Abstract: Provided is a method of manufacturing a zinc-plated steel sheet. The method includes: coating a metal on the steel sheet on a steel sheet; annealing the metal coated steel sheet; and zinc plating the annealed steel sheet by dipping in a molten zinc plating bath. Further provided is a method of manufacturing a hot-press part including: coating a metal on the steel sheet on a steel sheet; annealing the metal coated steel sheet; zinc plating the annealed steel sheet by dipping in a molten zinc plating bath; heating the zinc-plated steel sheet; and press forming the heated steel sheet.

Abstract: Provided is a method of manufacturing a hot-dip galvanized steel sheet. According to an aspect of the present invention, the method may include preparing a base steel sheet, forming a iron (Fe)-plated layer on the prepared base steel sheet, oxidation heating the steel sheet having the Fe-plated layer formed thereon at a temperature ranging from 600° C. to 800° C., maintaining the heated steel sheet at a temperature ranging from 750° C. to 900° C. for 5 seconds or more in a reducing atmosphere with a dew point of between -30° C. to 5° C. including 20 ppm or less of oxygen, 1 vol % to 20 vol % of H2, and N2 as well as unavoidable gases as a remainder, cooling the maintained steel sheet, and plating the cooled steel sheet by dipping in a hot-dip galvanizing bath.

Abstract: Provided is a zinc-plated steel sheet for hot pressing having outstanding surface characteristics, comprising: a steel foundation plate comprising a metal surface diffusion layer of which the Gibbs free energy reduction per mole of oxygen during oxidation is less than that of Cr, an aluminum-rich layer containing at least 30 wt. % of aluminum formed on the surface diffusion layer, and a zinc plating layer formed on the aluminum-rich layer. In this way, a metal having a low affinity for oxygen is coated to an effective thickness prior to annealing and thus the creation of annealing oxides at the surface of the steel sheet is suppressed and a uniform zinc plating layer is formed, and alloying of the zinc plating layer is promoted during press-processing heat treatment. Cracking in the steel foundation plate during hot press molding is prevented.

Abstract: Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Abstract: A method of manufacturing a transparent pattern printed steel plate includes forming a printed paint film layer by jetting transparent ink onto at least one surface of a steel plate, and curing the printed paint film layer with ultraviolet light to form a cured printed paint film layer. Further, a method of manufacturing a transparent pattern printed steel plate includes preparing a steel plate having a color painted film layer formed on at least one surface thereof, forming a printed paint film layer by jetting transparent ink onto the color painted film layer, and curing the printed paint film layer to form a cured printed paint film layer.

Abstract: The present invention relates to a surface-treated steel plate and to a production method for same, and more specifically relates to a surface-treated steel plate having outstanding corrosion resistance and thermal conductivity. In order to achieve this aim, in the present invention a macromolecular resin composition comprising graphene, which has highly outstanding physical properties including electrical conductivity, is coated onto the surface of a steel foundation plate, thereby making it possible to provide a surface-treated steel plate able to supremely well ensure not only corrosion resistance but also the intrinsic characteristics of graphene due to the macromolecular resin composition.

Abstract: A conversion coating composition comprising 0.01 wt % to 0.2 wt % of phosphorous (P); 0.01 wt % to 0.2 wt % of magnesium (Mg); 0.005 wt % to 0.15 wt % of zirconium (Zr); 0.005 wt % to 0.15 wt % of titanium (Ti); 0.005 wt % to 0.15 wt % of vanadium (V); 0.05 wt % to 1 wt % of phenol resin; the balance of water and other unavoidable impurities is provided. A surface treated steel sheet comprising a base steel sheet; a zinc or zinc alloy plated layer formed on the base steel sheet; a blackening layer formed on the zinc or zinc alloy plated layer; and an organic and inorganic complex conversion coating layer formed on the blackening layer, wherein the organic and inorganic complex conversion coating layer may satisfy the weight ratio of P:Mg:Zr:Ti:V=1:0.045 to 2:0.035 to 1.5:0.035 to 1.3:0.035 to 1.5 (based on the weight of P) is also provided. A method for manufacturing a steel sheet treated with the conversion coating composition is also provided.

Abstract: Provided is a resin composition for an under coat of an UV coating layer and a coated steel sheet using the resin composition. The coated steel sheet comprises a material steel sheet; an under coat layer including a cured product of a resin composition for the under coat layer which contains a main resin and a metal powder, the under coat layer being formed on one side or both sides of the material steel sheet; and a top coat layer formed on the under coat layer and containing a radical compound, thereby providing a superior appearance, scratch resistance, corrosion resistance and superior weldability.

Abstract: According to the present invention, a noncovalent bond-modified carbon structure has advantages of: enabling the control of properties by controlling intervals between carbon structures according to the size and structure of a compound represented by Chemical Formula 1, which is inserted and adsorbed between the carbon structures; and enabling uniform dispersion in a polymer matrix without a change in intrinsic properties. In addition, a carbon structure/polymer composite comprising the modified carbon structure and a polymer matrix is simply manufactured and readily layered due to excellent orientation when forming a cured coating film, and thus can be useful for manufacturing a steel sheet having remarkable heat radiation, surface polarity, electrical properties and the like.

Abstract: A hot-dip galvanized steel sheet having excellent resistance to cracking caused by liquid metal embrittlement is provided. The hot-dip galvanized steel sheet having excellent resistance to cracking caused by liquid metal embrittlement includes a base steel sheet having a microstructure in which an austenite fraction is 90 area % or more; and a hot-dip galvanizing layer formed on the base steel sheet, wherein the hot-dip galvanizing layer includes an Fe—Zn alloy layer; and a Zn layer formed on the Fe—Zn alloy layer, and the Fe—Zn alloy layer has a thickness of [(3.4×t)/6] ?m or more, where t is a thickness of the hot-dip galvanizing layer. In addition, provided is the hot-dip galvanized steel sheet in which plating layer delamination easily occurring in vehicle welding and molding conditions according to the related art, is prevented, and cracking caused by liquid metal embrittlement is suppressed.

Abstract: A platelet-type zirconium phosphate, which has a P—OH group contained in a structure thereof, and has a crystalline peak at a 2? value of 11.6±2 degrees and no crystalline peak at a 2? value of less than 11.6±2 degrees in X-ray diffraction analysis, is provided. The platelet-type zirconium phosphate has a platelet-type structure and can be uniformly dispersed at a nanoscale level in a coating film to exhibit excellent surface gloss and barrier capability. Also, the platelet-type zirconium phosphate can exhibit excellent corrosion resistance due to the presence of the P—OH group on a surface thereof, and can be dispersed not only in an aqueous solution but also in an organic solvent.

Abstract: A platelet-type zirconium phosphate, which has a P—OH group contained in a structure thereof, and has a crystalline peak at a 2? value of 11.6±2 degrees and no crystalline peak at a 2? value of less than 11.6±2 degrees in X-ray diffraction analysis, is provided. The platelet-type zirconium phosphate has a platelet-type structure and can be uniformly dispersed at a nanoscale level in a coating film to exhibit excellent surface gloss and barrier capability. Also, the platelet-type zirconium phosphate can exhibit excellent corrosion resistance due to the presence of the P—OH group on a surface thereof, and can be dispersed not only in an aqueous solution but also in an organic solvent.

Abstract: Provided are a resin composition for surface treatment and a surface-treated steel sheet coated therewith. The resin composition for surface treatment includes a dispersing element having excellent thermal conductivity and heat dissipation, thereby maintaining physical properties of the conventional anti-fingerprint steel sheet, for example, high whiteness, fingerprint resistance, workability, electric conductivity and alkali resistance, and providing heat dissipation. In addition, the surface-treated steel sheet coated with the resin composition for surface treatment of the present invention has physical properties such as high heat dissipation, electric conductivity and whiteness, and thus may be replaced with a bottom chassis of a backlight unit, particularly, an edge-type backlight unit.

Abstract: Provided is a hot-dip galvanized steel sheet having excellent adhesiveness at ultra-low temperatures as well as fine spangles, and a method of manufacturing the same. According to the present invention, a hot-dip galvanized steel sheet having excellent adhesiveness at ultra-low temperatures includes a base steel sheet, a composite layer formed on the base steel sheet and including transition metal, an inhibition layer formed on the composite layer and including a iron-aluminum (Fe—Al) based intermetallic compound, and a zinc (Zn)-plated layer formed on the inhibition layer, in which an average diameter of spangles in the zinc-plated layer is 150 ?m or less, and a method of manufacturing the hot-dip galvanized steel sheet is provided.

Abstract: The present invention relates to a surface-treated steel plate and to a production method for same, and more specifically relates to a surface-treated steel plate having outstanding corrosion resistance and thermal conductivity. In order to achieve this aim, in the present invention a macromolecular resin composition comprising graphene, which has highly outstanding physical properties including electrical conductivity, is coated onto the surface of a steel foundation plate, thereby making it possible to provide a surface-treated steel plate able to supremely well ensure not only corrosion resistance but also the intrinsic characteristics of graphene due to the macromolecular resin composition.

Abstract: Provided are a graphene oxide, a graphene-polymer complex, a coating solution containing same, a graphene-polymer complex-coated steel sheet, and a method for manufacturing same. According to the present invention, a steel sheet is provided, in which graphenes can be directly coated to a base steel sheet without using a separate binder and said graphenes can be located on a coating layer, thus properties of the graphenes can be efficiently exhibited.

Abstract: Provided is a metal coated steel sheet having a coating layer including a metal having a level of Gibbs free energy equal to that of Fe or above and an oxide thereof. Accordingly, the quality of a plated steel sheet may be improved by preventing the generation of bare spots through inhibition of the formation of Mn oxide, Si oxide, or Al oxide on the surface thereof, and simultaneously, the complexity of a manufacturing facility or an increase in manufacturing costs may be minimized. Economic benefits are thus realized.

Abstract: Provided is a zinc-plated steel sheet for hot pressing having outstanding surface characteristics, comprising: a steel foundation plate comprising a metal surface diffusion layer of which the Gibbs free energy reduction per mole of oxygen during oxidation is less than that of Cr, an aluminium-rich layer containing at least 30 wt. % of aluminium formed on the surface diffusion layer, and a zinc plating layer formed on the aluminium-rich layer. In this way, a metal having a low affinity for oxygen is coated to an effective thickness prior to annealing and thus the creation of annealing oxides at the surface of the steel sheet is suppressed and a uniform zinc plating layer is formed, and alloying of the zinc plating layer is promoted during press-processing heat treatment. Cracking in the steel foundation plate during hot press molding is prevented.

Abstract: Provided are an organic-inorganic hybrid coating solution composition including 12 wt % to 36 wt % of a urethane-acryl hybrid resin, 8 wt % to 24 wt % of a nanosilicate-phenoxy hybrid resin, and 40 wt % to 80 wt % of an inorganic-based anti-corrosion agent based on a solid content, and an organic-inorganic hybrid coated steel sheet having a coating layer formed with the coating solution composition. A coating solution composition having excellent solution stability and a coated steel sheet having improved corrosion resistance, solvent resistance, and conductivity may be provided.

Abstract: A conversion coating composition comprising 0.01 wt % to 0.2 wt % of phosphorous (P); 0.01 wt % to 0.2 wt % of magnesium (Mg); 0.005 wt % to 0.15 wt % of zirconium (Zr); 0.005 wt % to 0.15 wt % of titanium (Ti); 0.005 wt % to 0.15 wt % of vanadium (V); 0.05 wt % to 1 wt % of phenol resin; the balance of water and other unavoidable impurities is provided. A surface treated steel sheet comprising a base steel sheet; a zinc or zinc alloy plated layer formed on the base steel sheet; a blackening layer formed on the zinc or zinc alloy plated layer; and an organic and inorganic complex conversion coating layer formed on the blackening layer, wherein the organic and inorganic complex conversion coating layer may satisfy the weight ratio of P:Mg:Zr:Ti:V=1:0.045 to 2:0.035 to 1.5:0.035 to 1.3:0.035 to 1.5 (based on the weight of P) is also provided. A method for manufacturing a steel sheet treated with the conversion coating composition is also provided.