Abstract: A fluororesin-metal oxide mixed dispersion (sol) with excellent operability and workability provided in a coating step is obtained by mixing aqueous dispersion of fluororesin particle, and particle sol of metal oxide with suitable pH value that is any one of titanium oxide, zirconium oxide, lanthanum oxide, neodymium oxide, cerium oxide, or tin oxide. Both the fluororesin particle and the metal oxide particle float and disperse without coagulation precipitation, gelation and solidification, and/or phase separation. The floating and dispersion state is stably maintained under room temperature storage for three days or more. Water contact angle of a solid product obtained by evaporation and scattering of a solvent from the fluororesin-metal oxide mixed dispersion is 130 degrees or less, and surface resistivity is 2.0×1012?/? (ohm/square) or less.

Abstract: A method of manufacturing a mixture PTFE thread using a mixture PTFE powder consisting of PTFE: 73-95 wt %, MoS2: 3-25 wt %, Al2O3: 1-5 wt %, and Al(OH)3: 1-5 wt % comprises heat-retaining step for adding 18-25 wt % kerosene of a solvent to the mixture PTFE powder and keeping it warm at 30-50° C. for 40 to 50 hours, extruding the heat-retained mixture PTFE powder into a rod shape with a circular or elliptical cross section at the cylinder temperature of 70-90° C., rolling the extrusion at 100-150° C. into a 0.3-0.7 mm thick sheet shape, multiple-folding the sheet and passing the sheet through an oven at 250-270° C. at the rate of 10-40 cm/s, and stretching the folded sheet with a stretch ratio of 200-600% in multiple stages after heating the sheet at 450-500° C.

Abstract: The invention aims to provide a method of manufacturing a carbon fiber resin tape capable of being adhered with a high adhesive strength without being pressurized at high pressure nor heated at high temperature. A method of manufacturing a carbon fiber resin tape F2 comprises: a first step of immersing a carbon fiber bundle F1 having several carbon fibers in reduced water having a negative oxidation-reduction potential to flatten the carbon fiber bundle; a second step of immersing the above-described carbon fiber bundle in an adhesive solution containing an adhesive S, alumina sol A, and potassium persulfate B after the above-described first step; and a third step of drying the above-described carbon fiber bundle after the above-described second step.

Abstract: Problem: A heat radiating material is provided to increase thermal conductivity in thickness direction by combining an expanded graphite and one or more kinds of thermally conductive fillers selected from a group consisting of artificial graphite, boron nitride, and milled pitch based carbon fiber, and also to enhance thermal conductivity in plane direction by sandwiching the mixture between sheet bodies. Solution: A heat radiating material consisting of a mixed graphite having a mixture of a filler and an expanded graphite, and a 10-100 micrometer thick sheet body, wherein the expanded graphite accounts for 70-95% of the entire mixed graphite, and wherein the mixed graphite and the sheet body are laminated.

Abstract: Provided is a composite material which can be preferably used as alternative seal materials to asbestos seal materials or as a heat dissipation sheet with excellent thermal conductivity. The composite material comprises: (1) an inorganic filler-containing material containing an inorganic filler and any of the following: a polyimide film, a polyimide varnish consisting of a polyamide acid solution, an incompletely-imidized and self-standing polyimide precursor film obtained by drying a polyamide acid solution, a polybenzimidazole film, a varnish consisting of a polybenzimidazole solution, a polyazomethine film, a mixed film consisting of a polyimide resin and a polybenzimidazole resin, a mixed varnish consisting of a polyamide acid solution and a polybenzimidazole solution, a mixed film consisting of a polyimide precursor and polyazomethine, a polybenzoxazole film, etc; and (2) a molding consisting of any of expanded graphite, organic fiber and inorganic fiber.

Abstract: To provide a composite that can find application to various uses in a wide spectrum of fields, for example, sealing members, such as a joint sheet, a gasket and a packing, for use in junction portions, etc. of pipings of power plant and chemical plant, radiation sheets, electromagnetic wave shielding members, soundproof sheets, etc., and provide a process for producing the composite; a gasket or packing based on the composite and a clay dispersion liquid used for the composite. There is provided a composite composed mainly of graphite and clay and having the structure of graphite laminated with and/or impregnated with clay. The composite is produced by subjecting an exfoliated graphite sheet or film or a molding therefrom to coating with and/or immersion in a clay dispersion liquid with clay particles dispersed therein, or by laminating together of an exfoliated graphite sheet and/or film and a sheet and/or film composed mainly of clay. Further, a gasket or packing is produced by molding the composite.

Abstract: [Problems to be Solved] To provide a graphite clay composite material, a process for producing the same, a gasket or packing comprising the composite material, and a clay dispersion used for the composite material, which can be applied to the various usages in a wide fields including; sealing material such as joint sheet, gasket, packing and the like, heat-release sheet, electromagnetic wave shielding material, sound-proof sheet and the like. [Means to Solving the Problems] A composite material comprising mainly a graphite and a clay, wherein the clay is laminated on and/or enters into a graphite layer.

Abstract: The purpose of the present invention is to provide a heat release sheet comprised of an expansive graphite sheet and a reticulated body with bursiform configuration,wherein said reticulated body is comprised of metal wire, wherein said expansive graphite sheet is inserted in the bursiform configuration, wherein at least a part of outer surface of said reticulated body is covered with resin layer, and wherein a protective layer comprised of a synthetic resin film is applied on a surface of said resin layer.

Abstract: 6 The present invention relates to the versatile packing material that has enough lubricating property, durability and sealing ability even if they are used under high PV value (speed of rotating shaft is more than 25 m/sec) to a shaft seal part of a fluid machinery where the rotating shaft rotates with high speed or under very high pressure to a seal of shuttle slide part of fluid machinery, and are high quality in durability, withstand pressure ability, heat resistance, lubricating property (low torque ability etc.), chemical resistance, sealing ability, low-emission ability and reducing production cost etc.

Abstract: The purpose of the present invention is to provide a heat release sheet and a heat sink that have excellent heat conductivity to both of plane direction and orthogonalized direction and can efficiently release heat which generates from a notebook computer and a plasma television etc. The heat release sheet is comprised of an expansive graphite sheet and a reticulated body, wherein said reticulated body is comprised of metal wire, and it is overlapped on both sides of said expansive graphite sheet, and said expansive graphite sheet and said reticulated body are combined by metal rolling process. The heat sink is comprised by forming the heat release sheet.

Abstract: The purpose of the present invention is to provide a packing material having enough durability even if it is used under high temperature and high pressure, and also the purpose of the present invention is to provide the packing material that only one type of the gland packing is enough to be used in a stuffing box.

Abstract: A packing material wherein one or a plurality of hard metal wire and one or a plurality of soft metal wire are tied up or twisted in a bundle to construct a weft material wherein the ratio of the number of the former to the number of the later is 1:1-0.3, the weft material is put in weft knit processing such as plain stitch, rib stitch, pearl stitch, welt stitch, half cardigan, full cardigan, plating stitch and inter-lock stitch, and Brinell hardness of said hard metal wire is 90-240 (Kg/mm2) and Brinell hardness of said soft metal is 40-55 (Kg/mm2).

Abstract: The present invention relates to gland packing materials made from expansive graphite, gland packing made from expansive graphite made from the materials, and a producing method of gland packing made from expansive graphite; braiding thread is a filamentose with winding or twisting a strip laminated sheet that a bundle of sprit fiber is laminated and unified through an adhesive layer so as to be a reinforcing material, and a cord body is constructed by braiding the braiding thread, then a packing is constructed by pressure forming this cord body.

Abstract: The present invention relates to the versatile packing material that has enough lubricating property, durability and sealing ability even if they are used under high PV value (speed of rotating shaft is more than 25 m/sec) to a shaft seal part of a fluid machinery where the rotating shaft rotates with high speed or under very high pressure to a seal of shuttle slide part of fluid machinery, and are high quality in durability, withstand pressure ability, heat resistance, lubricating property (low torque ability etc.), chemical resistance, sealing ability, low-emission ability and reducing production cost etc.

Abstract: The present invention relates to gland packing materials made from expansive graphite, gland packing made from expansive graphite made from the materials, and a producing method of gland packing made from expansive graphite; braiding thread is a filamentose with winding or twisting a strip laminated sheet that a bundle of sprit fiber is laminated and unified through an adhesive layer so as to be a reinforcing material, and a cord body is constructed by braiding the braiding thread, then a packing is constructed by pressure forming this cord body.

Abstract: The present invention relates to the materials used in a gland packing made from expansive graphite, the gland packing made from expansive graphite using the materials and a producing method of the gland packing made from expansive graphite, with producing facility in addition to sealing ability, heat resistance, chemical resistance and such properties and with causing no electrolytic corrosion to shaft and apparatus casing, and braiding thread which constructs these is braiding thread wherein a strip laminated sheet comprising an expansive graphite sheet laminated with a film made from polytetrafluoroethylene on one side thereof and is set with polyvinylalcohol layer on the other side thereof, is twist processed so that the film made from polytetrafluoroethylene positions on the outside.

Abstract: The present invention provides a clad steel plate of a base material and a cover material attached to the base material. The base material has holes with rising rims and the rims pass through the covering material and expand over its surface to unite the base and covering materials.