Abstract: A first impurity region is formed by ion implantation through a first opening formed in a mask layer. By depositing a spacer layer on an etching stop layer on which the mask layer has been provided, a mask portion having the mask layer and the spacer layer is formed. By anisotropically etching the spacer layer, a second opening surrounded by a second sidewall is formed in the mask portion. A second impurity region is formed by ion implantation through the second opening. An angle of the second sidewall with respect to a surface is 90°±10° across a height as great as a second depth. Thus, accuracy in extension of an impurity region can be enhanced.

Abstract: A method of cleaning a SiC semiconductor includes the steps of forming an oxide film at the surface of a SiC semiconductor, and removing the oxide film. At the step of forming an oxide film, an oxide film is formed using ozone water having a concentration greater than or equal to 30 ppm. The forming step preferably includes the step of heating at least one of the surface of the SiC semiconductor and the ozone water. Thus, there can be obtained a method of cleaning a SiC semiconductor that can exhibit cleaning effect on the SiC semiconductor.

Abstract: A method for manufacturing a semiconductor device includes the steps of: preparing a substrate made of silicon carbide; forming, on one main surface of the substrate, a detection film having a light transmittance different from that of silicon carbide; confirming presence of the substrate by applying light to the detection film; and forming an active region in the substrate whose presence has been confirmed.

Abstract: The present invention provides a silicon carbide substrate, an epitaxial layer provided substrate, a semiconductor device, and a method for manufacturing the silicon carbide substrate, each of which achieves reduced on-resistance. The silicon carbide substrate is a silicon carbide substrate having a main surface, and includes: a SiC single-crystal substrate formed in at least a portion of the main surface; and a base member disposed to surround the SiC single-crystal substrate. The base member includes a boundary region and a base region. The boundary region is adjacent to the SiC single-crystal substrate in a direction along the main surface, and has a crystal grain boundary therein. The base region is adjacent to the SiC single-crystal substrate in a direction perpendicular to the main surface, and has an impurity concentration higher than that of the SiC single-crystal substrate.

Abstract: The present power device includes a metal-made support substrate, and a group III nitride conductive layer, a group III nitride active layer and an electrode successively formed on one main surface side of the metal-made support substrate. In addition, the present method for manufacturing a power device includes the steps of preparing a conductive-layer-joined metal-made support substrate in which a group III nitride conductive layer is joined to a metal-made support substrate, forming a group III nitride active layer on the group III nitride conductive layer, and forming an electrode on the group III nitride active layer. Thus, an inexpensive power device low in on-resistance and a method for manufacturing the same can be provided.

Abstract: A MOSFET includes a silicon carbide substrate including a main surface having an off angle of not less than 50° and not more than 65° with respect to a {0001} plane, a buffer layer and a drift layer formed on the main surface, a gate oxide film formed on and in contact with the drift layer, and a p type body region of a p conductivity type formed in the drift layer to include a region in contact with the gate oxide film. The p type body region has a p type impurity density of not less than 5×1016 cm?3.

Abstract: A method of cleaning an SiC semiconductor capable of exhibiting an effect of cleaning an SiC semiconductor is provided. An SiC semiconductor and an SiC semiconductor device capable of achieving improved characteristics are provided. The method of cleaning an SiC semiconductor includes the steps of forming an oxide film on a surface of an SiC semiconductor (step S2) and removing the oxide film (step S3). In the forming step (step S2), the oxide film is formed in a dry atmosphere at a temperature not lower than 700° C. that contains O element. The SiC semiconductor is an SiC semiconductor having a surface and the surface has metal surface density not higher than 1×1012 cm?2. The SiC semiconductor device includes an SiC semiconductor and an oxide film formed on a surface of the SiC semiconductor.

Abstract: The present method of forming a nitride semiconductor epitaxial layer includes the steps of growing at least one layer of nitride semiconductor epitaxial layer on a nitride semiconductor substrate having a dislocation density lower than or equal to 1×107 cm?2 with a chemical decomposition layer interposed therebetween, the chemical decomposition layer being chemically decomposed at least with either a gas or an electrolytic solution, and decomposing the chemical decomposition layer at least with either the gas or the electrolytic solution at least either during or after the step of growing the nitride semiconductor epitaxial layer, thereby separating the nitride semiconductor epitaxial layer from the nitride semiconductor substrate. A high-quality nitride semiconductor epitaxial layer suffering less damage when separated from the nitride semiconductor substrate is thereby formed.

Abstract: SiC single crystal that includes a first dopant functioning as an acceptor, and a second dopant functioning as a donor is provided, where the content of the first dopant is no less than 5×1015 atoms/cm3, the content of the second dopant is no less than 5×1015 atoms/cm3, and the content of the first dopant is greater than the content of the second dopant. A manufacturing method for silicon carbide single crystal is provided with the steps of: fabricating a raw material by mixing a metal boride with a material that includes carbon and silicon; vaporizing the raw material; generating a mixed gas that includes carbon, silicon, boron and nitride; and growing silicon carbide single crystal that includes boron and nitrogen on a surface of a seed crystal substrate by re-crystallizing the mixed gas on the surface of the seed crystal substrate.

Abstract: Provided is a III nitride semiconductor electronic device having a structure capable of reducing leakage current. A laminate 11 includes a substrate 13 and a III nitride semiconductor epitaxial film 15. The substrate 13 is made of a III nitride semiconductor having a carrier concentration of more than 1×1018 cm?3. The epitaxial structure 15 includes a III nitride semiconductor epitaxial film 17. A first face 13a of the substrate 13 is inclined at an angle ? of more than 5 degrees with respect to an axis Cx extending in a direction of the c-axis. A normal vector VN and a c-axis vector VC make the angle ?. The III nitride semiconductor epitaxial film 17 includes first, second and third regions 17a, 17b and 17c arranged in order in a direction of a normal to the first face 13a. A dislocation density of the third region 17c is smaller than that of the first region 17a. A dislocation density of the second region 17b is smaller than that of the substrate 13.

Abstract: A method of fabricating a gallium nitride-based semiconductor electronic device is provided, the method preventing a reduction in adhesiveness between a gallium nitride-based semiconductor layer and a conductive substrate. A substrate 11 is prepared. The substrate 11 has a first surface 11a and a second surface 11b, the first surface 11a allowing a gallium nitride-based semiconductor to be deposited thereon. The substrate 11 includes a support 13 of a material different from the gallium nitride-based semiconductor. The support is exposed on the second surface 11b of the substrate 11. An array of grooves 15 is provided in the second surface 11b. A semiconductor region including at least one gallium nitride-based semiconductor layer is deposited on the first surface 11a of the substrate 11, and thereby an epitaxial substrate E is fabricated.

Abstract: A method of epitaxial growth of a 4H—SiC single crystal enabling growth of an SiC single crystal with low defects and low impurities able to be used for a semiconductor material at a practical growth rate, comprising growing a 4H—SiC single crystal on a 4H—SiC single crystal substrate by epitaxial growth while inclining an epitaxial growth plane of the substrate from a (0001) plane of the 4H—SiC single crystal by an off-angle of at least 12 degrees and less than 30 degrees in a <11-20> axial direction, and a 4H—SiC single crystal obtained by the same.

Abstract: A method of epitaxial growth of a 4H—SiC single crystal enabling growth of an SiC single crystal with low defects and low impurities able to be used for a semiconductor material at a practical growth rate, comprising growing a 4H—SiC single crystal on a 4H—SiC single crystal substrate by epitaxial growth while inclining an epitaxial growth plane of the substrate from a (0001) plane of the 4H—SiC single crystal by an off-angle of at least 12 degrees and less than 30 degrees in a <11-20> axial direction, and a 4H—SiC single crystal obtained by the same.

Abstract: Disclosed is a phosphor which is excited by a long wavelength light source in the ultraviolet region or blue-violet visible region and mainly emits light in violet-blue-yellow-red visible region. Also disclosed is a low-cost light-emitting diode which is easily mounted and excellent in color rendering properties. This light-emitting diode does not have much color change due to radiation angle. A phosphor composed of SiC is characterized in that it is excited by an outside light source for emitting light and doped with N and at least one of B and Al.

Abstract: SiC single crystal that includes a first dopant functioning as an acceptor, and a second dopant functioning as a donor is provided, where the content of the first dopant is no less than 5×1015 atoms/cm3, the content of the second dopant is no less than 5×1015 atoms/cm3, and the content of the first dopant is greater than the content of the second dopant. A manufacturing method for silicon carbide single crystal is provided with the steps of: fabricating a raw material by mixing a metal boride with a material that includes carbon and silicon; vaporizing the raw material; generating a mixed gas that includes carbon, silicon, boron and nitride; and growing silicon carbide single crystal that includes boron and nitrogen on a surface of a seed crystal substrate by re-crystallizing the mixed gas on the surface of the seed crystal substrate.

Abstract: A SiC wafer comprises a 4H polytype SiC substrate 2 in which the crystal plane orientation is substantially {03-38}, and a buffer layer 4 composed of SiC formed over this SiC substrate 2. The {03-38} plane forms an angle of approximately 35° with respect to the <0001> axial direction in which micropipes and so forth extend, so micropipes and so forth are eliminated at the crystal sides, and do not go through to an active layer 6 on the buffer layer 4. Lattice mismatching between the SiC substrate 2 and the active layer 6 is suppressed by the buffer layer 4. Furthermore, anisotropy in the electron mobility is low because a 4H polytype is used. Therefore, it is possible to obtain a SiC wafer and a SiC semiconductor device with which there is little anisotropy in the electron mobility, and strain caused by lattice mismatching can be lessened, as well as a method for manufacturing these.

Abstract: A method of growing a 4H-poly type SiC single crystal 40, characterized in that the 4H-poly type SiC single crystal 40 is grown on a seed crystal 30 comprised of an SiC single crystal where a {03-38} plane 30u or a plane which is inclined at off angle &agr;, within about 10°, with respect to the {03-38} plane, is exposed.

Abstract: An apparatus comprises an Si-disposing section in which solid Si is disposed; a seed-crystal-disposing section in which a seed crystal of SiC is disposed; a synthesis vessel adapted to accommodate the Si-disposing section, the seed-crystal-disposing section, and carbon; heating means adapted to heat the Si-disposing section and the seed-crystal-disposing section; and a control section for transmitting to the heating means a command for heating the Si to an evaporation temperature of Si or higher and heating the seed crystal to a temperature higher than that of Si; wherein the Si evaporated by the heating means is adapted to reach the seed-crystal-disposing section.

Abstract: A conductive polycrystalline diamond film having specific resistance of at least 1×10−4 &OHgr;cm and less than 1×103 &OHgr;cm, whose film thickness is in the range of at least 0.1 &mgr;m and not more than 500 &mgr;m, is film-formed by vapor-phase synthesis on a surface employed for pressure bonding, a surface opposite to this surface or at least two side surfaces intersecting with these surfaces on a substrate of a bonding tool tip that is applicable for bonding and packaging a semiconductor chip.

Abstract: An electron-emitting element comprises a diamond substrate, and a diamond protrusion grown on a surface of the diamond substrate so as to have a pointed portion in a form capable of emitting an electron. Since the diamond protrusion formed by growth has a sharply pointed tip portion, it can fully emit electrons. Preferably, the surface of the diamond substrate is a {100} face, and the diamond protrusion is surrounded by {111} faces.