Abstract: Provided are a hot-dip zinc plated steel material and a method for preparing same, the hot-dip zinc plated steel material comprising: base iron comprising 0.01-1.6 wt % of Si and 1.2-3.1 wt % of Mn; a Zn—Al—Mg alloy plating layer; and an Al-rich layer formed on the interface of the base iron and Zn—Al—Mg alloy plating layer, wherein the rate of occupied surface area of the Al-rich layer is 70% or higher (including 100%).

Abstract: Provided is a hot press formed product, which is prepared by means of hot press forming of a Zn—Al—Mg-based plated steel material comprising base iron and a Zn—Al—Mg-based plated layer, and a method for preparing the same, the hot press formed product comprising an oxide layer formed on the surface thereof, wherein the content ratio of Al to Mg (Al/Mg) in the oxide layer is 0.8 or more.

Abstract: Provided is a method of manufacturing an HPF part comprising: preparing a steel sheet comprising C: 0.18% to 0.25%, Si: 0.1% to 1.0%, Mn: 0.9% to 1.5%, P: 0.03% or less, S: 0.01% or less, Al: 0.01% to 0.05%, Cr: 0.05% to 0.5%, Ti: 0.01% to 0.05%, B: 0.001% to 0.005%, N: 0.009% or less, and a balance of Fe and impurities; heating the steel sheet at 550° C. to 850° C. followed by maintaining at 640° C. to 680° C., and immersing the steel sheet in a hot dip aluminum plating bath, and a balance of Al and impurities; cooling the plated steel sheet at 15° C./s or faster; heating the cooled hot dip aluminum plated steel sheet at 880° C. to 930° C. followed by maintaining for a certain time; and hot forming the alloyed hot dip aluminum plated steel sheet and quenching at a range of 300° C. or lower at the same time.

Abstract: Provided is a method of manufacturing a zinc-plated steel sheet. The method includes: coating a metal on the steel sheet on a steel sheet; annealing the metal coated steel sheet; and zinc plating the annealed steel sheet by dipping in a molten zinc plating bath. Further provided is a method of manufacturing a hot-press part including: coating a metal on the steel sheet on a steel sheet; annealing the metal coated steel sheet; zinc plating the annealed steel sheet by dipping in a molten zinc plating bath; heating the zinc-plated steel sheet; and press forming the heated steel sheet.

Abstract: Provided is a hot press-formed (HPF) member with excellent powdering resistance at the time of press forming. The HPF member includes a hot-dip coating layer containing Al on a surface of a base steel sheet. The base steel sheet includes, based on wt %, 0.18-0.25% of C, 0.1-1.0% of Si, 0.9-1.5% of Mn, 0.03% or less of P, 0.01% or less of S, 0.01-0.05% of Al, 0.05-0.5% of Cr, 0.01-0.05% of Ti, 0.001-0.005% of B, 0.009% or less of N, the balance Fe, and the other impurities. The hot-dip coating layer comprises a soft diffusion layer and a hard alloy layer. The alloy layer has a Tau phase in the range of 10-30%, in terms of area percent.

Abstract: Provided is a zinc-plated steel sheet for hot pressing having outstanding surface characteristics, comprising: a steel foundation plate comprising a metal surface diffusion layer of which the Gibbs free energy reduction per mole of oxygen during oxidation is less than that of Cr, an aluminum-rich layer containing at least 30 wt. % of aluminum formed on the surface diffusion layer, and a zinc plating layer formed on the aluminum-rich layer. In this way, a metal having a low affinity for oxygen is coated to an effective thickness prior to annealing and thus the creation of annealing oxides at the surface of the steel sheet is suppressed and a uniform zinc plating layer is formed, and alloying of the zinc plating layer is promoted during press-processing heat treatment. Cracking in the steel foundation plate during hot press molding is prevented.

Abstract: Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Abstract: A high-manganese hot-dip coated steel sheet is disclosed which provides high corrosion resistance, high ductility and high strength, mainly used for inner and outer panels of automobiles, and a method of manufacturing the same. The high-manganese hot-dip coated steel sheet includes a substrate steel sheet having a composition of (in weight %) 0.1 to 1.5% of C, 5 to 35% of Mn, and the remainder includes Fe and other unavoidable impurities, and a hot-dip zinc coating layer formed on the substrate steel sheet, the hot-dip zinc coating layer having a composition of (in weight %) 0.1 to 10% of Mn, 5 to 15% of Fe, and the remainder including Zn and other unavoidable impurities.

Abstract: An HPF molding member having a melted aluminum plating layer formed on the surface of a base steel sheet and excellent delamination resistance. The base steel sheet comprises: 0.18-0.25% by weight of C; 0.1-1.0% by weight of Si; 0.9-1.5% by weight of Mn; 0.03% by weight or less of P; 0.01% by weight or less of S; 0.01-0.05% by weight of Al; 0.05-0.5% by weight of Cr; 0.01-0.05% by weight of Ti; 0.001-0.005% by weight of B; 0.009% by weight or less of N; and the balance Fe and other impurities. The plating layer consists of a soft diffusion layer and a hard alloy layer, the hard alloy layer having a tau layer irregularly and non-continuously dispersed and distributed on the inside thereof at 10% or more of the entire area fraction. The difference in hardness between the alloy layer and the diffusion layer is 400 (Hv) or less.

Abstract: Provided is a hot press-formed (HPF) member with excellent powdering resistance at the time of press forming. The HPF member includes a hot-dip coating layer containing Al on a surface of a base steel sheet. The base steel sheet includes, based on wt %, 0.18-0.25% of C, 0.1-1.0% of Si, 0.9-1.5% of Mn, 0.03% or less of P, 0.01% or less of S, 0.01-0.05% of Al, 0.05-0.5% of Cr, 0.01-0.05% of Ti, 0.001-0.005% of B, 0.009% or less of N, the balance Fe, and the other impurities. The hot-dip coating layer comprises a soft diffusion layer and a hard alloy layer. The alloy layer has a Tau phase in the range of 10-30%, in terms of area percent.

Abstract: The present invention relates to a plated steel sheet having a plated layer with excellent stability for hot press molding, and more specifically, to a plated steel sheet having a plated layer with excellent stability for hot press molding in which a LME (Liquid Metal Embrittlement) phenomenon caused by a zinc enrichment region included in the plated layer is suppressed during hot press molding.

Abstract: Provided is a zinc-plated steel sheet for hot pressing having outstanding surface characteristics, comprising: a steel foundation plate comprising a metal surface diffusion layer of which the Gibbs free energy reduction per mole of oxygen during oxidation is less than that of Cr, an aluminium-rich layer containing at least 30 wt. % of aluminium formed on the surface diffusion layer, and a zinc plating layer formed on the aluminium-rich layer. In this way, a metal having a low affinity for oxygen is coated to an effective thickness prior to annealing and thus the creation of annealing oxides at the surface of the steel sheet is suppressed and a uniform zinc plating layer is formed, and alloying of the zinc plating layer is promoted during press-processing heat treatment. Cracking in the steel foundation plate during hot press molding is prevented.

Abstract: A high-ductility, high-strength and high Mn steel strip used for steel strips of automobiles requiring superior formability and high strength, a plated steel strip produced by using the same, and a manufacturing method thereof are disclosed. The high Mn steel strip comprises, by weight %, 0.2˜1.5% of C, 10˜25% of Mn, 0.01˜3.0% of Al, 0.005˜2.0% of Si, 0.03% or less of P, 0.03% or less of S, 0.040% or less of N, and the balance of Fe and other unavoidable impurities. The high-ductility, high-strength and high Mn steel strip, and the plated steel strip produced by using the same have superior surface properties and plating characteristics.

Abstract: Provided is a zinc-plated steel sheet for hot pressing having outstanding surface characteristics, comprising: a steel foundation plate comprising a metal surface diffusion layer of which the Gibbs free energy reduction per mole of oxygen during oxidation is less than that of Cr; an aluminum-rich layer containing at least 30 wt. % of aluminum formed on the surface diffusion layer, and a zinc plating layer formed on the aluminum-rich layer. In this way, a metal having a low affinity for oxygen is coated to an effective thickness prior to annealing and thus the creation of annealing oxides at the surface of the steel sheet is suppressed and a uniform zinc plating layer is formed, and alloying of the zinc plating layer is promoted during press-processing heat treatment. Cracking in the steel foundation plate during hot press molding is prevented.

Abstract: Provided are a bake hardening steel having a crystalline grain size of ASTM No. 9 or more and a method for preparing the bake hardening steel by controlling the winding, rolling and cooling conditions. The bake hardening steel includes: C:0.0016˜0.0025%, Si:0.02% or less, P:0.01˜0.05%, S:0.01% or less, sol.Al:0.08˜0.12%, N:0.0025% or less, Ti:0.003% or less, Nb:0.003˜0.011%, Mo:0.01˜0.1%, B:0.0005˜0.0015% or less, balance Fe and other inevitable impurities, wherein % is weight %, and Mn and P satisfy the relation of ?30(° C.)?803P?24.4Mn?58.

Abstract: A high-ductility, high-strength and high Mn steel strip used for steel strips of automobiles requiring superior formability and high strength, a plated steel strip produced by using the same, and a manufacturing method thereof are disclosed. The high Mn steel strip comprises, by weight %, 0.2˜1.5% of C, 10˜25% of Mn, 0.01˜3.0% of Al, 0.005˜2.0% of Si, 0.03% or less of P, 0.03% or less of S, 0.040% or less of N, and the balance of Fe and other unavoidable impurities. The high-ductility, high-strength and high Mn steel strip, and the plated steel strip produced by using the same have superior surface properties and plating characteristics.

Abstract: The present invention relates to a plated steel sheet having a plated layer with excellent stability for hot press molding, and more specifically, to a plated steel sheet having a plated layer with excellent stability for hot press molding in which a LME (Liquid Metal Embrittlement) phenomenon caused by a zinc enrichment region included in the plated layer is suppressed during hot press molding.

Abstract: Provided is a zinc-plated steel sheet for hot pressing having outstanding surface characteristics, comprising: a steel foundation plate comprising a metal surface diffusion layer of which the Gibbs free energy reduction per mole of oxygen during oxidation is less than that of Cr; an aluminum-rich layer containing at least 30 wt. % of aluminium formed on the surface diffusion layer, and a zinc plating layer formed on the aluminum-rich layer. In this way, a metal having a low affinity for oxygen is coated to an effective thickness prior to annealing and thus the creation of annealing oxides at the surface of the steel sheet is suppressed and a uniform zinc plating layer is formed, and alloying of the zinc plating layer is promoted during press-processing heat treatment. Cracking in the steel foundation plate during hot press molding is prevented.

Abstract: A method for manufacturing a steel sheet used for structural members, elements, etc. of automobiles including a front side member, pillar, and the like, and more particularly, a method for manufacturing a steel sheet having a high strength and formability as well as hot-dip galvanizing properties is disclosed. In the method, after an aluminum killed steel slab, which comprises, by weight %: C: 0.05% to 0.25%; Si: 0.1% to 1.5%; S: 0.02% or less; N: 0.01% or less; Al: 0.02% to 2.0%; Mn: 1.0% to 2.5%; P: 0.001% to 0.1%; Sb: 0.005% to 0.10%; the balance of Fe and other unavoidable impurities, is subjected to a homogenization treatment at a temperature range of 1050° C. to 1300° C., the aluminum killed steel slab is subjected to a hot rolling under a finishing hot rolling temperature of 850° C. to 950° C. and a coiling temperature of 400° C. to 700° C., followed by a cold rolling under a cold rolling reduction ration of 30% to 80%, and annealing the cold rolled steel sheet.

Abstract: Provided are a bake hardening steel having a crystalline grain size of ASTM No. 9 or more and a method for preparing the bake hardening steel by controlling the winding, rolling and cooling conditions. The bake hardening steel includes: C:0.0016˜0.0025%, Si:0.02% or less, P:0.01˜0.05%, S:0.01% or less, sol.Al:0.08˜0.12%, N:0.0025% or less, Ti:0.003% or less, Nb:0.003˜0.011%, Mo:0.01˜0.1%, B:0.0005˜0.0015% or less, balance Fe and other inevitable impurities, wherein % is weight %, and Mn and P satisfy the relation of ?30(° C.)?803P?24.4Mn?58.