Abstract: A method for constructing a welded construction, including the steps of: (a) providing separate component parts of the construction and (b) welding the separate parts together with an Al—Mg—Mn weld filler alloy having a good corrosion resistance and improved strength levels. The separate component parts having the following composition (in weight percent): Mg 4.9 to 6.0; Mn 0.6 to 1.2; Zn 0.25 to 1.5; Zr 0.05 to 0.25; Cr 0.3 max.; Ti 0.2 max.; Fe 0.5 max.; Si 0.5 max.; Cu 0.25 max.; Sc 0.3 max., balance inevitable impurities and aluminium. The Al—Mg—Mn weld filler alloy having the following composition (in weight percent): Mg 7.0-9.5; Mn 0.9-2.0; Zn 0.2-0.9 Zr?0.3; Cr?0.5; Sc?2.8; Cu?0.5; Fe?0.5; Si?0.5; Ti?0.3, the balance aluminium and incidental elements and impurities.

Abstract: A composite aluminium panel comprising two parallel plates and/or sheets secured to the peaks and troughs of a corrugated aluminium stiffener sheet between the parallel plates and/or sheets, wherein the corrugated aluminium stiffener sheet is made from an aluminium alloy rolled sheet of composition (in weight percent): Mg 1.5-6.0, Mn 0.3-1.4, Zn 0.4-5.0, Fe up to 0.5, Si up to 0.5, Zr up to 0.30; optionally one or more of Cr 0.05-0.3, Ti 0.01-0.20, V 0.05-0.25, Ag 0.05-0.40, and Cu up to 0.40; and other elements up to 0.05 each, 0.15 total, with a balance of Al; and having in an H-condition or in an O-condition a ratio of PS/UTS in the range of 0.4 to 0.9 and having good roll formability.

Abstract: Improved shape and strength of the weld in a welded structure are obtained by use of a weldable aluminum product comprising a structural component which is a sheet, a plate or an extruded body and is made of an aluminum alloy containing not more than 1.5 wt % Zn. This component has, adhered on at least one side, a cladding layer made of an AA7xxx-series alloy having a corrosion potential lower than that of the alloy of the structural component. The alloy of the structural component is preferably an AA5xxx-series alloy containing Mg in the range 2 to 6 wt %.