Abstract: A screen protector application kit includes a glass-based substrate (110) having an adhesive belt (270) and an adhesive container (478) of an uncured adhesive composition. The adhesive belt (270) includes a first major surface (272) adhered to the glass-based substrate (110), a second major surface (274), a distal edge (276) extending between the first major surface (272) and the second major surface (274), and a proximal edge (278) extending between the first major surface (272) and the second major surface (274). The uncured adhesive composition includes 30 wt % to 99.9 wt % of at least one of: (i) a monomer; and (ii) an oligomer; and 0.01 wt % to 10 wt % of a visible-light photoinitiator. The uncured adhesive composition may further include 0.1 wt % to 10 wt % of a co-initiator. The uncured adhesive composition may further include 0.1 wt % to 5 wt % of an oxygen inhibitor.

Abstract: Embodiments are directed to strengthened glass articles comprising a thickness t?1 mm (1000 ?m), an inner region under a central tension CT (in MPa), and at least one compressive stress layer adjacent the inner region and extending within the strengthened glass article from a surface of the strengthened glass article to a depth of layer DOL (in ?m), wherein the strengthened glass article is under a compressive stress at the surface CSs (in MPa), wherein the strengthened glass article is an alkali aluminosilicate glass article comprising 0-5 mol % Li2O, and at least 3 mol % Al2O3, and wherein the DOL?70 ?m, and a CSs/DOL ratio?2.5 MPa/?m.

Abstract: Embodiments are directed to strengthened glass articles comprising a thickness t?1 mm (1000 ?m), an inner region under a central tension CT (in MPa), and at least one compressive stress layer adjacent the inner region and extending within the strengthened glass article from a surface of the strengthened glass article to a depth of layer DOL (in ?m), wherein the strengthened glass article is under a compressive stress at the surface CSs (in MPa), wherein the strengthened glass article is an alkali aluminosilicate glass article comprising 0-5 mol % Li2O, and at least 3 mol % Al2O3, and wherein the DOL?70 ?m, and a CSs/DOL ratio?2.5 MPa/?m.