Abstract: A method for preparing hollow nanofibers having carbon as a primary component by contacting a carbon-containing compound with a catalyst at 500 to 1200° C., wherein the catalyst is one of a zeolite exhibiting thermal resistance at 900° C. and, supported thereon, a metal; a metallosilicate zeolite containing a heteroatom except aluminum and silicon and a metal; a supporting material and fine cobalt particles exhibiting a binding energy of a cobalt 2P3/2 electron of 779.3 to 781.0 eV; a supporting material and fine cobalt particles exhibiting a cobalt atom ratio in the surface of the supporting material of 0.1 to 1.5%, as measured by the X-ray photoelectron spectroscopy at 10 kV and 18 mA; a supporting material and fine cobalt particles exhibiting a weight ratio of cobalt to a second metal component of 2.5 or more; and a zeolite having a film form and a metal.

Abstract: A carbon fiber bundle is coated with a sizing agent containing a flexible epoxy resin (A) and an epoxy resin (B) incompatible with the flexible epoxy resin (A) as essential components, wherein the epoxy resin (B) is an aliphatic polyglycidyl ether compound having three or more epoxy groups and an epoxy equivalent of 200 or less. The carbon fiber bundle of this invention provides a carbon fiber reinforced composite excellent in the tensile strength and the compressive strength in the fiber direction and excellent in the tensile strength in the perpendicular direction to the fiber direction and the interlaminar shear strength.

Abstract: The invention provides epoxy resin composition containing, as epoxy resin, the following epoxy resin (a) and epoxy resin (b), solid rubber at a ratio of 1 to 20 parts by weight to 100 parts by weight of the entire epoxy resins, and an aromatic amine as a curing agent and having a glass transition temperature of 160 to 220° C. in form of a cured material after heat curing at 180° C. for 2 hours: (a) an epoxy resin having oxazolidone rings and (b) a glycidylamine type epoxy resin.

Abstract: A method for preparing hollow nanofibers having carbon as a primary component by contacting a carbon-containing compound with a catalyst at 500 to 1200° C., wherein the catalyst is one of a zeolite exhibiting thermal resistance at 900° C. and, supported thereon, a metal; a metallosilicate zeolite containing a heteroatom except aluminum and silicon and a metal; a supporting material and fine cobalt particles exhibiting a binding energy of a cobalt 2P3/2 electron of 779.3 to 781.0 eV; a supporting material and fine cobalt particles exhibiting a cobalt atom ratio in the surface of the supporting material of 0.1 to 1.5%, as measured by the X-ray photoelectron spectroscopy at 10 kV and 18 mA; a supporting material and fine cobalt particles exhibiting a weight ratio of cobalt to a second metal component of 2.5 or more; and a zeolite having a film form and a metal.

Abstract: A cooking oven is provided with a weight detection unit for detecting the weight of a cooking object placed on a turntable. The turntable is movable into and out of a heating chamber associated with the cooking oven by means of a moving unit drivingly connected to the turntable through a lever and connecting rod. A heater and a rotary drive unit for rotating a table upon which the turntable is mounted are controlled according to a signal from the weight detection unit. The cooking oven is also provided with an external input unit for supplying data on the heating operation and on the driving of the turntable. Either manual or automatic operation of moving the turntable back and forth can be selected according to a signal from the external input unit.