Abstract: The present invention relates to a variety of dispersible doped multi-component BaTiO.sub.3 based powder compositions. The primary particles of each of the products are substantially spherical, have sizes in the range of 0.05 to 0.4 microns and have narrow size distributions. Further, the compositions of the primary particles, forming each powder, are comparable. The amount of dopant oxide or oxides contained in the powder composition ranges from between greater than 1 to 10 mole percent. Regardless of the dopant or dopants utilzied, all the powder compositions of the present invention are identified by the same unique morphological characteristics.

Abstract: The present invention involves a method for producing a variety of barium titanate based powder products consisting of submicron, dispersible primary particles having narrow size distributions. The method, in its broadest aspects, involves heating an aqueous slurry of PbO, or Pb(OH).sub.2, and Ca(OH).sub.2 with a stoichiometric excess of the hydrous oxides of Ti(IV), Sn(IV), Zr(IV) and Hf(IV) to a temperature not exceeding 200.degree. C. Thereafter, the resulting slurry temperature is adjusted to between 50.degree. and 200.degree. C. and a solution of Ba(OH).sub.2 and Sr(OH).sub.2, having a temperature of 70.degree. to 100.degree. C. is added within a period of five minutes or less to the slurry. About 10 minutes after the addition of the Ba(OH).sub.2 and Sr(OH).sub.2 solution is completed, the slurry is heated to a temperature not exceeding 225.degree. C. to ensure formation of a stoichiometric perovskite product. Thereafter, the slurry is cooled and the solid product is recovered.