Abstract: Provided are: a spherical magnesium oxide having not only high sphericity but also smooth surface and having excellent moisture resistance and excellent filling properties, and a method producing the same. In the present invention, by controlling the boron and iron contents of the calcined magnesium oxide to be in the respective predetermined ranges, there is provided a spherical magnesium oxide having a volume-based cumulative 50% particle diameter (D50), as measured by a laser diffraction/scattering particle size distribution measurement, in the range of from 3 to 200 ?m, which is the range for a relatively large particle diameter, and a high sphericity of 1.00 to 1.20, as measured from viewing a SEM photomicrograph, as well as smooth surface, and having excellent moisture resistance and excellent filling properties. A predetermined spherical magnesium oxide is provided by virtue of the synergies obtained from the boron content of 300 to 2,000 ppm and the iron content of 100 to 1,500 ppm.

Abstract: Provided are: a spherical magnesium oxide having not only high sphericity but also smooth surface and having excellent moisture resistance and excellent filling properties, and a method producing the same. In the present invention, by controlling the boron and iron contents of the calcined magnesium oxide to be in the respective predetermined ranges, there is provided a spherical magnesium oxide having a volume-based cumulative 50% particle diameter (D50), as measured by a laser diffraction/scattering particle size distribution measurement, in the range of from 3 to 200 ?m, which is the range for a relatively large particle diameter, and a high sphericity of 1.00 to 1.20, as measured from viewing a SEM photomicrograph, as well as smooth surface, and having excellent moisture resistance and excellent filling properties. A predetermined spherical magnesium oxide is provided by virtue of the synergies obtained from the boron content of 300 to 2,000 ppm and the iron content of 100 to 1,500 ppm.

Abstract: A metal hydroxide solid solution and a metal oxide solid solution, wherein the crystal form is an octahedron comprising upper and lower parallel basal planes and six peripheral pyramidal planes, the pyramidal planes consisting of upward-inclined planes and downward-inclined planes which are alternatively located. The ratio of the major axis diameter of the basal plane to the thickness between the upper and lower basal planes (major axis diameter/thickness) if 1 to 9. This improves fluidity, processability and the like when the solid solutions are kneaded into resins and the like.