Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Jr and Pt.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir and Pt.

Abstract: A transition-metal-CHA molecular sieve catalyst and mixed-template synthesis procedure are disclosed.

Abstract: A transition-metal-CHA molecular sieve catalyst and mixed-template synthesis procedure are disclosed.

Abstract: A copper-CHA zeolite catalyst for SCR of NOx is disclosed.

Abstract: A catalyst article including a substrate with an inlet side and an outlet side, a first zone and a second zone, where the first zone includes a passive NOx adsorber (PNA), and an ammonia slip catalyst (ASC) comprising a platinum group metal on a support and a first SCR catalyst; where the second zone includes a catalyst selected from the group consisting of a diesel oxidation catalyst (DOC) and a diesel exotherm catalyst (DEC); and where the first zone is located upstream of the second zone. The first zone may include a bottom layer with a blend of: (1) the platinum group metal on a support and (2) the first SCR catalyst; and a top layer with a second SCR catalyst, the top layer located over the bottom layer.

Abstract: A catalyst article including a substrate with an inlet end and an outlet end, a first zone and a second zone, where the first zone comprises: a) an ammonia slip catalyst (ASC) bottom layer comprising a platinum group metal on a support; and b) an SCR layer comprising a second SCR catalyst, the SCR layer located over the ASC bottom layer; where the second zone comprises a catalyst (“second zone catalyst”) selected from the group consisting of a diesel oxidation catalyst (DOC) and a diesel exotherm catalyst (DEC); wherein the ASC bottom layer extends into the second zone; and where the first zone is located upstream of the second zone. The ASC bottom layer may include a blend of: (1) the platinum group metal on a support and (2) a first SCR catalyst.

Abstract: A catalyst article including a substrate with an inlet side and an outlet side, a first zone and a second zone, where the first zone includes an ammonia slip catalyst (ASC) comprising a platinum group metal on a support and a first SCR catalyst; where the second zone includes a catalyst selected from the group consisting of a diesel oxidation catalyst (DOC) and a diesel exotherm catalyst (DEC); and where the first zone is located upstream of the second zone. The first zone may include a bottom layer with a blend of: (1) the platinum group metal on a support and (2) the first SCR catalyst; and a top layer comprising a second SCR catalyst, the top layer located over the bottom layer.

Abstract: Provided is catalyst material useful for the selective catalytic reduction of NOx in lean burn exhaust gas, wherein the catalyst material is a hydrothermally stable, low SAR aluminosilicate zeolite loaded with a synergistic combination of one or more transition metals, such as copper, and one or more alkali or alkaline earth metals, such as calcium or potassium.

Abstract: A copper-CHA zeolite catalyst for SCR of NOx is disclosed.

Abstract: A catalytic material for treating an exhaust gas produced by a natural gas engine, which catalytic material comprises a molecular sieve and a platinum group metal (PGM) supported on the molecular sieve, wherein the molecular sieve has a framework comprising silicon, oxygen and optionally germanium, and has a content of heteroatom T-atoms is ?about 0.20 mol %.

Abstract: A copper-CHA zeolite catalyst for SCR of NOx is disclosed.

Abstract: Provided is catalyst material useful for the selective catalytic reduction of NOx in lean burn exhaust gas, wherein the catalyst material is a hydrothermally stable, low SAR aluminosilicate zeolite loaded with a synergistic combination of one or more transition metals, such as copper, and one or more alkali or alkaline earth metals, such as calcium or potassium.

Abstract: A catalyst washcoat is provided having a molecular sieve with a CHA crystal structure; about 0.5 to about 5.0 mol % phosphorus; and SiO2 and Al2O3 in a mole ratio of about 5 to about 40. The washcoat includes one or more promoters or stabilizers, and may be applied to a monolith substrate to produce a catalytically active article.

Abstract: Provided is catalyst material useful for the selective catalytic reduction of NOx in lean burn exhaust gas, wherein the catalyst material is a hydrothermally stable, low SAR aluminosilicate zeolite loaded with a synergistic combination of one or more transition metals, such as copper, and one or more alkali or alkaline earth metals, such as calcium or potassium.

Abstract: Provided is an ammonia slip catalyst article having supported palladium in a top or upstream layer for oxidation of carbon monoxide and/or hydrocarbons, an SCR catalyst either in the top layer or in a separate lower or downstream layer, and an ammonia oxidation catalyst in a bottom layer. Also provided are methods for treating an exhaust gas using the catalyst article, wherein the treatment involves reducing the concentrations of ammonia and optionally carbon monoxide and/or hydrocarbons in the exhaust gas.

Abstract: Provided is a catalyst composition comprising a small pore molecular sieve, about 0.5-5 weight percent of a transition metal (TM) selected from copper and/or iron, based on the total weight of the zeolite, and about 0.5-5 weight percent nickel, based on the total weight of the molecular sieve, wherein the transition metal and nickel are present in a TM:Ni ratio of about 10:1 to about 1:2. Also provided is a synthesis method for preparing a small pore molecular sieve having both Cu and Ni incorporated in situ. Also provided is a method for using such a catalyst for selectively reducing NOx in an exhaust gas.

Abstract: A catalyst article including a substrate with an inlet side and an outlet side, a first zone and a second zone, where the first zone includes a passive NOx adsorber (PNA), and an ammonia slip catalyst (ASC) comprising a platinum group metal on a support and a first SCR catalyst; where the second zone includes a catalyst selected from the group consisting of a diesel oxidation catalyst (DOC) and a diesel exotherm catalyst (DEC); and where the first zone is located upstream of the second zone. The first zone may include a bottom layer with a blend of: (1) the platinum group metal on a support and (2) the first SCR catalyst; and a top layer with a second SCR catalyst, the top layer located over the bottom layer.

Abstract: Provided is a method for reducing N2O emissions in an exhaust gas comprising contacting an exhaust gas containing NH3 and an inlet NO concentration with an SCR catalyst composition containing small pore zeolite having an SAR of about 3 to about 15 and having about 1-5 wt. % of an exchanged transition metal.

Abstract: Provided is a catalyst for the selective reduction of NOx comprising a two molecular sieve materials having a CHA structure, wherein the first molecular sieve has a mean crystal size of about 0.01 to 1 ?m and the second molecular sieve has a mean crystal size of about 1-5 ?m, and wherein the first molecular sieve contains a first extra-framework metal, the second molecular sieve contains a second extra-framework metal, and wherein said first and second extra-framework metals are independently selected from the group consisting of cesium, copper, nickel, zinc, iron, tin, tungsten, molybdenum, cobalt, bismuth, titanium, zirconium, antimony, manganese, chromium, vanadium, niobium, and combinations thereof.