Abstract: An in-vehicle lithium ion battery member produced by molding a resin composition containing (a) a polyphenylene ether resin, the resin composition having a critical strain in a chemical resistance evaluation of 0.5% or more and a Charpy impact strength at 23° C. of 20 kJ/m2 or more.

Abstract: The present disclosure is directed to provide a reinforced resin composition excellent in mechanical strength at elevated temperatures and a molded product including such a reinforced resin composition. A reinforced resin composition of the present disclosure includes (A) a polyamide; (B) a polyamide; (C) a polyphenylene ether; and (D) an inorganic filler, wherein a mass ratio of the component (C) with respect to 100 parts by mass of a sum of the component (A), the component (B), and the component (C) is from 20 to 50 parts by mass, ?HTcMt is 10 J/g or more, and ?HMpMt is 35 J/g or less.

Abstract: A resin composition containing (a) a polyphenylene ether resin, (b) a polypropylene resin, (c) a compatibilizer, (d) an inorganic filler, and (e) a hydrotalcite-like compound, and a molded product obtained by molding the resin composition.

Abstract: A resin composition of the present disclosure comprises (a) a polyphenylene ether resin; and (b) a graft copolymer wherein 30 to 70% by mass of an ethylene-?-olefin copolymer rubber latex having a gel content ratio of 30 to 90% by mass and a volume average particle diameter of a rubber dispersion of 0.2 to 1.0 ?m is graft-polymerized with 30 to 70% by mass of an aromatic vinyl compound, wherein the (a) component forms a continuous phase.

Abstract: An in-vehicle lithium ion battery member produced by molding a resin composition containing (a) a polyphenylene ether resin, the resin composition having a critical strain in a chemical resistance evaluation of 0.5% or more and a Charpy impact strength at 23° C. of 20 kJ/m2 or more.

Abstract: Provided is a polyphenylene ether resin composition having excellent heat aging resistance and fluidity. A polyphenylene ether includes at least one structural unit selected from chemical formulae (1), (2), and (3).

Abstract: Provided is a polyphenylene ether flame-retardant resin composition having excellent flame retardance and long-term flame retardance. The flame-retardant resin composition contains: (A) a resin including (A-1) a polyphenylene ether; and (B) a flame retardant. The (A-1) component has a content of 50 mass % or more when the flame-retardant resin composition minus ash content, corresponding to a residue obtained upon burning of the flame-retardant resin composition, is taken to be 100 mass %. A shaped article of 12.6 cm in length, 1.3 cm in width, and 1.6 mm in thickness formed from the flame-retardant resin composition exhibits a rate of change of chloroform-insoluble content of 15 mass % or less through aging in which the shaped article is left for 1,000 hours at 150° C. in an atmospheric air.

Abstract: A resin composition of the present disclosure comprises (a) a polyphenylene ether resin; and (b) a graft copolymer wherein 30 to 70% by mass of an ethylene-?-olefin copolymer rubber latex having a gel content ratio of 30 to 90% by mass and a volume average particle diameter of a rubber dispersion of 0.2 to 1.0 ?m is graft-polymerized with 30 to 70% by mass of an aromatic vinyl compound, wherein the (a) component forms a continuous phase.

Abstract: Provided are a resin composition and a shaped product having excellent smoke generation properties and chemical resistance. The resin composition and the shaped product contain: a polyphenylene ether resin (I); a polypropylene resin (II); a hydrogenated block copolymer (III) that is a hydrogenated product of a block copolymer including a polymer block A and a polymer block B in which the total amount of vinyl bonding is 30-90%; and a phosphate ester compound (IV). Relative to 100 parts by mass, in total, of components (I) and (II), component (I) is 40-99 parts by mass, component (II) is 1-60 parts by mass, component (III) is 1-20 parts by mass, and component (IV) is 5-45 parts by mass. A partition ratio of component (IV) present in a fraction that dissolves in chloroform and component (IV) present in a fraction that dissolves in o-dichlorobenzene is 10 or more.

Abstract: Provided are a resin composition and a shaped product having excellent smoke generation properties and chemical resistance. The resin composition and the shaped product contain: a polyphenylene ether resin (I); a polypropylene resin (II); a hydrogenated block copolymer (III) that is a hydrogenated product of a block copolymer including a polymer block A and a polymer block B in which the total amount of vinyl bonding is 30-90%; and a phosphate ester compound (IV). Relative to 100 parts by mass, in total, of components (I) and (II), component (I) is 40-99 parts by mass, component (II) is 1-60 parts by mass, component (III) is 1-20 parts by mass, and component (IV) is 5-45 parts by mass. A partition ratio of component (IV) present in a fraction that dissolves in chloroform and component (IV) present in a fraction that dissolves in o-dichlorobenzene is 10 or more.

Abstract: Provided is a flame retardant resin composition excellent in flame retardance, and surface smoothness, appearance, flame retardance and electrical properties after a long-term thermal aging (e.g. 150° C., 500 hours) while maintaining mechanical and electrical properties. The disclosed flame retardant resin composition is a flame retardant resin composition containing a polyphenylene ether, in which, based on UL94 flammability test, an average burning time of a molded product having a length of 12.6 cm, a width of 1.3 cm and a thickness of 1.6 mm formed of the flame retardant resin composition before and after the aging processing in which the molded product is left to stand at 150° C. for 1000 hours under the atmospheric pressure is within 10 seconds, and a change rate of chloroform-insoluble component of the molded product before and after the aging processing is 15 mass % or less.

Abstract: The thermoplastic resin composition contains (A) a polyamide, (B) a polyphenylene ether, and (C) a compatibilizer. When the thermoplastic resin composition is molded into a specimen, a continuous phase containing the polyamide (A) and a dispersed phase containing the polyphenylene ether (B) are formed in the specimen, and E-20 represents a mean ellipticity of the dispersed phase in region I extending from a surface of the hinge portion to a depth of 20 ?m in the thickness direction, and E-mid represents a mean ellipticity of the dispersed phase in region II extending from a distance, measured along the thickness direction from the surface, equal to 48% of the thickness to a distance, measured along the thickness direction from the surface, equal to 52% of the thickness, the following formula (1) is satisfied: 4.0?(E-20)/(E-mid)??(1).

Abstract: A method of manufacturing a resin composition is provided. The resin composition includes: 100 parts by mass in total of (A) polypropylene-based resin and (B) polyphenylene ether resin; 1 part to 20 parts by mass of (C) an admixture; and 0.01 parts to 0.5 parts by mass of (D) one or more compounds selected from the group consisting of a higher fatty acid, a higher fatty acid metal salt, and a higher fatty acid ester. A proportion XD(B+C) of the component (D) present in a whole fraction of 100 mass % dissolved in the chloroform is 0.13 mass % to 0.80 mass %. The method includes a step of melt-kneading the whole component (B), the whole component (C), and 15 mass % to 100 mass % of the component (D) to obtain kneaded material, and a step of adding the whole component (A) and the rest of the component (D).

Abstract: Provided is a polyphenylene ether flame-retardant resin composition having excellent flame retardance and long-term flame retardance. The flame-retardant resin composition contains: (A) a resin including (A-1) a polyphenylene ether; and (B) a flame retardant. The (A-1) component has a content of 50 mass % or more when the flame-retardant resin composition minus ash content, corresponding to a residue obtained upon burning of the flame-retardant resin composition, is taken to be 100 mass %. A shaped article of 12.6 cm in length, 1.3 cm in width, and 1.6 mm in thickness formed from the flame-retardant resin composition exhibits a rate of change of chloroform-insoluble content of 15 mass % or less through aging in which the shaped article is left for 1,000 hours at 150° C. in an atmospheric air.

Abstract: Provided is a polyphenylene ether resin composition having excellent heat aging resistance and fluidity. A polyphenylene ether includes at least one structural unit selected from chemical formulae (1), (2), and (3).

Abstract: Provided is a pellet that contains a polyphenylene ether resin in a high concentration, is highly suitable for use as a modifier for imparting creep resistance, and has excellent post-molding external appearance. The pellet contains 80 mass % to 99 mass % of a polyphenylene ether resin (I) and 1 mass % to 20 mass % of a hydrogenated block copolymer (II) that is an at least partially hydrogenated product of a block copolymer including a polymer block P of mainly a vinyl aromatic compound and a polymer block Q of mainly a conjugated diene compound in which the total of 1,2-vinyl bond content and 3,4-vinyl bond content is 50% to 95%. No black spot contaminants having a major diameter of greater than 0.7 mm are present on front and rear surfaces of four plates of 90.0 mm×50.0 mm×2.0 mm in size obtained through molding of the pellet.

Abstract: Provided are a resin composition and a shaped product having excellent smoke generation properties and chemical resistance. The resin composition and the shaped product contain: a polyphenylene ether resin (I); a polypropylene resin (II); a hydrogenated block copolymer (III) that is a hydrogenated product of a block copolymer including a polymer block A and a polymer block B in which the total amount of vinyl bonding is 30-90%; and a phosphate ester compound (IV). Relative to 100 parts by mass, in total, of components (I) and (II), component (I) is 40-99 parts by mass, component (II) is 1-60 parts by mass, component (III) is 1-20 parts by mass, and component (IV) is 5-45 parts by mass. A partition ratio of component (IV) present in a fraction that dissolves in chloroform and component (IV) present in a fraction that dissolves in o-dichlorobenzene is 10 or more.

Abstract: Provided is a flame retardant resin composition excellent in flame retardance, and surface smoothness, appearance, flame retardance and electrical properties after a long-term thermal aging (e.g. 150° C., 500 hours) while maintaining mechanical and electrical properties. The disclosed flame retardant resin composition is a flame retardant resin composition containing a polyphenylene ether, in which, based on UL94 flammability test, an average burning time of a molded product having a length of 12.6 cm, a width of 1.3 cm and a thickness of 1.6 mm formed of the flame retardant resin composition before and after the aging processing in which the molded product is left to stand at 150° C. for 1000 hours under the atmospheric pressure is within 10 seconds, and a change rate of chloroform-insoluble component of the molded product before and after the aging processing is 15 mass % or less.

Abstract: A resin composition that has an excellent balance between thermal creep resistance and toughness and from which a molded product with favorable appearance can be obtained is provided. The resin composition includes: 100 parts by mass in total of (A) polypropylene-based resin and (B) polyphenylene ether resin; 1 parts to 20 parts by mass of (C) an admixture; and 0.01 parts to 0.5 parts by mass of (D) one or more compounds selected from the group consisting of a higher fatty acid, a higher fatty acid metal salt, and a higher fatty acid ester, wherein when the resin composition is dissolved in chloroform, a proportion XD(B+C) of the component (D) present in a whole fraction of 100 mass % dissolved in the chloroform is 0.13 mass % to 0.80 mass %.

Abstract: Provided is a resin composition having excellent flame retardance, molding processability, and post-heat aging flame retardance. A flame-retardant resin composition contains: (A) a polyphenylene ether; (B) at least one thermoplastic resin selected from the group consisting of (B-1) a polystyrene resin, (B-2) a polyamide resin, (B-3) a polypropylene resin, and (B-4) a polyphenylene sulfide resin; and (C) a flame retardant. The (A) component has a content of less than 50 mass % when the flame-retardant resin composition minus ash content is taken to be 100 mass %. The flame-retardant resin composition has a flame retardance level of V-0 as measured by a UL 94 vertical burning test. A molded article formed from the flame-retardant resin composition exhibits a rate of change of chloroform-insoluble content of no greater than 15 mass % before and after being subjected to aging in which the molded article is left for 1,000 hours at 150° C. in an atmospheric environment.