Abstract: A synthetic fiber suited for use as a reinforcement for cement mortar or concrete as derived from monofilaments having a tensile strength of not less than 80 kg/mm.sup.2, Young's modulus of not less than 2,300 kg/mm.sup.2, a flat cross section in which the minor axis-to-major axis ratio is 1:2 to 1:10, and a fineness of 1,000-9,000 denier, and being cut to a fiber length such that the aspect ratio (the value obtained by dividing the fiber length by the diameter of a circle equivalent in area to the cross section of the fiber) amounts to 20-150, in particular a polyvinyl alcohol fiber having the above-mentioned characteristic features, shows good dispersibility in cement mortar and produces very good reinforcing effect. Materials of construction which are excellent in workability and postcure strength can be obtained by incorporating the above-mentioned fiber to cement and the like.

Abstract: Rapidly shrinking fibers hardly soluble in water and capable of shrinking in water at 20.degree. C. by not less than 30% in not longer than 10 seconds are obtained, for example, by spinning, drawing and heat-treating a carboxy-modified polyvinyl alcohol under specific conditions. Yarns made from a fiber of this kind in conjunction with a fiber slowing shrinking in water as well as nonwoven fabrics made by incorporating yarns containing said rapidly shrinking fibers in nonwoven fabric shrinkable upon absorption of water are suited as means of tightly fitting edge portions of disposable diapers to the thigh.

Abstract: Rapidly shrinking fibers hardly soluble in water and capable of shrinking in water at 20.degree. C. by not less than 30% in not longer than 10 seconds are obtained, for example, by spinning, drawing and heat-treating a carboxy-modified polyvinyl alcohol under specific conditions. Yarns made from a fiber of this kind in conjunction with a fiber slowing shrinking in water as well as nonwoven fabrics made by incorporating yarns containing said rapidly shrinking fibers in nonwoven fabric shrinkable upon absorption of water are suited as means of tightly fitting edge portions of disposable diapers to the thigh.