Abstract: A method and apparatus for manufacturing fiber-optic devices to precise CWL specifications by plasticizing one attachment end of a mounted fiber-optic device and finely adjusting the fiber tension while monitoring the CWL. In one embodiment, the method of manufacturing an optical fiber component to a precise CWL includes the step of affixing the ends of a fiber component under tension to a substrate to approximate a desired CWL. Subsequently, one end of the fiber is gripped with a movable clamp and the adjacent attachment plasticized while the tension on the fiber is adjusted until the CWL is within a desired range. The attachment is rehardened while the tension on the fiber is maintained by the movable clamp.

Abstract: The present invention is directed to a defect-free magnetic memory disc substrate. In particular, it is directed to a composite alumina-based, glass-coated, article with a defect free surface. Several methods for its manufacture including frit bonding, molten glass submersion, and tape formation are disclosed.

Abstract: Magnesia partially-stabilized zirconia ceramic materials can be prepared from "unpurified" zirconia which contains at least about 0.05 weight percent silica. Despite the relatively high silica content, a thermal shock resistant material can be produced by a firing schedule which includes heating to a top temperature at a specified rate and cooling back to room temperature at specified rates and which incorporates a thermal aging step at 1000-1200.degree. C. Differences in microstructure and monoclinic zirconia content, with consequent differences in physical properties of the ceramic material, can be attained by variations in the firing and thermal-aging schedules.

Abstract: Whisker-reinforced zirconia-mullite ceramic articles exhibiting excellent high-temperature modulus of rupture strength and good toughness are provided from batches comprising the free oxides ZrO.sub.2, SiO.sub.2 and Al.sub.2 O.sub.3 in combination with SiC whiskers for reinforcement. Due to the fine oxide particle sizes attainable and the fact that the mullite is formed in situ in the consolidation process, dense, whisker-reinforced mullite composite articles exhibiting excellent high-temperature strength and toughness may conveniently be obtained.

Abstract: A composite ceramic extrusion die consisting of a silicon carbide wisker-reinforced cordierite ceramic wherein the predominant matrix phase is cordierite or, preferably, barium-stuffed cordierite having a crystal compositon xBaO.4MgO.(4+x)Al.sub.2 O.sub.3.(10-2x)SiO.sub.2 wherein x ranges from zero up to about 0.5, such extrusion die exhibiting excellent durability under the conditions of non-ferrous metal alloy extrusion at temperatures of 700.degree.-900.degree. C., is described.