Abstract: An automotive component is produced by hot forming and press hardening a hardenable steel alloy having a tensile strength of at least 1700 MPa. The hardenable steel alloy, in addition to a balance made up of iron and melting-related impurities, has the following alloy elements carbon, niobium, and titanium. The automotive component is coated by a thermal coating process.

Abstract: A vehicle door includes a window frame and a lower surface portion formed jointly with the window frame in one piece from a hot formed and press hardened sheet metal plate which is made of a steel alloy which includes, in weight-%: Carbon 0.33-0.38, Silicon 0.2-0.7, Manganese 0.7-1.2, Phosphorus max. 0.03, Sulfur max. 0.02, Boron 0.002-0.005, Chromium 0.6-1.0, Copper max. 0.12, Nitrogen max. 0.005, Titanium 0.015-0.025, Nickel 1.5-2.0, Molybdenum 0.2-0.6, Tin max. 0.04, and as optional components Aluminum 0.006-0.08, Niobium 0.02-0.05, with a balance being iron and incidental impurities. At least the lower surface portion has a Brinell hardness of 500 to 600 HB and a yield strength of 1,200 to 1,450 MPa, wherein the lower surface portion and/or the window frame has a wall thickness of at least 6 mm.

Abstract: A motor vehicle component and a method of manufacturing thereof is disclosed having at least regionally high-strength and at the same time ductile properties, including providing a sheet metal blank composed of a hardenable steel alloy with at least 0.25% carbon fraction, at least partially heating the sheet metal blank to above austenitizing temperature, in less than 20 seconds, hot-forming and press-hardening the sheet metal blank, in the process, setting a tensile strength Rm of greater than 1800 MPa and an elongation at break A20 of greater than 6%.

Abstract: A vehicle door includes a window frame and a lower surface portion formed jointly with the window frame in one piece from a hot formed and press hardened sheet metal plate which is made of a steel alloy which includes, in weight-%: Carbon 0.33-0.38, Silicon 0.2-0.7, Manganese 0.7-1.2, Phosphorus max. 0.03, Sulfur max. 0.02, Boron 0.002-0.005, Chromium 0.6-1.0, Copper max. 0.12, Nitrogen max. 0.005, Titanium 0.015-0.025, Nickel 1.5-2.0, Molybdenum 0.2-0.6, Tin max. 0.04, and as optional components Aluminum 0.006-0.08, Niobium 0.02-0.05, with a balance being iron and incidental impurities. At least the lower surface portion has a Brinell hardness of 500 to 600 HB and a yield strength of 1,200 to 1,450 MPa, wherein the lower surface portion and/or the window frame has a wall thickness of at least 6 mm.

Abstract: An automotive component is produced by hot forming and press hardening a hardenable steel alloy having a tensile strength of at least 1700 MPa. The hardenable steel alloy, in addition to a balance made up of iron and melting-related impurities, has the following alloy elements carbon, niobium, and titanium. The automotive component is coated by a thermal coating process.

Abstract: The present invention relates to a method of producing a motor vehicle component and to a motor vehicle component. Said motor vehicle component is produced by means of hot forming and press hardening. A blank is heated in a continuous furnace with supply of nitrogen. This produces a skin-decarburized layer on the blank that achieves ductility in a motor vehicle component produced with ultrahigh strength.

Abstract: A motor vehicle component and a method of manufacturing thereof is disclosed having at least regionally high-strength and at the same time ductile properties, including providing a sheet metal blank composed of a hardenable steel alloy with at least 0.25% carbon fraction, at least partially heating the sheet metal blank to above austenitizing temperature, in less than 20 seconds, hot-forming and press-hardening the sheet metal blank, in the process, setting a tensile strength Rm of greater than 1800 MPa and an elongation at break A20 of greater than 6%.

Abstract: An armoring part for a vehicle includes a steel plate made of at least partially hot formed and press hardened armor steel and having a hardness of 380 to 760 Vickers (HV). Applied on at least one side of the steel plate is a coat which is made of a metal material which is softer than a metal material of the armor steel. The coat is a thermally applied layer and has a hardness of 10 to 230 Vickers (HV).