Abstract: Method for thermally treating a scrolling steel strip (5), said method comprising the following steps: heating the strip (5) in a zone for heating with a direct flame (10); temperature homogenisation of the strip (5) in a homogenisation chamber (20) comprising at least one radiant heating tube (25), so as to homogenise the strip (5) in temperature after the passing thereof into the zone for heating with a direct flame (10) of the preceding step; oxidation of the strip (5) in an oxidation chamber (30) with an oxidising atmosphere having an oxygen volume concentration greater than 1%; reduction of the strip (5) in a reduction zone (40).

Abstract: A method for rinsing an overflow chamber at the bath-side end of a snout of a device for hot-dip coating a metal strip is presented. The snout guides the metal strip in a protective gas atmosphere before the metal strip is coated with a metal melt. A rinsing cycle is carried out in the overflow chamber of the snout by feeding metal melt from the molten bath into the overflow chamber and at the same time, sucking and pumping said melt out of the overflow chamber back into the molten bath. This rinsing cycle can be performed even when the snout has been retracted from the melt by supplying the melt from the molten bath to the overflow chamber with a delivery pump.

Abstract: Method for the preoxidation of high-strength strip steel. The invention relates to an improved method for the preoxidation of high-strength strip steel in a reaction chamber arranged in a furnace chamber.

Abstract: A method for rinsing an overflow chamber at the bath-side end of a snout of a device for hot-dip coating a metal strip is presented. The snout guides the metal strip in a protective gas atmosphere before the metal strip is coated with a metal melt. A rinsing cycle is carried out in the overflow chamber of the snout by feeding metal melt from the molten bath into the overflow chamber and at the same time, sucking and pumping said melt out of the overflow chamber back into the molten bath. This rinsing cycle can be performed even when the snout has been retracted from the melt by supplying the melt from the molten bath to the overflow chamber with a delivery pump.

Abstract: Method for thermally treating a scrolling steel strip (5), said method comprising the following steps: heating the strip (5) in a zone for heating with a direct flame (10); temperature homogenisation of the strip (5) in a homogenisation chamber (20) comprising at least one radiant heating tube (25), so as to homogenise the strip (5) in temperature after the passing thereof into the zone for heating with a direct flame (10) of the preceding step; oxidation of the strip (5) in an oxidation chamber (30) with an oxidising atmosphere having an oxygen volume concentration greater than 1%; reduction of the strip (5) in a reduction zone (40).

Abstract: A method for heat treating metallic strips inside a heat treatment chamber at a pressure greater than atmospheric pressure including passing the strips through at least one heating zone of the chamber and moving the strip through at least one cooling zone of the chamber. A first protective gas atmosphere containing nitrogen and hydrogen and/or helium is established in all but at least one cooling zone. The at least one cooling zone has a second protective atmosphere containing nitrogen and a second amount of hydrogen, the second amount of hydrogen is greater than the first amount. Nitrogen is introduced into the chamber, and a protective gas containing a third hydrogen content greater than the second hydrogen content is injected into the cooling zone, producing a gas exchange between one zone of the chamber having the first protective atmosphere and the cooling zone, and controlling the flow of introduction and injection.

Abstract: The invention concerns a method for metal strip heat treatment comprising: passing the strip inside a chamber through a heating zone, and a cooling zone, and establishing a first protective gas atmosphere containing nitrogen and a first hydrogen content in the chamber, except for the cooling zone, wherein is adjusted a second protective gas atmosphere containing nitrogen and a second hydrogen content higher than the first, introducing nitrogen into the chamber, injecting protective gas containing a third hydrogen content higher than said second content in said cooling zone, producing a gas exchange between one zone of the chamber having said first protective gas atmosphere and said cooling zone, and controlling the flow of said introduction and said injection.