Abstract: A process can prepare a bio-resorbable polyester as a granulate or powder by bulk polymerization of one or more monomer(s). The process involves a) filling a monomer granulate, containing the one or more monomer(s), into a container; b) adding a polymerization catalyst and a chain length moderator on top of the monomer granulate; c) adding further monomer granulate on top; d) closing the container; e) carrying out a polymerization reaction in the closed container at a temperature in the range of 50° C. to 170° C., wherein a solid polymer in the form of a polymer block is formed; f) removing the polymer block from the container; and g) comminuting the polymer block to a granulate or powder; wherein the container is an unstirred container, wherein steps b) and c) are carried out once or are repeated, and wherein steps a) to e) are carried out under inert atmosphere.

Abstract: The invention refers to a Process for preparing a bio-resorbable polyester the form of a powder with a bulk density of 0.3 g/ml or more, a tapped density of 0.4 g/ml or more and a specific surface area of 2.0 m2/g or less comprising the steps a. dissolving a bio-resorbable polyester in a first solvent to form a polymer solution, b. contacting the polymer solution with a second solvent which is a non-solvent for the bioresorbable polyester and which is mainly water to result the precipitation of the bio-resorbable polyester in the form of a wet polymer mass, c. pre-drying the wet polymer mass at a temperature below the TgO of the bio-resorbable polyester, d. comminuting the pre-dried polymer mass to polymer particles with a size below 10 mm, e. drying the comminuted polymer particles below the TgO of the bio-resorbable polyester to a residual water content of 1% or less by weight/weight, f.

Abstract: The invention refers to a Process for preparing a bio-resorbable polyester the form of a powder with a bulk density of 0.3 g/ml or more, a tapped density of 0.4 g/ml or more and a specific surface area of 2.0 m2/g or less comprising the steps a. dissolving a bio-resorbable polyester in a first solvent to form a polymer solution, b. contacting the polymer solution with a second solvent which is a non-solvent for the bioresorbable polyester and which is mainly water to result the precipitation of the bio-resorbable polyester in the form of a wet polymer mass, c. pre-drying the wet polymer mass at a temperature below the TgO of the bio-resorbable polyester, d. comminuting the pre-dried polymer mass to polymer particles with a size below 10 mm, e. drying the comminuted polymer particles below the TgO of the bio-resorbable polyester to a residual water content of 1% or less by weight/weight, f.