Abstract: The an adhesive composition characterized in that the kisstack, which is defined as the force measured when a sheet coated with the adhesive composition is instantaneously peeled off after being attached, is about 6 N/inch or higher. The composition not only has excellent loop tack but also exhibits high kisstack characteristics, and thus can be widely used for various substrates.

Abstract: An aqueous acrylic pressure-sensitive adhesive composition, a method of preparing the same and a pressure-sensitive adhesive sheet including the same are disclosed herein. In some embodiments, an aqueous acrylic pressure-sensitive adhesive composition includes a copolymer including 20 to 99% by weight of an alkyl (meth)acrylate monomer, greater than 0 and 3% or less by weight of an acrylate monomer including a hydroxy group and greater than 0 and 3% or less by weight of an unsaturated carboxylic acid, and an anionic surfactant, wherein the anionic surfactant is present in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the copolymer, and wherein the copolymer has an average particle diameter of 500 nm or less and satisfies Equation 1.

Abstract: The present invention relates to superabsorbent polymer having an improved absorption speed through micropores formed inside, and a method for preparing the same.

Abstract: The present invention relates to a superabsorbent polymer having an improved adsorption rate and a high bulk density, and a preparation method thereof.

Abstract: The present invention relates to a method for preparing superabsorbent polymer. According to the preparation method of the present invention, by maintaining the hydrophilicity of superabsorbent polymer and appropriately controlling the crosslinking density, superabsorbent polymer with excellent properties can be prepared though homogeneous surface crosslinking. Thus, superabsorbent polymer with improved absorption speed can be provided without decrease in absorbency under load.

Abstract: An adhesive composition characterized in that the kisstack, which is defined as the force measured when a sheet coated with the adhesive composition is instantaneously peeled off after being attached, is about 6 N/inch or higher. The composition not only has excellent loop tack but also exhibits high kisstack characteristics, and thus can be widely used for various substrates.

Abstract: The present invention relates to a method for preparing super absorbent polymer, and the method for preparing super absorbent polymer according to the present invention may reduce the content of non-reacted monomers in the super absorbent polymer, by using three kinds of polymerization initiators.

Abstract: The present invention relates to a method for preparing superabsorbent polymer. According to the preparation method of the present invention, by maintaining the hydrophilicity of superabsorbent polymer and appropriately controlling the crosslinking density, superabsorbent polymer with excellent properties can be prepared though homogeneous surface crosslinking. Thus, superabsorbent polymer with improved absorption speed can be provided without decrease in absorbency under load.

Abstract: The present invention relates to a method for preparing super absorbent polymer, and the method for preparing super absorbent polymer according to the present invention may reduce the content of non-reacted monomers in the super absorbent polymer, by using three kinds of polymerization initiators.

Abstract: Provided is a method of preparing a superabsorbent polymer. In the method of preparing the superabsorbent polymer according to the present disclosure, a polymer resulting from polymerization of ethylene-based unsaturated monomers is subjected to a reassembling process by mixing with a compound of a particular Chemical Formula and water. According to the preparation method of the present disclosure, provided is a method of preparing a superabsorbent polymer having improved water holding capacity and a reduced content of residual monomers, thereby improving quality of final polymer products.

Abstract: The present invention relates to a superabsorbent polymer having an improved adsorption rate and a high bulk density, and a preparation method thereof.

Abstract: The present invention relates to superabsorbent polymer having an improved absorption speed through micropores formed inside, and a method for preparing the same.

Abstract: Provided is a method of preparing a superabsorbent polymer. In the method of preparing the superabsorbent polymer according to the present disclosure, a polymer resulting from polymerization of ethylene-based unsaturated monomers is subjected to a reassembling process by mixing with a compound of a particular Chemical Formula and water. According to the preparation method of the present disclosure, provided is a method of preparing a superabsorbent polymer having improved water holding capacity and a reduced content of residual monomers, thereby improving quality of final polymer products.

Abstract: The present invention relates to a method for preparing super absorbent polymer, and the method for preparing super absorbent polymer according to the present invention may reduce the content of non-reacted monomers in the super absorbent polymer, by using three kinds of polymerization initiators.

Abstract: Acrylic pressure-sensitive adhesive including an acrylic copolymer formed by copolymerizing: i) 81 to 96% by weight of an alkyl (meth) acrylic acid ester monomer having a carbon number of an alkyl group of 2 to 14; ii) 1 to 10% by weight of at least one monomer selected from the group consisting of an allyl ester, a vinyl ester and an unsaturated acetate; iii) 1 to 10% by weight of an acrylonitrile monomer; and iv) 0.1 to 2% by weight of a crosslinker including 5 to 15 of an alkylene oxide group, and having two or more groups of an acrylate group, a vinyl group or the combination thereof, and a surface finishing material comprising the same, which is environmentally friendly, has an excellent room temperature and an aging adhesive property, and has an excellent constructability.

Abstract: Provided is a removable acrylic pressure sensitive adhesive comprising (A) 70-96.5 weight % of (meth)acrylic acid ester monomer having C1-C14 alkyl group; (B) 0.5-27 weight % of one or more functional group containing monomers selected from the group consisting of carboxyl group containing monomer, hydroxyl group containing monomer, epoxy group containing monomer, vinyl ester group containing monomer and cyano group containing monomer; and (C) 0.6-3 weight % of a cross linking agent having 5-13 alkylene oxide groups and acrylate group or vinyl group in 100 weight % of the monomers and the cross linking agent, and the adhesive of the present invention is a water based adhesive and pro-environmental, and demonstrates excellent adhesiveness at room temperature and under aging atmosphere and excellent dimensional stability as well, so that it can be widely used for various pressure sensitive adhesive sheets for outdoor/indoor advertisement, automobile, printing, decorating, etc.

Abstract: Disclosed are an acrylic pressure-sensitive adhesive and a surface finishing material comprising the same. More specifically, disclosed is an acrylic pressure-sensitive adhesive that is achieved by including an acrylic copolymer formed by copolymerizing: i) 81 to 96% by weight of an alkyl (meth) acrylic acid ester monomer having a carbon number of an alkyl group of 2 to 14; ii) 1 to 10% by weight of at least one monomer selected from the group consisting of an allyl ester, a vinyl ester and an unsaturated acetate; iii) 1 to 10% by weight of an acrylonitrile monomer; and iv) 0.

Abstract: An acrylic pressure-sensitive adhesive composition according to the present invention comprises: acrylic copolymer (A) formed by copolymerizing i) alkyl(meth)acrylic acid ester monomer wherein the carbon atom of alkyl group is 2 to 14, ii) monomer having a functional group capable of crosslinking, iii) methyl(meth)acrylate monomer, iv) vinyl acetate monomer, v) glycidyl(meth)acrylate, and vi) crosslinking agent having 5 to 15 of alkyleneoxide groups and at least two acrylate group or vinyl group; and flame retardant (B). The acrylic pressure-sensitive adhesive composition improves the adhesive property and the dispersion of the flame retardant by controlling the crosslinking structure of the acrylic copolymer, such that a surface finishing material comprising the same can have the excellent adhesion and fireproof.

Abstract: Provided is a removable acrylic pressure sensitive adhesive comprising (A) 70-96.5 weight % of (meth)acrylic acid ester monomer having C1-C14 alkyl group; (B) 0.5-27 weight % of one or more functional group containing monomers selected from the group consisting of carboxyl group containing monomer, hydroxyl group containing monomer, epoxy group containing monomer, vinyl ester group containing monomer and cyano group containing monomer; and (C) 0.6-3 weight % of a cross linking agent having 5-13 alkylene oxide groups and acrylate group or vinyl group in 100 weight % of the monomers and the cross linking agent, and the adhesive of the present invention is a water based adhesive and pro-environmental, and demonstrates excellent adhesiveness at room temperature and under aging atmosphere and excellent dimensional stability as well, so that it can be widely used for various pressure sensitive adhesive sheets for outdoor/indoor advertisement, automobile, printing, decorating, etc.

Abstract: An acrylic pressure-sensitive adhesive composition according to the present invention comprises: acrylic copolymer (A) formed by copolymerizing i) alkyl (meth) acrylic acid ester monomer wherein the carbon atom of alkyl group is 2 to 14, ii) monomer having a functional group capable of crosslinking, iii) methyl (meth)acrylate monomer, iv) vinyl acetate monomer, v) glycidyl (meth)acrylate, and vi) crosslinking agent having 5 to 15 of alkyleneoxide groups and at least two acrylate group or vinyl group; and flame retardant (B). The acrylic pressure-sensitive adhesive composition improves the adhesive property and the dispersion of the flame retardant by controlling the crosslinking structure of the acrylic copolymer, such that a surface finishing material comprising the same can have the excellent adhesion and fireproof.