Abstract: The present invention pertains to a UHMWPE film having a tensile strength of at least 2.0 GPa, a tensile energy to break of at least 30 J/g, an Mw of at least 500 000 gram/mole, and a Mw/Mn ratio of at most 6. The film may be manufactured via a process which comprises subjecting a starting UHMWPE with a weight average molecular weight of at least 500 000 gram/mole, an elastic shear modulus determined directly after melting at 160° C. of at most 0.9 MPa, and a Mw/Mn ratio of at most 6 to a compacting step and a stretching step under such conditions that at no point during the processing of the polymer its temperature is raised to a value above its melting point. The film may be used as starting material in any applications where high tensile strength and high energy to break are important. Suitable applications include ballistic applications, ropes, cables, nets, fabrics, and protective applications.

Abstract: A process for manufacturing a film of ultra-high molecular weight polyolefin includes (a) feeding an ultra-high molecular weight polyethylene with a weight average molecular weight of at least 500,000 gram/mole as a powder having a bulk density below 0.5 g/cm3 to a compaction zone of an isobaric double belt press; (b) subjecting the ultra-high molecular weight polyethylene powder in the compaction zone to an isobaric pressure to form a single layer sheet of compacted polyethylene at a temperature that is below the melting point of the polyethylene under process conditions and that is maintained within a temperature window of 2° C.; and (c) subjecting the sheet of compacted polyethylene to a rolling step and at least one stretching step at a temperature below the melting point of the polyethylene under process conditions.

Abstract: A process for manufacturing high molecular weight polyethylene fibers, including subjecting a polyethylene tape with a weight average molecular weight of at least 500,000 grams/mole, a Mw/Mn ratio of at most 6, and a 200/110 uniplanar orientation parameter of at least 3 to a force in the direction of the thickness of the tape over the entire width of the tape. A polyethylene fiber having a Mw of at least 500 000 gram/mole, a Mw/Mn ratio of at most 6, and a 020 uniplanar orientation value of at most 55°.

Abstract: A process for manufacturing a film of ultra-high molecular weight polyolefin comprising: (a) subjecting a starting ultra-high molecular weight polyolefin with a weight average molecular weight of at least 500 000 gram/mole in powder form to a compacting step using an isobaric press; and (b) subjecting the compacted polyolefin to a rolling step and at least one stretching step under such conditions that at no point during the processing of the polymer its temperature is raised to a value above its melting point. The process allows for the manufacture of ultra-high molecular weight polyolefin films of high quality.

Abstract: A process for manufacturing high molecular weight polyethylene fibers, including subjecting a polyethylene tape with a weight average molecular weight of at least 500,000 grams/mole, a Mw/Mn ratio of at most 6, and a 200/110 uniplanar orientation parameter of at least 3 to a force in the direction of the thickness of the tape over the entire width of the tape. A polyethylene fiber having a Mw of at least 500 000 gram/mole, a Mw/Mn ratio of at most 6, and a 020 uniplanar orientation value of at most 55°.

Abstract: A process for manufacturing a film of ultra-high molecular weight polyolefin comprising: (a) subjecting a starting ultra-high molecular weight polyolefin with a weight average molecular weight of at least 500 000 gram/mole in powder form to a compacting step using an isobaric press: and (b) subjecting the compacted polyolefin to a rolling step and at least one stretching step under such conditions that at no point during the processing of the polymer its temperature is raised to a value above its melting point. The process allows for the manufacture of ultra-high molecular weight polyolefin films of high quality.

Abstract: Ballistic-resistant moulded article comprising a compressed stack of sheets comprising tapes of a reinforcing material, characterised in that at least one sheet comprises woven tapes as weft and as warp, at least some of the tapes having a width of at least 10 mm. A method for manufacturing the ballistic-resistant moulded article is also claimed.