Abstract: A novel sulfanilamide containing epoxy resin composition capable of fast curing without negative impact on glass transition temperature or mechanical performance.

Abstract: A two-component curable epoxy resin system including a dye solution. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol. The system also includes a hardener mixture containing mainly polyethylene tetraamines. The system includes triethylene diamine in specific amounts as a catalyst. The system has beneficial curing characteristics with desired color that make it useful for producing fiber-reinforced composites in a resin transfer molding process.

Abstract: A two-component curable epoxy resin system including a dye solution. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol. The system also includes a hardener mixture containing mainly polyethylene tetraamines. The system includes triethylene diamine in specific amounts as a catalyst. The system has beneficial curing characteristics with desired color that make it useful for producing fiber-reinforced composites in a resin transfer molding process.

Abstract: Fiber reinforced epoxy resin composites are produced using a specific epoxy resin system. The epoxy resin system contains at least one polyglycidyl ether of a polyphenol. The system also contains a hardener that contains a mixture of aminocyclohexanealkylamine and polyalkylene polyamine hardeners. The ratio of epoxy resin groups to amine hydrogen groups is from 1.05 to 1.50. The epoxy resin system contains a tertiary amine catalyst such as a tertiaryaminophenol, a benzyl tertiary amine or an imidazole compound.

Abstract: A two-component curable epoxy resin system is disclosed. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol. The system also includes a hardener mixture containing mainly polyethylene tetraamines. The system includes one or more of i) alkali metal salts, ii) carboxylic acid-, carboxylic anhydride- or carboxylic acid ester-substituted phenol compounds, iii) an amino as a catalyst. The system has beneficial curing characteristics that make it useful for producing fiber-reinforced composites in a resin transfer molding process.

Abstract: Thermosets are formed by mixing an epoxy resin with a hardener composition that includes a norbornene-based anhydride hardener such as methyl nadic anhydride and a core-shell rubber. The presence of the core-shell rubber unexpectedly reduces the strong odor of that is normally produced in thermosets containing these anhydride hardeners.

Abstract: A two-component curable epoxy resin system is disclosed. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol. The system also includes an hardener mixture containing mainly polyethylene tetraamines. The system include triethylene diamine in specific amounts as a catalyst. The system has beneficial curing characteristics that make it useful for producing fiber-reinforced composites in a resin transfer molding process.

Abstract: A two-component curable epoxy resin system is disclosed. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol that has an epoxy equivalent weight of up to about 200 and contains no more than 2% by weight of monohydrolyzed resin species.

Abstract: A two-component curable epoxy resin system is disclosed. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol. The system also includes a hardener mixture containing mainly polyethylene tetraamines. The system includes one or more of i) alkali metal salts, ii) carboxylic acid-, carboxylic anhydride- or carboxylic acid ester-substituted phenol compounds, iii) an amino as a catalyst. The system has beneficial curing characteristics that make it useful for producing fiber-reinforced composites in a resin transfer molding process.

Abstract: A two-component curable epoxy resin system is disclosed. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol. The system also includes an hardener mixture containing mainly polyethylene tetraamines. The system include triethylene diamine in specific amounts as a catalyst. The system has beneficial curing characteristics that make it useful for producing fiber-reinforced composites in a resin transfer molding process.

Abstract: A two-component curable epoxy resin system is disclosed. The resin system includes an epoxy resin component containing at least 80% by weight of a polyglycidyl ether of a polyphenol that has an epoxy equivalent weight of up to about 200 and contains no more than 2% by weight of monohydrolyzed resin species.

Abstract: Fiber reinforced epoxy resin composites are produced using a specific epoxy resin system. The epoxy resin system contains at least one polyglycidyl ether of a polyphenol. The system also contains a hardener that contains a mixture of aminocyclohexanealkylamine and polyalkylene polyamine hardeners. The ratio of epoxy resin groups to amine hydrogen groups is from 1.05 to 1.50. The epoxy resin system contains a tertiary amine catalyst such as a tertiaryaminophenol, a benzyl tertiary amine or an imidazole compound.

Abstract: Attach a thermoplastic polymeric foam to multiple spaced apart structural support members of a structure wherein the foam has a resistance to water vapor permeability (mu) that is less than 50, a thermal conductivity that is less than 40 milliwatts per meter*Kelvin, a compressive strength that is greater than 80 kilopascals, and a density of 48 kilograms per cubic meter or less to provide insulation while also providing water vapor-permeability and structural durability to the structure.

Abstract: An acoustical insulation foam having, either with or without elastification, an Asker C hardness of less than about 65, a density of about 5 to about 150 kg/m3, a cell size of about 0.

Abstract: An acoustical insulation foam having, either with or without elastification, an Asker C hardness of less than about 65, a density of about 5 to about 150 kg/m3, a cell size of about 0.

Abstract: An acoustical insulation foam having, either with or without elastification, an Asker C hardness of less than about 65, a density of about 5 to about 150 kg/m3, a cell size of about 0.05 to about 15 mm, an open cell content of 0 to about 100 volume percent, a thickness of about 1 to about 200 mm, and a width of about 100 to about 3000 mm; comprising; (A) one or more alkenyl aromatic polymers, (B) one or more substantially random interpolymers and (C) optionally, one or more nucleating agents and (D) optionally, one or more other additives; and (E) one or more blowing agents.

Abstract: An acoustical insulation foam having, either with or without elastification, an Asker C hardness of less than about 65, a density of about 5 to about 150 kg/m3, a cell size of about 0.05 to about 15 mm, an open cell content of 0 to about 100 volume percent, a thickness of about 1 to about 200 mm, and a width of about 100 to about 3000 mm; comprising; (A) one or more alkenyl aromatic polymers, (B) one or more substantially random interpolymers and (C) optionally, one or more nucleating agents and (D) optionally, one or more other additives; and (E) one or more blowing agents.