Abstract: Provided are a thermoplastic polymer capable of reducing a dielectric dissipation factor in high frequency bands and a film thereof. The thermoplastic liquid crystal polymer includes repeating units represented by the following formulae (I), (II), (III) and (IV), in which a molar ratio of a total amount of the repeating units represented by formulae (I) and (II) to a total amount of all the repeating units in the thermoplastic liquid crystal polymer is 50 to 90 mol %, and a molar ratio of the repeating unit represented by formula (III) to the repeating unit represented by formula (IV) is the former/the latter=23/77 to 77/23.

Abstract: Provided are a thermoplastic polymer capable of reducing a dielectric dissipation factor in high frequency bands and a film thereof. The thermoplastic liquid crystal polymer includes repeating units represented by the following formulae (I), (II), (III) and (IV), in which a molar ratio of a total amount of the repeating units represented by formulae (I) and (II) to a total amount of all the repeating units in the thermoplastic liquid crystal polymer is 50 to 90 mol %, and a molar ratio of the repeating unit represented by formula (III) to the repeating unit represented by formula (IV) is the former/the latter=23/77 to 77/23.

Abstract: A method of manufacturing a biaxially stretched film according by: (I) preheating a thermoplastic resin film to a temperature in a rubbery plateau region in a storage elastic modulus curve; (II) biaxially stretching the thermoplastic resin film under a condition that a stretching speed is 500%/min or higher while heating the thermoplastic resin film to the temperature in the rubbery plateau region; (III) cooling the thermoplastic resin film after the biaxially stretching (II) to a temperature in a glass-to-rubber transition region or a glass region in the storage elastic modulus curve; and (IV) relaxing the thermoplastic resin film after the cooling (III) at a temperature in the glass-to-rubber transition region.

Abstract: The present invention provides a method of manufacturing a biaxially stretched film which exhibits small heat shrinkage and has excellent dimensional stability. An unstretched thermoplastic resin film composed of at least one thermoplastic resin layer is biaxially stretched in a longitudinal direction and a width direction to manufacture the biaxially stretched film.

Abstract: It is an object of the present invention to provide an aqueous ethylene-vinyl alcohol-based copolymer dispersion which is excellent in long-term storage stability and in film-forming properties even when subjected to low-temperature or short-time drying or applied to give thick coats and can give coatings showing high gas barrier performance. The prevent invention is an aqueous ethylene/vinyl alcohol-based copolymer dispersion, which comprises: (A) an ethylene/vinyl alcohol-based copolymer with an ethylene content of 15-65 mole percent and a degree of saponification of not lower than 80 mole percent, (B) a base-neutralized ethylene/?,?-unsaturated carboxylic acid-based copolymer and (C) a polyvinyl alcohol with a degree of saponification of 75-100 mole percent and a degree of polymerization of 100-3500, the content of the polyvinyl alcohol (C) being 0.5-100 parts by weight per 100 parts by weight of the ethylene/vinyl alcohol-based copolymer (A).

Abstract: Provided is a gas barrier film including a layer of a resin composition (C) on at least one side of a substrate (D), wherein the resin composition (C) contains a water soluble or water dispersible polymer (A) and a swellable inorganic layered silicate (B), where the swellable inorganic layered silicate (B) satisfying expressions (1) and (2) below is used. 11.0?D?2.0 ?m (1), ??1.8 ?m (2), wherein D and a are a logarithmic average particle diameter of the swellable inorganic layered silicate (B) measured by laser diffraction and standard deviation of a particle size distribution thereof, respectively. This provides a gas barrier film including a resin composition layer, with a swellable inorganic layered silicate dispersed therein, having an extremely excellent gas barrier property and a method of producing a multilayer barrier film having the resin composition layer with extremely less irregularities on a surface thereof.

Abstract: It is an object of the present invention to provide an aqueous ethylene-vinyl alcohol-based copolymer dispersion which is excellent in long-term storage stability and in film-forming properties even when subjected to low-temperature or short-time drying or applied to give thick coats and can give coatings showing high gas barrier performance. The prevent invention is an aqueous ethylene/vinyl alcohol-based copolymer dispersion, which comprises: (A) an ethylene/vinyl alcohol-based copolymer with an ethylene content of 15-65 mole percent and a degree of saponification of not lower than 80 mole percent, (B) a base-neutralized ethylene/?,?-unsaturated carboxylic acid-based copolymer and (C) a polyvinyl alcohol with a degree of saponification of 75-100 mole percent and a degree of polymerization of 100-3500, the content of the polyvinyl alcohol (C) being 0.5-100 parts by weight per 100 parts by weight of the ethylene/vinyl alcohol-based copolymer (A).