Abstract: Moldings based on pyrogenically produced mixed oxide having the following physicochemical parameters: External diameter 0.8-25 mm BET surface area 5-400 m2/g Pore Volume 0.2-1.8 ml/g Fracture strength 5 to 350 N Composition At least two oxides selected from the group SiO2, Al2O3, TiO 2 and ZrO2 in any desired combination but with the exception of SiO2/Al2O3 mixed oxides, in which > 75 wt. % of SiO2 is present. Other constituents <1 wt. % Bulk density 250-1500 g/l, are produced by homogenizing pyrogenically produced mixed oxide as desired with one or more compounds from the group methylcellulose, methylhydroxyethylcellulose, wax, polyethylene glycol, magnesium stearate and/or aluminium stearate with addition of water, drying the product at a temperature of 70-150° C.