Abstract: A method for producing a cermet composition, including mixing a first predetermined amount of a yttria stabilized zirconia powder with between 2 and 8 weight percent mu-metal powder to define a homogeneous admixture, oxidizing the mu-metal in the admixture, forming the homogeneous admixture into a green body, calcining the green body in a first reducing atmosphere to remove oxygen from the oxidized mu-metal to yield a calcined body, and sintering the calcined body in a second reducing atmosphere to yield a densified body having no more than 0.8% porosity. The densified body has a plurality of mu-metal particles distributed therethrough, a hardness of at least 1450 HV, flexural strength of at least 200 kPSI, and a relative permeability ?/?o of at least 850.

Abstract: A method for producing a metal detectible ceramic, including mixing a first amount of ceramic material with a second metal oxide to define an admixture, forming the admixture into a green body, sintering the green body to yield a densified body, wherein the densified body has a plurality of metallic particles distributed therethrough, and wherein the densified body is detectible by a metal detector.

Abstract: A method for producing a cermet composition, including mixing a first predetermined amount of a yttria stabilized zirconia powder with between 2 and 8 weight percent mu-metal powder to define a homogeneous admixture, oxidizing the mu-metal in the admixture, forming the homogeneous admixture into a green body, calcining the green body in a first reducing atmosphere to remove oxygen from the oxidized mu-metal to yield a calcined body, and sintering the calcined body in a second reducing atmosphere to yield a densified body having no more than 0.8% porosity. The densified body has a plurality of mu-metal particles distributed therethrough, a hardness of at least 1450 HV, flexural strength of at least 200 kPSI, and a relative permeability ?/?o of at least 850.

Abstract: A cermet catalyst material, including a spinel matrix defining a spinel grain and a plurality metal particles embedded in and on the surface of the spinel grain. When the spinel grain is in a first oxidizing atmosphere and at a temperature above about 800 degrees Celsius the metal particles are absorbed into the spinel matrix in the form of metal cations. When the grain is in an second, less oxidizing atmosphere and at a temperature below about 1100 degrees Celsius the metal cations emerge from the spinel matrix to yield a plurality of metal particles adhering to the spinel grain or residing in intragranular pores.

Abstract: A cermet catalyst material, including a spinel matrix defining a spinel grain and a plurality metal particles embedded in and on the surface of the spinel grain. When the spinel grain is in a first oxidizing atmosphere and at a temperature above about 800 degrees Celsius the metal particles are absorbed into the spinel matrix in the form of metal cations. When the grain is in an second, less oxidizing atmosphere and at a temperature below about 1100 degrees Celsius the metal cations emerge from the spinel matrix to yield a plurality of metal particles adhering to the spinel grain or residing in intragranular pores.

Abstract: A method for producing a metal detectible ceramic, including mixing a first amount of ceramic material with a second metal oxide to define an admixture, forming the admixture into a green body, sintering the green body to yield a densified body, wherein the densified body has a plurality of metallic particles distributed therethrough, and wherein the densified body is detectible by a metal detector.

Abstract: A cermet catalyst material, including a spinel matrix defining a spinel grain and a plurality metal particles embedded in the surface of the spinel grain. When the spinel grain is in an first oxidizing atmosphere and at a temperature above about 800 degrees Celsius the metal particles are absorbed into the spinel matrix. When the grain is in an second, less oxidizing atmosphere and at a temperature below about 1100 degrees Celsius the metal particles emerge from the spinel matrix to yield a plurality of metal particles adhering to the spinel grain or residing in intragranular pores.