Abstract: A titanium dioxide micro-nanocontainers, corrosion-resistant waterborne epoxy coatings and preparation method thereof, including preparation steps as follows: TiO2 micro-nano spheres are synthesized by applying hydrothermal method; a polyaniline layer doped with molybdate ions is deposited on the surface of TiO2 micro-nano spheres by adopting the method of in-situ chemical polymerization, TiO2/PANI-MoO42? micro-nano-spheres are obtained, then, polydopamine is encapsulated on the surface of TiO2/PANI-MoO42? micro-nano spheres to obtain titanium dioxide micro-nanocontainers; next, antirust filler, defoamer, dispersant and thickener are added into waterborne epoxy emulsion, then titanium dioxide micro-nanocontainers are added in the waterborne epoxy emulsion for dispersing and grinding, filtering and encapsulating to obtain component A; the waterborne epoxy curing agent and deionized water are mixed in proportion to obtain component B; component A is stirred, then it is mixed with the component B in proportion,

Abstract: The present invention provides a thermosetting resin composition based on an orthophthalic unsaturated polymer resin, a dicyclopentadiene (DCPD) resin and a polyether urethane acrylate having two or more acrylate functionality per molecule.

Abstract: A polyetherester-based laminating resin composition includes an unsaturated polyetherester resin, and an epoxy acrylate oligomer. The laminating resin has no greater than about 35 percent by weight of ethylenically unsaturated monomer.