Abstract: An austenitic stainless steel alloy is disclosed, having excellent fast neutron irradiation swelling resistance and good post irradiation ductility, making it especially useful for liquid metal fast breeder reactor applications. The alloy contains: about 0.04 to 0.09 wt. % carbon; about 1.5 to 2.5 wt. % manganese; about 0.5 to 1.6 wt. % silicon; about 0.030 to 0.08 wt. % phosphorus; about 13.3 to 16.5 wt. % chromium; about 13.7 to 16.0 wt. % nickel; about 1.0 to 3.0 wt. % molybdenum; and about 0.10 to 0.35 wt. % titanium.

Abstract: An article of an alloy of AISI 316 stainless steel is reduced in size to predetermined dimensions by cold working in repeated steps. Before the last reduction step the article is annealed by heating within a temperature range, specifically between 1010.degree. C. and 1038.degree. C. for a time interval between 90 and 60 seconds depending on the actual temperature. By this treatment the swelling under neutron bombardment by epithermal neutrons is reduced while substantial recrystallization does not occur in actual use for a time interval of at least of the order of 5000 hours.

Abstract: An alloy system is disclosed which is particularly useful for heat exchanger and water tubing applications. This alloy system utilizes additions of zinc, nickel and iron to a copper base. Cobalt and manganese may also be added to the alloy and such elements as arsenic, antimony and phosphorus may be added as parting inhibitors to the system.

Abstract: An alloy system is disclosed which is particularly useful for heat exchanger and water tubing applications. This alloy system utilizes additions of zinc, nickel and iron to a copper base. Cobalt and manganese may also be added to the alloy and such elements as arsenic, antimony and phosphorus may be added as parting inhibitors to the system.