Abstract: A seamless steel pipe for oil country tubular goods which simultaneously has a high strength of a 110 ksi grade of yield strength and a superior low temperature toughness and a method for manufacturing the same are provided. A quenching treatment is performed on a stainless steel seamless pipe having a composition which contains on a mass percent basis, less than 0.010% of C, 1.0% or less of Si, 0.1% to 2.0% of Mn, 0.020% or less of P, 0.010% or less of S, 0.10% or less of Al, 10% to 14% of Cr, 0.1% to 4.0% of Ni, 0.05% or less of N, and the balance being Fe and inevitable impurities in which after heating is performed to a heating temperature for quenching equivalent to or more than the Ac3 transformation point, cooling is performed to a temperature range of 100° C. or less at a cooling rate equivalent to or more than that of air cooling; and following the quenching treatment, a tempering treatment is performed in which heating is performed to a tempering temperature in the range of more than 450° C.

Abstract: A lubricant is provided for use in hot working such as cross-roll rolling of a seamless steel pipe. It effectively reduces the friction coefficient between the working tools and the material under the hot work, thus extending the lives of the tools. The lubricant contains: (A) from about 10 to about 60 wt % of alkali silicate; (B) from about 1 to about 20 wt % of silane coupling agent; (C) from about 0.1 to about 5.0 wt % of at least one kind of alkali compound selected from a group consisting of an alkali hydroxide, an alkali carbonate, an alkali borate and an alkali salt of mineral acid; and (D) from about 30 to about 70 wt % of water. Alternatively, the lubricant contains: (A) from about 10 to about 60 wt % of alkali silicate; (B) from about 1 to about 20 wt % of silane coupling agent; (C) from about 0.1 to about 5.

Abstract: A lubricant is provided for use in hot working such as cross-roll rolling of a seamless steel pipe. It effectively reduces the friction coefficient between the working tools and the material under the hot work, thus extending the lives of the tools. The lubricant contains: (A) from about 10 to about 60 wt % of alkali silicate; (B) from about 1 to about 20 wt % of silane coupling agent; (C) from about 0.1 to about 5.0 wt % of at least one kind of alkali compound selected from a group consisting of an alkali hydroxide, an alkali carbonate, an alkali borate and an alkali salt of mineral acid; and (D) from about 30 to about 70 wt % of water. Alternatively, the lubricant contains: (A) from about 10 to about 60 wt % of alkali silicate; (B) from about 1 to about 20 wt % of silane coupling agent; (C) from about 0.1 to about 5.