Abstract: The objective of the present invention is to impart coating film adhesion, corrosion resistance and rust prevention to magnesium alloys.

Abstract: A metal surface treatment composition is provided which improves corrosion resistance and film adhesion, and confers slip properties. This composition is an acrylic resin-containing metal surface treatment composition which is water-soluble, water-dispersible or emulsifiable, which comprises an acrylic resin, this resin comprising either or both of an amino group and an ammonium group together with a hydroxyl group and a hydrophobic group, and which further comprises a heavy metal or one of its salts.

Abstract: A metal surface treatment composition which can improve the corrosion resistance and the tight adhesion to coating films and impart slipperiness. The composition is an aqueous solution, dispersion or emulsion containing both an acrylic resin having nitrogenous heterocycles, amino and/or ammonium groups and hydrophobic groups and a heavy metal or a salt thereof. The amino or ammonium groups have at least one structure selected from among those represented by general formulae (I) (wherein in R.sub.1, R.sub.2 : hydrogen, hydroxyl, substituted or unsubstituted, linear or branched C.sub.1 -C.sub.5 alkyl, or substituted or unsubstituted, linear or branched C.sub.1 -C.sub.5 hydroxyalkyl) and (II) (wherein R.sub.3, R.sub.4, R.sub.5 : hydrogen, hydroxyl, substituted or unsubstituted, linear or branched C.sub.1 -C.sub.5 alkyl, or substituted or unsubstituted, linear or branched C.sub.1 -C.sub.5 hydroxyalkyl).

Abstract: A flux composition for brazing of an aluminum material which can feed a proper amount of flux to an area to be joined at the time of brazing and at the same time can improve working environment, and a method for brazing of an aluminum material. The method comprises: coating an aluminum material to be joined with a flux composition comprising 0.5 to 25 parts by weight of a polymeric compound having a number average molecular weight of 50000 to 5000000 and comprising repeating alkylene oxide units, 5 to 30 parts by weight of a fluoride flux, and water added in such an amount as will provide a total amount of the composition of 100 parts by weight; heating the coated area to remove water; heating the coated area to decompose and remove the polymeric compound; and then conducting heating for brazing.

Abstract: A surface-treated metal material wherein a film comprising an organic polymer compound having 5-100 mg of carbon per m.sup.2 and a phosphoric acid compound having 1-30 mg of phosphorus per m.sup.2 is formed on a metal surface, the ratio C/P of carbon atoms C to phosphorus atoms P in the film lying within the range 2-25.

Abstract: In a continuous surface treating method and apparatus with an inline centrifugal separator, an object to be treated is contained in a basket and hung from a hanger of an overhead type and a series of surface treatments of the object is carried out by using a continuous conveyer of a power and free type. By using a hanger attach-detach conveyer, the object is moved from a main conveyer to a sub-conveyer and an excessive treating liquid attached to the object in a previous process is separated by using the centrifugal separator. Then, the object is returned from the sub-conveyer to the main conveyer to perform a next process. The surface treating apparatus includes the rotatable basket for containing the object.

Abstract: The hydrophilic coating composition including, on a solid basis, (a) 0.3-6 parts by weight of polyvinyl pyrrolidone having a polymerization degree of 10-1000; and (b) 1-10 parts by weight of polyvinyl alcohol having a saponification degree of 80% or more and a polymerization degree of 100-1000, a weight ratio of the component (a) to the component (b), (a)/[(a)+(b)], being in the range of 0.1-0.9.

Abstract: A cleaning agent is used to wash surfaces of aluminum products in a cleaning bath. The cleaning agent is a water-soluble acid containing ferric ions. During the cleaning process, the ferric ions are reduced to ferrous ions. The used cleaning agent is sent to an electrolytic tank so that the ferrous ions are subject to the electrolytic oxidation to be converted into ferric ions. The regenerated cleaning agent is returned to the cleaning bath.

Abstract: A hydrophilic surface treatment chemicals comprising, on a solid basis,(a) 1-10 parts by weight of at least partially saponified polyvinyl acetate having a saponification degree of 45 or more and a polymerization degree of 100-600,(b) 0.3-15 parts by weight of water-soluble nylon, and(c) 0.1-5 parts by weight of a water-soluble amino resin,a weight ratio of the component (b) to the total of the components (a) and (c), (b)/[(a)+(c)], being in the range of 1-1/4, and a weight ratio of the component (a) to the component (c), (a)/(c), being in the range of 1/0.05-1/0.5. The hydrophilic surface treatment bath is prepared by properly diluting the chemicals for surface-treating aluminum members.

Abstract: In chromium-free aqueous acidic washing solutions for cleaning the surfaces of aluminum and aluminum-alloy particles, so as to remove therefrom smut and lubricating oil left on the surfaces thereof after metal forming operations, which solutions contain from 0.2 to 4 g/l ferric ion and sufficient sulfuric and/or nitric acid to impart a pH of 2 or less to the solutionh (and which optionally may also contain fluoride ions up to a concentration of 0.5 g/l) there is provided a method of controlling the effectiveness of the washing solution in which the ferric ion concentration therein is monitored, conveniently by the oxidation-reduction potential of the washing solution, as shown in FIG. 3, and is controlled within the desired limits by adding when appropriate suitable amounts of oxidant capable of oxidizing ferrous ions to ferric ions and, separately or in conjunction therewith, a replenisher containing a source of iron ions.

Abstract: A degreasing detergent composition for tin surfaces and a method for its use, wherein the composition is an aqueous solution having a pH of 9 to 13 and containing at least one surfactant, at least one alkali metal detergent builder, and at least an alkaline earth metal salt at a concentration of at least 0.003 g/l.

Abstract: A detergent degreasing composition for DI-process tin-plated cans, comprising an alkali metal or ammonium salt of orthophosphoric acid, an alkali metal salt of nitrous acid, an optional surfactant, sufficient of at least one alkali metal salt of carbonic acid to adjust the pH to 9 to 11, and water.

Abstract: An acidic aqueous zinc-containing coating solution containing about 0.4 to about 1 g/l of zinc, about 5 to about 40 g/l of phosphate, about 2 to about 5 g/l of chlorate, and about 0.01 to about 0.2 g/l of nitrite, and useful for forming on metal surfaces zinc phosphate coatings that exhibit excellent adhesion to a paint film and excellent corrosion resistance after painting when used as an undercoat for the cationic electrodeposition of a paint film, and a process for applying coating composition, including continuous spray or intermittent spray.

Abstract: An acidic aqueous zinc-containing coating solution containing about 0.08 to about 0.2 weight percent of zinc, about 0.8 to about 3 weight percent of phosphate, about 0.05 to about 0.35 weight percent of chlorate, about 0.001 to about 0.1 weight percent of nitrite, and a complex fluoride ion having the following concentration:0.4.gtoreq.y.gtoreq.0.63x-0.042wherein x is the concentration of the zinc in weight percent and y is the concentration of the complex fluoride ion in weight percent. The coating solution is useful for forming on metal surfaces zinc phosphate coatings that exhibit excellent alkali resistance, good adhesion to a paint film, and good corrosion resistance after painting when used as an undercoat for the cationic electrodeposition of a paint film.