Abstract: A process is described in which non-structural galvanized steel studs are sequentially chemically treated with a permanganate coating to improve oxidation resistance, followed by treatment with a silicate coating sealant, optionally with zinc surface activation using an acid treatment.

Abstract: A process is described in which non-structural galvanized steel studs are sequentially chemically treated with a permanganate coating to improve oxidation resistance, followed by treatment with a silicate coating sealant, optionally with zinc surface activation using an acid treatment.

Abstract: I provide an aqueous coating composition to provide an outer protective coating for a metal selected from the group consisting of an aluminum, aluminum alloy, iron, iron alloy, zinc, zinc alloy, zinc coated iron, zinc coated iron alloy, and these metals and magnesium and magnesium alloys having a conversion coating thereon. The aqueous coating composition consists essentially of 60 to 90 parts by weight water, 0.5 to 10 parts by weight of a polyvinyl alcohol having a weight average molecular weight of at least 100,000 and being at least 95% hydrolyzed, 0.5 to 20 parts by weight of a polybasic acid or anhydride, and 0.0 to 3 parts by weight of a cross-linking agent or plasticizer to form a in-situ polyester conversion coating on the metal. The composition is applied directly to the metal or to the metal article which has a non-chromium conversion coating thereon and forms a thin film thereon. Then the metal with the film thereon is heated to between 300° to 550° F.

Abstract: A method for coating zinc, zinc plated, or steel articles with a hydroxy benzoic acid protective coating by coating a cleaned zinc, zinc plated, or steel with a hydoxy benzoic acid composition having a pH of about 2.0 to 5.0; and coating cleaned tin surfaced articles with a composition having a PH of 2.0 to 12.0, and the composition having as its essential ingredients proteins, amino acids, amino acid-protein compounds and amine alcohols; and the articles produced thereby along with the coated articles having an appropriate paint thereon.

Abstract: I provide a method of coating zinc or zinc plated article with a non-hexavalent chromium oxide protective coating by coating a cleaned zinc or zinc plated article with a permanganate composition having a PH of about 2.0 to about 9.

Abstract: I provide a method of coating zinc or zinc plated article with a non-hexavalent chromium oxide protective coating by coating a cleaned zinc or zinc plated article with a permanganate composition having a PH of about 2.0 to about 9.