Abstract: A method for depositing a first material on a substrate includes providing the substrate in a deposition chamber. A molten body is formed between the substrate and a source of the first material by melting one or more second materials. A flow of the first material is passed through the molten body and from the molten body to the substrate as a vapor flow. An essentially non-expending portion of the molten body comprises an alloy having a melting temperature below a melting temperature of the first material.

Abstract: A method for treating a deposited titanium-base material from an initial condition to a treated condition includes a rapid heating and a rapid cooling. The heating is from a first temperature to a second temperature, the first temperature being below a ? transus and the second temperature being below above the ? transus. The cooling is from the second temperature to a third temperature below an equilibrium ? transus.

Abstract: In accordance with the present invention, a process for repairing metal workpieces, such as turbine engine components, is provided. The process comprises the steps of forming a braze paste containing a first nickel base alloy material containing boron and chromium and a second nickel base alloy material containing chromium and cobalt, applying the brazing paste to an area of the metal workpiece containing at least one crack, and subjecting the workpiece and the brazing paste to a brazing cycle by heating the brazing paste and the workpiece, preferably to a temperature in the range of from 2000 to 2200 degrees Fahrenheit. During the brazing cycle, the brazing paste flows into and fills the at least one crack and thus repairs the metal workpiece.

Abstract: In accordance with the present invention, a process for repairing metal workpieces, such as turbine engine components, is provided. The process comprises the steps of forming a braze paste containing a first nickel base alloy material containing boron and chromium and a second nickel base alloy material containing chromium and cobalt, applying the brazing paste to an area of the metal workpiece containing at least one crack, and subjecting the workpiece and the brazing paste to a brazing cycle by heating the brazing paste and the workpiece, preferably to a temperature in the range of from 2000 to 2200 degrees Fahrenheit. During the brazing cycle, the brazing paste flows into and fills the at least one crack and thus repairs the metal workpiece.