para-oriented. A method for making said para-aramid fibrid film by (a) polymerizing a para-oriented aromatic diamine and a para-oriented aromatic dicarboxylic acid halide to an aramid polymer having only para-oriented bonds in a mixture of solvents consisting of N-methylpyrrolidone or dimethylacetamide and calcium chloride or lithium chloride to obtain a dope wherein the polymer is dissolved in the mixture of solvents and the polymer concentration is 2 to 6 wt. %, and (b) converting the dope to para-aramid fibrid film is also described.

Abstract: Aramid fibrils having in the wet phase a Canadian Standard Freeness (CSF) value less than 100 ml, after drying a specific surface area (SSA) less than 7 m2/g, and a weight weighted length for particles having a length >250 ?m (WL 0.25) less than 1.2 mm, are described. A method of preparing the fibrils includes the steps (a) polymerizing an aromatic diamine and an aromatic dicarboxylic acid halide to an aramid polymer, in a mixture of N-methylpyrrolidone or dimethylacetamide and calcium chloride or lithium chloride to obtain a dope wherein the polymer is dissolved in the mixture and the polymer concentration is 2 to 6 wt. %, (b) converting the dope to fibrils by using a jet spin nozzle under a gas stream, and (c) coagulating the fibrils using a coagulation jet.