Abstract: The present invention relates to a process for the preparation of a hydroxy-amino polymer, comprising the steps: a) reacting an H-functional starter compound carrying at least one Zerewitinoff-active H atom with an unsaturated cyclic carboxylic acid anhydride and at least one alkylene oxide compound to give a hydroxyl-group-carrying prepolymer, b) adding a primary amine and/or ammonia to the double bonds of the hydroxyl-group-carrying prepolymer obtained according to step a) to give the hydroxy-amino polymer, wherein the reaction of the H-functional starter compound with the unsaturated cyclic carboxylic acid anhydride and/or the addition of the alkylene oxide compound is carried out using a double metal cyanide catalyst (DMC catalyst). The invention relates additionally to a hydroxy-amino polymer obtainable by the above-mentioned process, wherein the ratio of the amount of alkylene oxide compound to the amount of carboxylic acid anhydride is at least 1.

Abstract: The invention relates to composite elements comprising a thermoplastic polymer and an adjacent polyurethane bonded thereto, to a process for production thereof and to the use thereof.

Abstract: The invention relates to stable emulsions for the production of foams based on isocyanate, at least comprising three polyols A1a, A1b and A1c as well as at least one physical blowing agent T, wherein A1a is a polyether polyol obtained by addition of epoxides to starter compounds selected from carbohydrates and di- or higher-functional alcohols, A1b is a polyether polyol started on an aromatic amine, and A1c is a polyester polyol obtained by esterification of a polycarboxylic acid component and a polyalcohol component, wherein the total amount of aromatic dicarboxylic acid derivatives used in the esterification, calculated on the basis of the free aromatic dicarboxylic acids and based on the total mass of polyalcohol component and polycarboxylic acid component, is less than or equal to 48.5% by mass.

Abstract: The present invention relates to homogeneous extruded articles made from thermoplastically processable polyurethanes based on polyester diols formed from succinic acid and 1,3-propanediol.

Abstract: The invention provides a process for producing rigid polyurethane-polyisocyanurate foams using polyols having a high proportion of secondary hydroxyl end groups. The invention further relates to the rigid polyurethane-polyisocyanurate foams thus obtainable and to the use thereof in the production of composite elements from rigid polyurethane-polyisocyanurate foams and suitable outer layers. The invention further provides the composite elements thus obtainable.

Abstract: The invention relates to composite elements comprising a thermoplastic polymer and an adjacent polyurethane bonded thereto, to a process for production thereof and to the use thereof.

Abstract: The present invention relates to high-value polyurethane (PUR) and polyurethaneurea elastomers, which can be processed in a particularly simple manner by use of low-viscosity prepolymers based on naphthalene 1,5-diisocyanate, and to a process for production thereof.

Abstract: Light-stable, sinterable, thermoplastic polyurethanes with improved blooming behavior and good thermal stability as well as good technical processability are produced from an aliphatic diisocyanate using one or more chain extenders corresponding to a specified formula. These polyurethanes are particularly useful in the production of molded articles, particularly molded articles for automotive interiors.

Abstract: A process for the preparation of polyricinoleic acid esters comprising the step of reaction of ricinoleic acid with an alcohol component which comprises mono- and/or polyfunctional alcohols having a molecular weight of ?32 g/mol to ?40 g/mol, wherein the reaction is carried out at least partly in the presence of a catalyst. The amount of catalyst, based on the total weight of the ricinoleic acid and the alcohol component, is in a range of from ?10 ppm to ?100 ppm. The reaction is ended when the acid number of the reaction product obtained is ?5 mg of KOH/g to ?100 mg of KOH/g. The invention furthermore relates to a polyurethane polymer, in particular a flexible polyurethane foam, which is obtainable using these polyricinoleic acid esters.

Abstract: Polyester polyols are produced from at least one carboxylic acid hydride and diethylene glycol by a process in which the formation of 1,4-dioxane is suppressed. These polyester polyols are useful for producing polyurethane (PUR) and polyisocyanurate (PIR) foams and metal composite elements containing these PUR or PIR foams.

Abstract: The present invention relates to a process for the preparation of polyether carbonate polyols with primary hydroxyl end groups, comprising the steps of reaction of a starter compound containing active hydrogen atoms with an epoxide and carbon dioxide under double metal cyanide catalysis, reaction of the product obtained with a cyclic carboxylic acid anhydride and reaction of this product obtained with ethylene oxide in the presence of a catalyst which contains at least one nitrogen atom per molecule, excluding non-cyclic tertiary amines with identical substituents. The invention furthermore relates to polyether carbonate polyols obtainable by this process, compositions comprising these polyether carbonate polyols and polyurethane polymers based on these polyether carbonate polyols.

Abstract: The present invention relates to a process for the preparation of polyricinoleic acid ester polyols having primary hydroxyl end groups. It furthermore relates to polyricinoleic acid ester polyols obtainable according to the invention and polyurethane polymers prepared using these polyols. The process comprises the steps: a) polycondensation of ricinoleic acid until a hydroxyl number of >0 mg of KOH/g to <60 mg of KOH/g is reached; and b) reaction of the product obtained in step a) or of a secondary product of the product obtained in step a) comprising carboxyl groups with an epoxide of the general formula (I), wherein R1 represents hydrogen, an alkyl radical or an aryl radical, with the proviso that >80% by weight to <100% by weight, based on the total amount of the epoxide (I) employed, is ethylene oxide and the reaction is carried out in the presence of an amine as the catalyst.

Abstract: The present invention relates to a method for producing flexible polyurethane foams, wherein a polyol component which comprises polyricinoleic acid esters is used as starting substance. The flexible polyurethane foams according to the invention have a bulk density according to DIN EN ISO 3386-1-98 in the range of ?10 kg/m3 to ?150 kg/m3, preferably ?20 kg/m3 to ?70 kg/m3, and in general their compressive strength according to DIN EN ISO 3386-1-98 is in the range of ?0.5 kPa to ?20 kPa (at 40% deformation and 4th cycle). The polyricinoleic acid esters are obtainable by the reaction of ricinoleic acid with an alcohol component which comprises mono- and/or polyhydric alcohols with a molecular mass of ?32 g/mol to ?400 g/mol, the reaction being carried out at least in part in the presence of a catalyst.

Abstract: The present invention relates to a reaction system for preparing polyurethane microcellular foam, a polyurethane microcellular foam and the use thereof. The reaction system for preparing polyurethane microcellular foam comprises isocyanate prepolymer, polyols, catalysts and chain extenders. The isocyanate prepolymer is a reaction product of polyisocyanates and polyester polyols, wherein the polyester polyols comprise 10-60 wt. % succinic acid units, based on 100 wt. % of the polyester polyols, the NCO content of the isocyanate prepolymer is 13-30 wt. %, based on 100 wt. % of isocyanate prepolymer. By using the reaction components provided in the present invention, the demould time for preparing the polyurethane microcellular foam can be reduced. The obtained polyurethane microcellular foam, which possesses good physical and mechanical properties, is particularly suitable to prepare shoes.

Abstract: The invention relates to the production and use of polyester polyols, formed from at least one carboxylic acid anhydride and ethylene glycol, wherein a specialized reaction control substantially suppresses the formation of 1,4-dioxane from diethylene glycol.

Abstract: Polyester polyols are produced by reacting terephthalic acid with a glycol corresponding to the formula H—(OCH2CH2)n—OH and an aliphatic dicarboxylic acid. These polyester polyols are particularly useful for the production of polyurethane) (PUR) and polyurethane/polyisocyanurate (PUR/PIR) foams for use in insulation applications.

Abstract: The invention relates to polyisocyanate polyaddition products, to a method for producing same, and to the use thereof.

Abstract: The invention relates to a process for the preparation of carbon nanotubes having hydroxyalkyl ester groups by reacting carbon nanotubes which have carboxylic acid groups with one or more epoxides, and to dispersions and materials which contain the carbon nanotubes functionalized thus.

Abstract: The present invention relates to a hydrogel on the basis of polyurethane or polyurethane urea, said hydrogel comprising hydrolysable functional groups in the polymer chain, to a method for producing the hydrogel and to the use of the hydrogel as adhesion barriers.

Abstract: The present invention relates to high-quality polyurethane and polyurethane urea elastomers which exhibit unique combinations of processing characteristics, oxidation resistance, mechanical and mechanical/dynamic properties in particularly demanding applications. These polyurethane elastomers and polyurethane urea elastomers are based on novel polycarbonate polyols.