Abstract: A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.

Abstract: A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.

Abstract: A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.

Abstract: A method of forming a shaped steel object, includes cutting a blank from an alloy composition. The alloy composition includes 0.1-1 wt. % carbon, 0.1-3 wt. % manganese, 0.1-3 wt. % silicon, 1-10 wt. % aluminum, and a balance being iron. The method also includes heating the blank to a temperature above a temperature at which austenite begins to form to generate a heated blank, transferring the heated blank to a die, forming the heated blank into a predetermined shape defined by the die to generate a shaped steel object, and decreasing the temperature of the shaped steel object to ambient temperature. The heating is performed under an atmosphere comprising at least one of an inert gas, a carbon (C)-based gas, and nitrogen (N2) gas.

Abstract: A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.

Abstract: A method of forming a shaped steel object, includes cutting a blank from an alloy composition. The alloy composition includes 0.1-1 wt. % carbon, 0.1-3 wt. % manganese, 0.1-3 wt. % silicon, 1-10 wt. % aluminum, and a balance being iron. The method also includes heating the blank to a temperature above a temperature at which austenite begins to form to generate a heated blank, transferring the heated blank to a die, forming the heated blank into a predetermined shape defined by the die to generate a shaped steel object, and decreasing the temperature of the shaped steel object to ambient temperature. The heating is performed under an atmosphere comprising at least one of an inert gas, a carbon (C)-based gas, and nitrogen (N2) gas.

Abstract: An alloy composition is provided. The alloy composition includes chromium (Cr) at a concentration of greater than or equal to about 0.5 wt. % to less than or equal to about 9 wt. %, carbon (C) at a concentration of greater than or equal to about 0.15 wt. % to less than or equal to about 0.5 wt. %, manganese (Mn) at a concentration of greater than or equal to about 0 wt. % to less than or equal to about 3 wt. %, silicon (Si) at a concentration of greater than or equal to about 0.5 wt. % to less than or equal to about 2 wt. %, and a balance of the alloy composition being iron. Methods of making shaped steel objects from the alloy composition are also provided.