Abstract: Embodiments relate to a method for fabricating nano-wires in nano-devices, and more particularly to nano-device fabrication using end-of-range (EOR) defects. In one embodiment, a substrate with a surface crystalline layer over the substrate is provided and EOR defects are created in the surface crystalline layer. One or more fins with EOR defects embedded within is formed and oxidized to form one or more fully oxidized nano-wires with nano-crystals within the core of the nano-wire.

Abstract: A method for fabricating a semiconductor device is presented. The method includes providing a substrate and forming a gate stack over the substrate. A first laser processing to form vacancy rich regions within the substrate on opposing sides of the gate stack is performed. The vacancy rich regions have a first depth from a surface of the substrate. A first implant causing end of range defect regions to be formed on opposing sides of the gate stack at a second depth from the surface of the substrate is also carried out, wherein the first depth is proximate to the second depth.

Abstract: Embodiments relate to a method for fabricating nano-wires in nano-devices, and more particularly to nano-device fabrication using end-of-range (EOR) defects. In one embodiment, a substrate with a surface crystalline layer over the substrate is provided and EOR defects are created in the surface crystalline layer. One or more fins with EOR defects embedded within is formed and oxidized to form one or more fully oxidized nano-wires with nano-crystals within the core of the nano-wire.

Abstract: A process for forming a strained channel region for a MOSFET device via formation of adjacent silicon-germanium source/drain regions, has been developed. The process features either blanket deposition of a silicon-germanium layer, or selective growth of a silicon-germanium layer on exposed portions of a source/drain extension region. A laser anneal procedure results in formation of a silicon-germanium source/drain region via consumption of a bottom portion of the silicon-germanium layer and a top portion of the underlying source/drain region. Optimization of the formation of the silicon-germanium source/drain region via laser annealing can be achieved via a pre-amorphization implantation (PAI) procedure applied to exposed portions of the source/drain region prior to deposition of the silicon-germanium layer. Un-reacted top portions of the silicon-germanium layer are selectively removed after the laser anneal procedure.

Abstract: A method for forming a shallow junction region in a crystalline semiconductor substrate and method for fabricating a semiconductor device having the shallow junction region includes a defect engineering step in which first ions are introduced into a first region of the substrate and vacancies are generated in the first region. During the generation of substrate vacancies, the first region remains substantially crystalline. Interstitial species are generated in a second region and second ions are introduced into the second region to capture the interstitial species. Laser annealing is used to activate dopant species in the first region and repair implantation damage in the second region. The defect engineering process creates a vacancy-rich surface region in which source and drain extension regions having high dopant activation and low sheet resistance are created in an MOS device.

Abstract: A method for forming a shallow junction region in a crystalline semiconductor substrate and method for fabricating a semiconductor device having the shallow junction region includes a defect engineering step in which first ions are introduced into a first region of the substrate and vacancies are generated in the first region. During the generation of substrate vacancies, the first region remains substantially crystalline. Interstitial species are generated in a second region and second ions are introduced into the second region to capture the interstitial species. Laser annealing is used to activate dopant species in the first region and repair implantation damage in the second region. The defect engineering process creates a vacancy-rich surface region in which source and drain extension regions having high dopant activation and low sheet resistance are created in an MOS device.

Abstract: A method for fabricating a semiconductor device is presented. The method includes providing a substrate and forming a gate stack over the substrate. A first laser processing to form vacancy rich regions within the substrate on opposing sides of the gate stack is performed. The vacancy rich regions have a first depth from a surface of the substrate. A first implant causing end of range defect regions to be formed on opposing sides of the gate stack at a second depth from the surface of the substrate is also carried out, wherein the first depth is proximate to the second depth.