Abstract: There is disclosed a magnetic material having a composition in atomic percentage of: (MM1-aRa)uFe100-u-v-w-x-yYvMwTxBy wherein MM is a mischmetal or a synthetic equivalent thereof; R is Nd, Pr or a combination thereof; Y is a transition metal other than Fe; M is one or more of a metal selected from Groups 4 to 6 of the periodic table; and T is one or more of a metal other than B, selected from Groups 11 to 14 of the periodic table, wherein 0?a?1, 7?u?13, 0?v?20, 0?w?5; 0?x?5 and 4?y?12.

Abstract: The present invention relates to highly quenchable Fe-based rare earth magnetic materials that are made by rapid solidification process and exhibit good magnetic properties and thermal stability. More specifically, the invention relates to isotropic Nd—Fe—B type magnetic materials made from a rapid solidification process with a lower optimal wheel speed and a broader optimal wheel speed window than those used in producing conventional magnetic materials. The materials exhibit remanence (Br) and intrinsic coercivity (Hci) values of between 7.0 to 8.5 kG and 6.5 to 9.9 kOe, respectively, at room temperature. The invention also relates to process of making the materials and to bonded magnets made from the magnetic materials, which are suitable for direct replacement of anisotropic sintered ferrites in many applications.

Abstract: The present invention relates to highly quenchable Fe-based rare earth magnetic materials that are made by rapid solidification process and exhibit good magnetic properties and thermal stability. More specifically, the invention relates to isotropic Nd—Fe—B type magnetic materials made from a rapid solidification process with a lower optimal wheel speed and a broader optimal wheel speed window than those used in producing conventional magnetic materials. The materials exhibit remanence (Br) and intrinsic coercivity (Hci) values of between 7.0 to 8.5 kG and 6.5 to 9.9 kOe, respectively, at room temperature. The invention also relates to process of making the materials and to bonded magnets made from the magnetic materials, which are suitable for direct replacement of anisotropic sintered ferrites in many applications.

Abstract: The present invention relates to highly quenchable Fe-based rare earth magnetic materials that are made by rapid solidification process and exhibit good magnetic properties and thermal stability. More specifically, the invention relates to isotropic Nd—Fe—B type magnetic materials made from a rapid solidification process with a lower optimal wheel speed and a broader optimal wheel speed window than those used in producing conventional magnetic materials. The materials exhibit remanence (Br) and intrinsic coercivity (Hci) values of between 7.0 to 8.5 kG and 6.5 to 9.9 kOe, respectively, at room temperature. The invention also relates to process of making the materials and to bonded magnets made from the magnetic materials, which are suitable for direct replacement of anisotropic sintered ferrites in many applications.

Abstract: A rare earth-containing powder is pressed into a compact at ambient temperatures using a solid lubricant applied only to the die wall and/or a core. The solid lubricant is applied by suspending lubricant powder in a fluorinated hydrocarbon liquid.