Abstract: A method of assembling aluminum alloy products, such as sheets, strips or tubes, by means of fluxless brazing, where the absence of flux is made possible by using a prior treatment resulting in formation of a conversion layer on the surface of the products. The treatment involves using a solution containing K+ and F? ions and at least one acid in a quantity such that the pH of the solution is less than 3. The inventive method enables effective flux was brazing in industrial conditions, such as a for the production of heat exchangers used in motor vehicles.

Abstract: A method of assembling aluminum alloy products, such as sheets, strips or tubes, by means of fluxless brazing, where the absence of flux is made possible by using a prior treatment resulting in formation of a conversion layer on the surface of the products. The treatment involves using a solution containing K+ and F? ions and at least one acid in a quantity such that the pH of the solution is less than 3. The inventive method enables effective flux was brazing in industrial conditions, such as a for the production of heat exchangers used in motor vehicles.

Abstract: The invention relates to a process to manufacture a clad strip, preferably <1.5 mm thick, intended for the manufacture of brazed heat exchangers, comprising: casting a plate of core alloy comprising (% by weight): Si<0.8, Fe<0.8, Cu 0.2-0.9, Mn 0.7-1.5, Mg<0.4, Zn<0.2, Ti<0.1, other elements <0.05 each and <0.15 in total, the remainder aluminum, homogenizing the plate between 550 and 630° C. for at least one hour, cladding one or two sides of the plate with a brazing aluminum alloy, preferentially containing 5 to 13% silicon, hot rolling followed by cold rolling of the plate to a thickness close to a final desired thickness, recrystallization annealing of the strip between 300 and 4000 C., strain hardening of the annealed strip to obtain a permanent deformation between 2 and 10% and to obtain the desired final thickness.

Abstract: The invention relates to a process to manufacture a clad strip, <1.5 mm thick, intended for the manufacture of brazed heat exchangers, comprising: casting of a plate made of core alloy composed as follows (o by weight): Si<0.8 Fe<0.8 Cu: 0.2-0.9 Mn: 0.7-1.5 Mg<0.4 Zn<0.2 Ti<0.1 other elements <0.05 each and <0.15 in total, the remainder aluminum, homogenization of said plate between 550 and 630° C. for at least one hour, cladding on one or two sides of said blank of a brazing aluminum alloy, preferentially containing 5 to 13% silicon, hot rolling followed by cold rolling of the plated blank to a thickness close to the final thickness, recrystallization annealing of the strip between 300 and 4000C., strain hardening of the annealed strip to obtain a permanent deformation between 2 and 10% and the final thickness.

Abstract: The invention relates to a process to manufacture a clad strip, preferably <1.

Abstract: The invention relates to a process to manufacture a clad strip, <1.