Abstract: A method of producing a refractory metal powder that includes providing a metal powder containing magnesium tantalate or magnesium niobate; and heating the powder in an inert atmosphere in the presence of magnesium, calcium and/or aluminum to a temperature sufficient to remove magnesium tantalate or magnesium niobate from the powder and/or heating the powder under vacuum to a temperature sufficient to remove magnesium tantalate or magnesium niobate from the powder, the heating steps being performed in any order. The metal powder can be formed into pellets at an appropriate sintering temperature, which can be formed into electrolytic capacitors.

Abstract: A method of preparing primary refractory metals (e.g., primary tantalum metal) by contacting a particulate refractory metal oxide (e.g., tantalum pentoxide) with a heated gas (e.g., a plasma), is described. The heated gas comprises hydrogen gas. The temperature range of the heated gas and the mass ratio of hydrogen gas to refractory metal oxide are each selected such that: (i) the heated gas comprises atomic hydrogen; (ii) the refractory metal oxide feed material is substantially thermodynamically stabilized (i.e., the concurrent formation of suboxides that are not reduced by atomic hydrogen is minimized); and (iii) the refractory metal oxide is reduced by contact with the heated gas, thereby forming primary refractory metal (e.g., primary tantalum metal and/or primary niobium metal).

Abstract: The present invention is directed a molybdenum alloy consisting essentially of a) molybdenum present in a major amount, b) tantalum and tungsten as major metal alloy additions and c) a minor amount of an element selected from the group consisting of boron, hafnium, carbon and mixtures thereof. The invention is also directed to an X-ray tube anode composed of a molybdenum alloy body having a focal track thereon, with the body consisting essentially of the above-described molybdenum alloy.

Abstract: A method of producing a refractory metal powder by (A) combining (i) an oxide particle component and (ii) a reducing agent; (B) forming a substantially uniform mixture of (i) and (ii); (C) continuously feeding the mixture into a furnace; (D) igniting the mixture at a reaction zone and starting a reaction that is sufficiently exothermic to form a high temperature flash; (E) starting a reaction that is sufficiently exothermic to form a high temperature self-sustaining flash; and (F) producing a free-flowing reduced oxide powder.