Abstract: A squeezable tubular container (a) which is formed from a composition containing a polyethylene having a density of 0.900 to 0.975 g/cm.sup.3 and an ethylene/.alpha.-olefin copolymer having a density smaller than 0.900 g/cm.sup.3, (b) has a crosslinking caused under irradiation with electron beam, and (c) is sterilizable at a high temperature or is heat-sealable or ultrasonically sealable; and a process for the production thereof.

Abstract: A squeezable tubular container (a) which is formed from a composition containing a polyethylene having a density of 0.900 to 0.975 g/cm.sup.3 and an ethylene/.alpha.-olefin copolymer having a density smaller than 0.900 g/cm.sup.3, (b) has a crosslinking caused under irradiation with electron beam, and (c) is sterilizable at a high temperature or is heat-sealable or ultrasonically sealable; and a process for the production thereof.

Abstract: A process for producing polypropylene, which comprises preliminarily polymerizing 3-methylbutene-1 in the presence of a catalyst system formed from[A] a solid titanium catalyst component containing magnesium, titanium, halogen and polycarboxylic acid esters as essential components,[B] an organoaluminum compound, and[C] an organosilicon compound represented by the general formula R.sub.n Si(OR').sub.4-n wherein R and R' represent a hydrocarbon group, and 0<n<4, the amount of the 3-methylbutene-1 preliminarily polymerized being 0.1 to 100 g per gram of the solid titanium catalyst, and thereafter, polymerizing propylene or copolymerizing propylene and an alpha-olefin in the presence of the catalyst used in the preliminary polymerization to such an extent that the amount of the monomer or monomers polymerized is from 1,000 to 100,000 times the amount of the 3-methylbutene-1 preliminarily polymerized.

Abstract: A process for producing polypropylene, which comprises preliminarily polymerizing 3-methylbuten3-1 in the presence of a catalyst system formed from[A] a solid titanium catalyst component containing magnesium, titanium, halogen and polycarboxylic acid esters as essential components,[B] an organoaluminum compound, and[C] an organosilicon compound represented by the general formula R.sub.n Si(OR').sub.4-n wherein R and R' represent a hydrocarbon group, and 0<n<4, the amount of the 3-methylbutene-1 preliminarily polymerized being 0.1 to 100 g per gram of the solid titanium catalyst, and thereafter, polymerizing propylene or copolymerizing propylene and an alpha-olefin in the presence of the catalyst used in the preliminary polymerization to such an extent that the amount of the monomer or monomers polymerized is from 1,000 to 100,000 times the amount of the 3-methylbutene-1 preliminarily polymerized.

Abstract: A film-forming propylene copolymer composed of a major amount of propylene and a minor amount of ethylene, characterized by having(A) an ethylene content (Ec) of from 0.1 mole % to 2.0 mole % based on the total amount of propylene and ethylene, and(B) an isotactic value (Iso) in the range represented by the following formula (1) or (2),(i) when 0.1.ltoreq.Ec.ltoreq.0.3,Iso.gtoreq.-5Ec30 96.3 (%) (1),and(ii) when 0.3<Ec.ltoreq.2.0,Iso.gtoreq.-0.67Ec30 95.0 (%) (2)wherein Ec0 represents the numerical value of Ec (mole %);a film of the copolymer; and a process for producing the film.