Abstract: Improved fin field effect transistor (FinFET) devices and methods for the fabrication thereof are provided. In one aspect, a field effect transistor device is provided. The field effect transistor device includes a source region; a drain region; a plurality of fins connecting the source region and the drain region, the fins having a pitch of between about 40 nanometers and about 200 nanometers and each fin having a width of between about ten nanometers and about 40 nanometers; and a gate stack over at least a portion of the fins, wherein the source region and the drain region are self-aligned with the gate stack.

Abstract: Improved fin field effect transistor (FinFET) devices and methods for the fabrication thereof are provided. In one aspect, a method for fabricating a field effect transistor device comprises the following steps. A substrate is provided having a silicon layer thereon. A fin lithography hardmask is patterned on the silicon layer. A dummy gate structure is placed over a central portion of the fin lithography hardmask. A filler layer is deposited around the dummy gate structure. The dummy gate structure is removed to reveal a trench in the filler layer, centered over the central portion of the fin lithography hardmask, that distinguishes a fin region of the device from source and drain regions of the device. The fin lithography hardmask in the fin region is used to etch a plurality of fins in the silicon layer. The trench is filled with a gate material to form a gate stack over the fins.

Abstract: Improved fin field effect transistor (FinFET) devices and methods for the fabrication thereof are provided. In one aspect, a method for fabricating a field effect transistor device comprises the following steps. A substrate is provided having a silicon layer thereon. A fin lithography hardmask is patterned on the silicon layer. A dummy gate structure is placed over a central portion of the fin lithography hardmask. A tiller layer is deposited around the dummy gate structure. The dummy gate structure is removed to reveal a trench in the filler layer, centered over the central portion of the fin lithography hardmask, that distinguishes a fin region of the device from source and drain regions of the device. The fin lithography hardmask in the fin region is used to etch a plurality of fins in the silicon layer. The trench is filled with a gate material to form a gate stack over the fins.

Abstract: Field-effect transistors (FETs) having nanowire channels are provided. In one aspect, a FET is provided. The FET comprises a substrate having a silicon-on-insulator (SOI) layer which is divided into at least two sections electrically isolated from one another, one section included in a source region and the other section included in a drain region; a channel region connecting the source region and the drain region and including at least one nanowire; an epitaxial semiconductor material, grown from the SOI layer, covering the nanowire and attaching the nanowire to each section of the SOI layer; and a gate over the channel region.

Abstract: A method of forming an integrated ferroelectric/CMOS structure which effectively separates incompatible high temperature deposition and annealing processes is provided. The method of the present invention includes separately forming a CMOS structure and a ferroelectric delivery wafer. These separate structures are then brought into contact with each and the ferroelectric film of the delivery wafer is bonded to the upper conductive electrode layer of the CMOS structure by using a low temperature anneal step. A portion of the delivery wafer is then removed providing an integrated FE/CMOS structure wherein the ferroelectric capacitor is formed on top of the CMOS structure. The capacitor is in contact with the transistor of the CMOS structure through all the wiring levels of the CMOS structure.

Abstract: Improved fin field effect transistor (FinFET) devices and methods for the fabrication thereof are provided. In one aspect, a method for fabricating a field effect transistor device comprises the following steps. A substrate is provided having a silicon layer thereon. A fin lithography hardmask is patterned on the silicon layer. A dummy gate structure is placed over a central portion of the fin lithography hardmask. A filler layer is deposited around the dummy gate structure. The dummy gate structure is removed to reveal a trench in the filler layer, centered over the central portion of the fin lithography hardmask, that distinguishes a fin region of the device from source and drain regions of the device. The fin lithography hardmask in the fin region is used to etch a plurality of fins in the silicon layer. The trench is filled with a gate material to form a gate stack over the fins.

Abstract: The present invention provides a method for forming low-defect density changed-orientation Si by amorphization/templated recrystallization (ATR) processes in which regions of Si having a first crystal orientation are amorphized by ion implantation and then recrystallized into the orientation of a template layer having a different orientation. More generally, the invention relates to the high temperature annealing conditions needed to eliminate the defects remaining in Si-containing single crystal semiconductor materials formed by ion-implant-induced amorphization and templated recrystallization from a layer whose orientation may be the same or different from the amorphous layer's original orientation. The key component of the inventive method is a thermal treatment for minutes to hours in the temperature range 1250-1330° C. to remove the defects remaining after the initial recrystallization anneal.

Abstract: Techniques for the fabrication of field-effect transistors (FETs) having nanowire channels are provided. In one aspect, a method of fabricating a FET is provided comprising the following steps. A substrate is provided having a silicon-on-insulator (SOI) layer. At least one nanowire is deposited over the SOI layer. A sacrificial gate is formed over the SOI layer so as to cover a portion of the nanowire that forms a channel region. An epitaxial semiconductor material is selectively grown from the SOI layer that covers the nanowire and attaches the nanowire to the SOI layer in a source region and in a drain region. The sacrificial gate is removed. An oxide is formed that divides the SOI layer into at least two electrically isolated sections, one section included in the source region and the other section included in the drain region. A gate dielectric layer is formed over the channel region. A gate is formed over the channel region separated from the nanowire by the gate dielectric layer.

Abstract: Field-effect transistors (FETs) having nanowire channels are provided. In one aspect, a FET is provided. The FET comprises a substrate having a silicon-on-insulator (SOI) layer which is divided into at least two sections electrically isolated from one another, one section included in a source region and the other section included in a drain region; a channel region connecting the source region and the drain region and including at least one nanowire; an epitaxial semiconductor material, grown from the SOI layer, covering the nanowire and attaching the nanowire to each section of the SOI layer; and a gate over the channel region.

Abstract: Techniques for the fabrication of field-effect transistors (FETs) having nanowire channels are provided. In one aspect, a method of fabricating a FET is provided comprising the following steps. A substrate is provided having a silicon-on-insulator (SOI) layer. At least one nanowire is deposited over the SOI layer. A sacrificial gate is formed over the SOI layer so as to cover a portion of the nanowire that forms a channel region. An epitaxial semiconductor material is selectively grown from the SOI layer that covers the nanowire and attaches the nanowire to the SOI layer in a source region and in a drain region. The sacrificial gate is removed. An oxide is formed that divides the SOI layer into at least two electrically isolated sections, one section included in the source region and the other section included in the drain region. A gate dielectric layer is formed over the channel region. A gate is formed over the channel region separated from the nanowire by the gate dielectric layer.

Abstract: Improved fin field effect transistor (FinFET) devices and methods for the fabrication thereof are provided. In one aspect, a method for fabricating a field effect transistor device comprises the following steps. A substrate is provided having a silicon layer thereon. A fin lithography hardmask is patterned on the silicon layer. A dummy gate structure is placed over a central portion of the fin lithography hardmask. A tiller layer is deposited around the dummy gate structure. The dummy gate structure is removed to reveal a trench in the filler layer, centered over the central portion of the fin lithography hardmask, that distinguishes a fin region of the device from source and drain regions of the device. The fin lithography hardmask in the fin region is used to etch a plurality of fins in the silicon layer. The trench is filled with a gate material to form a gate stack over the fins.

Abstract: A method of forming an integrated ferroelectric/CMOS structure which effectively separates incompatible high temperature deposition and annealing processes is provided. The method of the present invention includes separately forming a CMOS structure and a ferroelectric delivery wafer. These separate structures are then brought into contact with each and the ferroelectric film of the delivery wafer is bonded to the upper conductive electrode layer of the CMOS structure by using a low temperature anneal step. A portion of the delivery wafer is then removed providing an integrated FE/CMOS structure wherein the ferroelectric capacitor is formed on top of the CMOS structure. The capacitor is in contact with the transistor of the CMOS structure through all the wiring levels of the CMOS structure.

Abstract: A method of forming an integrated ferroelectric/CMOS structure which effectively separates incompatible high temperature deposition and annealing processes is provided. The method of the present invention includes separately forming a CMOS structure and a ferroelectric delivery wafer. These separate structures are then brought into contact with each and the ferroelectric film of the delivery wafer is bonded to the upper conductive electrode layer of the CMOS structure by using a low temperature anneal step. A portion of the delivery wafer is then removed providing an integrated FE/CMOS structure wherein the ferroelectric capacitor is formed on top of the CMOS structure. The capacitor is in contact with the transistor of the CMOS structure through all the wiring levels of the CMOS structure.

Abstract: The present invention provides a method for forming low-defect density changed-orientation Si by amorphization/templated recrystallization (ATR) processes in which regions of Si having a first crystal orientation are amorphized by ion implantation and then recrystallized into the orientation of a template layer having a different orientation. More generally, the invention relates to the high temperature annealing conditions needed to eliminate the defects remaining in Si-containing single crystal semiconductor materials formed by ion-implant-induced amorphization and templated recrystallization from a layer whose orientation may be the same or different from the amorphous layer's original orientation. The key component of the inventive method is a thermal treatment for minutes to hours in the the temperature range 1250-1330° C. to remove the defects remaining after the initial recrystallization anneal.

Abstract: A method of forming an integrated ferroelectric/CMOS structure which effectively separates incompatible high temperature deposition and annealing processes is provided. The method of the present invention includes separately forming a CMOS structure and a ferroelectric delivery wafer. These separate structures are then brought into contact with each and the ferroelectric film of the delivery wafer is bonded to the upper conductive electrode layer of the CMOS structure by using a low temperature anneal step. A portion of the delivery wafer is then removed providing an integrated FE/CMOS structure wherein the ferroelectric capacitor is formed on top of the CMOS structure. The capacitor is in contact with the transistor of the CMOS structure through all the wiring levels of the CMOS structure.

Abstract: A method of forming an integrated ferroelectric/CMOS structure which effectively separates incompatible high temperature deposition and annealing processes is provided. The method of the present invention includes separately forming a CMOS structure and a ferroelectric delivery wafer. These separate structures are then brought into contact with each and the ferroelectric film of the delivery wafer is bonded to the upper conductive electrode layer of the CMOS structure by using a low temperature anneal step. A portion of the delivery wafer is then removed providing an integrated FE/CMOS structure wherein the ferroelectric capacitor is formed on top of the CMOS structure. The capacitor is in contact with the transistor of the CMOS structure through all the wiring levels of the CMOS structure.

Abstract: A novel air-gap-containing interconnect wiring structure is described incorporating a solid low-k dielectric in the via levels, and a composite solid plus air-gap dielectric in the wiring levels. Also provided is a method for forming such an interconnect structure. The method is readily scalable to interconnect structures containing multiple wiring levels, and is compatible with Dual Damascene Back End of the Line (BEOL) processing.

Abstract: A structure and a method are disclosed of an enhanced T-gate for modulation doped field effect transistors (MODFETs). The enhanced T-gate has insulator spacer layers sandwiching the neck portion of the T-gate. The spacer layers are thinner than the T-bar portion overhang. The insulating layer provides mechanical support and protects the vulnerable neck portion of the T-gate from chemical attack during subsequent device processing, making the T-gate structure highly scalable and improving yield. The use of thin conformal low dielectric constant insulating layers ensures a low parasitic gate capacitance, and reduces the risk of shorting gate and source metallurgy when source-to-gate spacings are reduced to smaller dimensions.

Abstract: A field effect transistor and method for making is described incorporating self aligned source and drain contacts with Schottky metal-to-semiconductor junction and a T-shaped gate or incorporating highly doped semiconductor material for the source and drain contacts different from the channel material to provide etch selectivity and a T-shaped gate or incorporating a metal for the source and drain contacts and the oxide of the metal for the gate dielectric which is self aligned.

Abstract: A novel air-gap-containing interconnect wiring structure is described incorporating a solid low-k dielectric in the via levels, and a composite solid plus air-gap dielectric in the wiring levels. Also provided is a method for forming such an interconnect structure. The method is readily scalable to interconnect structures containing multiple wiring levels, and is compatible with Dual Damascene Back End of the Line (BEOL) processing.