Abstract: A material is described in the form of a millimetric article constituted by coarse alumina particles with a median diameter in the range 10 to 200 ?m, said coarse particles being at a distance, from one interface to another, of less than 10 ?m, fine alumina particles with a median diameter in the range 0.5 to 10 ?m, said fine particles being at a distance, from one interface to another, of less than 5 ?m and being located in the space between the coarse particles, and a binder constituted by aluminium phosphate, said binder being located in the space between said fine and coarse particles, said material having a mesoporous volume, measured by mercury porosimetry, in the range 0.2 to 2 mL/g, a macroporous volume, measured by mercury porosimetry, in the range 0.05 to 0.2 mL/g and a BET specific surface area in the range 80 to 350 m2/g.

Abstract: A material is described in the form of a millimetric article constituted by coarse alumina particles with a median diameter in the range 10 to 200 ?m, said coarse particles being at a distance, from one interface to another, of less than 10 ?m, fine alumina particles with a median diameter in the range 0.5 to 10 ?m, said fine particles being at a distance, from one interface to another, of less than 5 ?m and being located in the space between the coarse particles, and a binder constituted by aluminium phosphate, said binder being located in the space between said fine and coarse particles, said material having a mesoporous volume, measured by mercury porosimetry, in the range 0.2 to 2 mL/g, a macroporous volume, measured by mercury porosimetry, in the range 0.05 to 0.2 mL/g and a BET specific surface area in the range 80 to 350 m2/g.

Abstract: A process for preparing a mesoporous alumina is described, comprising the following steps: a) mixing, in aqueous solution, at least one source of aluminum constituted by an aluminum alkoxide, at least one cationic surfactant and at least one organic solvent selected from methanol and ethanol; b) hydrothermally treating the mixture formed in said step a); c) drying the solid formed in said step b); d) calcining the solid formed in said step c).

Abstract: The invention concerns a process for preparing an EU-1 zeolite having a XO2/Y2O3 ratio in the range 10 to 100, comprising the following steps: a) mixing, in an aqueous medium, at least one source of at least one oxide XO2, X being selected from silicon and/or germanium, at least one source of at least one oxide Y2O3, Y being selected from aluminium, iron, gallium and boron, and at least one organic template Q; b) drying the reaction mixture derived from step a) at a temperature of less than 200° C.; c) hydrothermal treatment of the dried reaction mixture derived from step b) in an autoclave, said dried reaction mixture not being in contact with a liquid phase at the bottom of the autoclave.

Abstract: The invention describes a porous composite material that comprises a porous substrate based on a refractory inorganic oxide in which said substrate has a zeolite crystal content that is less than 25% by mass, whereby said crystals are dispersed homogeneously in the pores of said substrate, and the distribution coefficient that is measured by Castaing microprobe is between 0.75 and 1.25, and in which the total pore volume of said substrate represents at least 40% of the initial total pore volume of the substrate, and the mean diameter of the pores represents at least 50% of the mean diameter of the pores of the initial substrate, its process for preparation and its use as catalyst in the hydrocarbon feedstock conversion reactions.

Abstract: A process for preparing a mesoporous alumina is described, comprising the following steps: a) mixing, in aqueous solution, at least one source of aluminium constituted by an aluminium alkoxide, at least one cationic surfactant and at least one organic solvent selected from methanol and ethanol; b) hydrothermally treating the mixture formed in said step a); c) drying the solid formed in said step b); d) calcining the solid formed in said step c).

Abstract: A process is described for preparing a spherical material comprising a porous core coated with a continuous and homogeneous porous layer, the degree of attrition of said material being less than 20%. Said preparation process comprises a) bringing a bed of spherical particles constituting the core of said material into contact with a suspension containing an inorganic binder in order to form a solid having a pre-layer around said core; b) bringing the solid derived from step a) into contact, in a stream of hot air, with a powder constituted by spherical particles of an inorganic oxide and a suspension containing an inorganic binder and an organic binder in order to form a solid the core of which is coated with at least one continuous and homogeneous porous layer, the ratio of the (mass of anhydrous inorganic binder/volume of powder particles) being in the range 0.05 to 1 g.mL?1; c) drying the solid derived from said step b); and d) calcining the solid derived from said step c).

Abstract: The invention relates to a FAU-type zeolite membrane that comprises a FAU-type zeolite crystal layer incorporated in the surface porosity of at least one selected face of a porous substrate, in which the ratio between the thickness of said zeolite layer incorporated in the surface porosity of said selected face of the substrate and the total thickness of said zeolite layer is at least 70%. It also relates to processes for preparation and application of these membranes.

Abstract: An EUO-structural-type zeolite that comprises at least one element X that is selected from among silicon and germanium and at least one element T that is selected from among aluminum, iron, gallium, vanadium, zirconium, molybdenum, arsenic, antimony, chromium and manganese is described. It contains at least one alkyl quinuclidinium cation in its intracrystalline pores and has an N/X atomic ratio of more than 0.065, whereby N represents the nitrogen element. This invention also relates to a process for preparation of said zeolite and the use of the latter as an acidic solid in a process for conversion of hydrocarbon feedstocks.

Abstract: A preparation process is described for a porous composite material formed from an amorphous core based on at least one silicon oxide on which crystals of EU-1 zeolite are dispersed, said process comprising 1) the impregnation of a solid comprising a silicon oxide and an aluminum oxide with an aqueous solution comprising a hexamethonium cation, 2) the hydrothermal treatment, implemented in an autoclave of volume V (ml) under steam and at a temperature T comprised between 120 and 220° C., of said solid from stage 1), the quantity of water introduced beforehand into said autoclave being strictly greater than a volumetric quantity equal to V*[23.48*10?10*T3?48*10?8*T2+5*10?5*T?0.002] and less than or equal to 0.25*V, and is such that said solid is not in direct contact with it, 3) the drying then calcination of the solid from stage 2). The preparation a catalyst from said material for its use in the isomerization of C8 aromatics is also described.

Abstract: The invention describes a porous composite material that comprises a porous substrate based on a refractory inorganic oxide in which said substrate has a zeolite crystal content that is less than 25% by mass, whereby said crystals are dispersed homogeneously in the pores of said substrate, and the distribution coefficient that is measured by Castaing microprobe is between 0.75 and 1.25, and in which the total pore volume of said substrate represents at least 40% of the initial total pore volume of the substrate, and the mean diameter of the pores represents at least 50% of the mean diameter of the pores of the initial substrate, its process for preparation and its use as catalyst in the hydrocarbon feedstock conversion reactions.

Abstract: The invention concerns a process for preparing an EU-1 zeolite having a XO2/Y2O3 ratio in the range 10 to 100, comprising the following steps: a) mixing, in an aqueous medium, at least one source of at least one oxide XO2, X being selected from silicon and/or germanium, at least one source of at least one oxide Y2O3, Y being selected from aluminium, iron, gallium and boron, and at least one organic template Q; b) drying the reaction mixture derived from step a) at a temperature of less than 200° C.; c) hydrothermal treatment of the dried reaction mixture derived from step b) in an autoclave, said dried reaction mixture not being in contact with a liquid phase at the bottom of the autoclave.

Abstract: The invention relates to a process for preparation of a zeolite that is selected from among the ZBM-30, ZSM-48, EU-2 and EU-11 zeolites, comprising the mixing in an aqueous medium of at least one source of at least one element X (Si and/or Ge) and at least one nitrogen-containing organic compound Q. Said nitrogen-containing organic compound Q is selected from among the compounds comprising at least one ether group and two terminal ammonium groups and their precursors.

Abstract: A preparation process is described for a porous composite material formed from an amorphous core based on at least one silicon oxide on which crystals of EU-1 zeolite are dispersed, said process comprising 1) the impregnation of a solid comprising a silicon oxide and an aluminium oxide with an aqueous solution comprising a hexamethonium cation, 2) the hydrothermal treatment, implemented in an autoclave of volume V (ml) under steam and at a temperature T comprised between 120 and 220° C., of said solid from stage 1), the quantity of water introduced beforehand into said autoclave being strictly greater than a volumetric quantity equal to V*[23.48*10?10*T3?48*10?8*T2+5*10?5T?0.002] and less than or equal to 0.25*V, and is such that said solid is not in direct contact with it, 3) the drying then calcination of the solid from stage 2). The preparation a catalyst from said material for its use in the isomerization of C8 aromatics is also described.

Abstract: An EUO-structural-type zeolite that comprises at least one element X that is selected from among silicon and germanium and at least one element T that is selected from among aluminum, iron, gallium, vanadium, zirconium, molybdenum, arsenic, antimony, chromium and manganese is described. It contains at least one alkyl quinuclidinium cation in its intracrystalline pores and has an N/X atomic ratio of more than 0.065, whereby N represents the nitrogen element. This invention also relates to a process for preparation of said zeolite and the use of the latter as an acidic solid in a process for conversion of hydrocarbon feedstocks.

Abstract: The invention relates to a FAU-type zeolite membrane that comprises a FAU-type zeolite crystal layer incorporated in the surface porosity of at least one selected face of a porous substrate, in which the ratio between the thickness of said zeolite layer incorporated in the surface porosity of said selected face of the substrate and the total thickness of said zeolite layer is at least 70%. It also relates to processes for preparation and application of these membranes.

Abstract: A non-homogeneous adsorbent is described, formed of a core and at least one continuous outer layer in which the core of said adsorbent has a volume adsorptive capacity representing at least 35% of the volume of the adsorbent and the outer layer has a diffusional selectivity greater than 5. The adsorbent is used in gas-separation processes or liquid-separation processes.

Abstract: A new EUO-structural-type zeolite that comprises at least one tetravalent element X that is selected from among silicon, tin, titanium and germanium and optionally at least one trivalent element T that is selected from among aluminum, iron, boron, indium and gallium is described. This new zeolite is characterized in that it contains, in its crude synthesis form, the nitrogen-containing organic cation of formula N,N-dimethyl-N,N-di(3,3-dimethylbutyl)ammonium. A method for the preparation of this zeolite is also described.

Abstract: This invention relates to a process for the preparation of a supported zeolite membrane that consists of a zeolite/substrate composite layer, whereby the crystallization stage is carried out while being stirred by a hydrothermal treatment of the immersed substrate. In addition, the process satisfies at least one of the following requirements: The crystallization is carried out with a water/silica molar ratio of 66-100, Before the crystallization stage, the porous substrate is pretreated by covering it at the outer periphery, where the zeolite is not desired, with a polytetrafluoroethylene film and by impregnating it with water in the pores where the zeolite is not desired, and the crystallization is conducted with a water/silica molar ratio of 10-100.

Abstract: The invention relates to a process for preparation of a zeolite that is selected from among the ZBM-30, ZSM-48, EU-2 and EU-11 zeolites, comprising the mixing in an aqueous medium of at least one source of at least one element X (Si and/or Ge) and at least one nitrogen-containing organic compound Q. Said nitrogen-containing organic compound Q is selected from among the compounds comprising at least one ether group and two terminal ammonium groups and their precursors.