Abstract: Improved catalyst supports, supported catalyst, and method of preparing and using the catalysts for the hydrodesulfurization of a residuum hydrocarbon feedstock are disclosed. The catalyst supports comprise titania alumina having 5 wt % or less titania and have greater than 70% of their pore volume in pores having a diameter between 70 ? and 130 ? and less than 2% in pores having a diameter above 1000 ?. Catalysts prepared from the supports contain Groups 6, 9 and 10 metals or metal compounds, and optionally phosphorus, supported on the titania alumina supports. Catalysts in accordance with the invention exhibit improved sulfur and MCR conversion in hydrotreating processes.

Abstract: Improved catalyst supports, supported catalyst, and method of preparing and using the catalysts for the hydrodesulfurization of a residuum hydrocarbon feedstock are disclosed. The catalyst supports comprise titania alumina having 5 wt % or less titania and have greater than 70% of their pore volume in pores having a diameter between 70 ? and 130 ? and less than 2% in pores having a diameter above 1000 ?. Catalysts prepared from the supports contain Groups 6, 9 and 10 metals or metal compounds, and optionally phosphorus, supported on the titania alumina supports. Catalysts in accordance with the invention exhibit improved sulfur and MCR conversion in hydrotreating processes.

Abstract: The process of this invention removes impurities from transesterification products comprising primarily fatty acid alkyl esters (FAAE) that are being processed for final fuel products, such as biodiesel. The inventive process is catalytic, and the resulting ester is suitable for use as biodiesel. Metal oxide and mixed metal oxide catalysts are particularly suitable. The invention is particularly suitable for treating fatty acid alkyl ester compositions comprising impurities such as glycerin, sterol glycosides, and/or triglyceride, diglyceride and/or monoglyceride. The invention is particularly useful in treating FAAE transesterification products made using homogeneous alkali catalysts. The treated ester exhibits improved performance under cold weather conditions, which can be measured by methods such as ASTM 7501 Cold Soak Filtration Test (CSFT).

Abstract: Improved catalyst supports, supported catalyst, and method of preparing and using the catalysts for the hydrodesulfurization of a residuum hydrocarbon feedstock are disclosed. The catalyst supports comprise titania alumina having 5 wt % or less titania and have greater than 70% of their pore volume in pores having a diameter between 70 ? and 130 ? and less than 2% in pores having a diameter above 1000 ?. Catalysts prepared from the supports contain Groups 6, 9 and 10 metals or metal compounds, and optionally phosphorus, supported on the titania alumina supports. Catalysts in accordance with the invention exhibit improved sulfur and MCR conversion in hydrotreating processes.

Abstract: Improved catalyst supports, supported catalyst, and method of preparing and using the catalysts for the hydrodesulfurization of a residuum hydrocarbon feedstock are disclosed. The catalyst supports comprise titania alumina having 5 wt % or less titania and have greater than 70% of their pore volume in pores having a diameter between 70 ? and 130 ? and less than 2% in pores having a diameter above 1000 ?. Catalysts prepared from the supports contain Groups 6, 9 and 10 metals or metal compounds, and optionally phosphorus, supported on the titania alumina supports. Catalysts in accordance with the invention exhibit improved sulfur and MCR conversion in hydrotreating processes.

Abstract: Improved catalyst supports, supported catalyst, and method of preparing and using the catalysts for the hydrodesulfurization of a residuum hydrocarbon feedstock are disclosed. The catalyst supports comprise titania alumina having 5 wt % or less titania and have greater than 70% of their pore volume in pores having a diameter between 70 and 130 and less than 2% in pores having a diameter above 1000. Catalysts prepared from the supports contain Groups 6, 9 and 10 metals or metal compounds, and optionally phosphorus, supported on the titania alumina supports. Catalysts in accordance with the invention exhibit improved sulfur and MCR conversion in hydrotreating processes.

Abstract: Improved catalyst supports, supported catalyst, and method of preparing and using the catalysts for the hydrodesulfurization of a residuum hydrocarbon feedstock are disclosed. The catalyst supports comprise titania alumina having 5 wt % or less titania and have greater than 70% of their pore volume in pores having a diameter between 70 and 130 and less than 2% in pores having a diameter above 1000. Catalysts prepared from the supports contain Groups 6, 9 and 10 metals or metal compounds, and optionally phosphorus, supported on the titania alumina supports. Catalysts in accordance with the invention exhibit improved sulfur and MCR conversion in hydrotreating processes.

Abstract: The process of this invention removes impurities from transesterification products comprising primarily fatty acid alkyl esters (FAAE) that are being processed for final fuel products, such as biodiesel. The inventive process is catalytic, and the resulting ester is suitable for use as biodiesel. Metal oxide and mixed metal oxide catalysts are particularly suitable. The invention is particularly suitable for treating fatty acid alkyl ester compositions comprising impurities such as glycerin, sterol glycosides, and/or triglyceride, diglyceride and/or monoglyceride. The invention is particularly useful in treating FAAE transesterification products made using homogeneous alkali catalysts. The treated ester exhibits improved performance under cold weather conditions, which can be measured by methods such as ASTM 7501 Cold Soak Filtration Test (CSFT).