Abstract: To prepare crystalline sodium disilicates having a laminar structure, a molar ratio of SiO.sub.2 to Na.sub.2 O of (1.9 to 2.1) 1 and a water content of less than 0.3% by weight, a water glass solution is first obtained by reacting sand with sodium hydroxide solution in a molar ratio of SiO.sub.2 to Na.sub.2 O of (2.0 to 2.3) : 1 at temperatures of 180.degree. to 240.degree. C. and pressures of 10 to 30 bar. This water glass solution having at least 20% by weight of solids is treated in a spray drier with hot air at 200.degree. to 300.degree. C. with the formation of a pulverulent amorphous sodium disilicate having a water content (determined as loss on heating at 700.degree. C.) of 15 to 23% by weight and a bulk density of at least 300 g/l. The spray-dried pulverulent, amorphous sodium disilicate is ground.