Abstract: A CIS solar cell having flexibility and high conversion efficiency may be produced, using, as a substrate, a polyimide film which is prepared from an aromatic tetracarboxylic acid component comprising 3,3?,4,4?-biphenyltetracarboxylic dianhydride as the main component and an aromatic diamine component comprising p-phenylenediamine as the main component, and has a maximum dimensional change in the temperature-increasing step of from 25° C. to 500° C. within a range of from +0.6% to +0.9%, excluding +0.6%, based on the dimension at 25° C. before heat treatment.

Abstract: A polyimide precursor composition including a polyimide precursor, and a fine particle having an optical anisotropy; and a polyimide composition including a polyimide, and a fine particle having an optical anisotropy.

Abstract: An easily producible electroconductive aromatic polyimide porous film comprising an aromatic polyimide porous film and carbon nanotubes dispersed in the film has a resistance in the thickness direction of 100 m?·cm2 or less and a Gurley air permeation resistance of 300 seconds/100 cc or less and exhibits especially high conductivity and high air permeability as a gas diffusion layer of a membrane-electrode assembly of a fuel cell.

Abstract: A CIS solar cell having flexibility and high conversion efficiency may be produced, using, as a substrate, a polyimide film which is prepared from an aromatic tetracarboxylic acid component comprising 3,3?,4,4?-biphenyltetracarboxylic dianhydride as the main component and an aromatic diamine component comprising p-phenylenediamine as the main component, and has a maximum dimensional change in the temperature-increasing step of from 25° C. to 500° C. within a range of from +0.6% to +0.9%, excluding +0.6%, based on the dimension at 25° C. before heat treatment.

Abstract: A polyimide-metal laminate comprising a polyimide film and a metal layer for use as an electrode, which is formed on the side (Side B) of the polyimide film which was in contact with a support when producing a self-supporting film in the production of the polyimide film, is used to produce a CIS solar cell.

Abstract: Disclosed is a polyimide film prepared from an aromatic tetracarboxylic acid component and an aromatic diamine component, which has a dimensional change from 25° C. to 500° C. within a range of from ?0.3% to +0.6% based on the initial dimension at 25° C. The polyimide film may be used as a substrate for a CIS solar cell.

Abstract: A CIS solar cell having flexibility and high conversion efficiency may be produced, using, as a substrate, a polyimide film which is prepared from an aromatic tetracarboxylic acid component comprising 3,3?,4,4?-biphenyltetracarboxylic dianhydride as the main component and an aromatic diamine component comprising p-phenylenediamine as the main component, and has a maximum dimensional change in the temperature-increasing step of from 25° C. to 500° C. within a range of from +0.6% to +0.9%, excluding +0.6%, based on the dimension at 25° C. before heat treatment.

Abstract: A polyimide-metal laminate comprising a polyimide film and a metal layer for use as an electrode, which is formed on the side (Side B) of the polyimide film which was in contact with a support when producing a self-supporting film in the production of the polyimide film, is used to produce a CIS solar cell.

Abstract: Disclosed is a polyimide film prepared from an aromatic tetracarboxylic acid component and an aromatic diamine component, which has a dimensional change from 25° C. to 500° C. within a range of from ?0.3% to +0.6% based on the initial dimension at 25° C. The polyimide film may be used as a substrate for a CIS solar cell.