Abstract: Disclosed herein is a high-strength hot-rolled steel sheet which is characterized by high strength (in terms of tensile strength at 900 MPa level) and excellent combined formability expressed by balance between strength and ductility [tensile strength (TS)×total elongation (El)] and balance between strength and stretch flangeability [tensile strength (TS)×bore expanding ratio (?)]. The hot-rolled steel sheet contains C: no less than 0.02% and no more than 0.15%, Si: no less than 0.2% and no more than 2.0%, Mn: no less than 0.5% and no more than 2.5%, Al: no less than 0.02% and no more than 0.15%, Cu: no less than 1.0% and no more than 3.0%, Ni: no less than 0.5% and no more than 3.0%, and Ti: no less than 0.03% and no more than 0.5%. (% means mass %) It also has a metallographic structure in longitudinal cross section such that the sum of bainitic ferrite and granular bainitic ferrite accounts for no less than 85% by area.

Abstract: A high-strength hot-rolled steel sheet containing C: 0.05 to 0.15%, Si: no more than 1.50% (excluding 0%), Mn: 0.5 to 2.5%, P: no more than 0.035% (excluding 0%), S: no more than 0.01% (including 0%), Al: 0.02 to 0.15%, and Ti: 0.05 to 0.2%, which is characterized in that its metallographic structure is composed of 60 to 95 vol % of bainite and solid solution-hardened or precipitation-hardened ferrite (or ferrite and martensite) and its fracture appearance transition temperature (vTrs) is no higher than 0° C. as obtained by impact tests (% in terms of % by weight).

Abstract: Disclosed is a high-strength electric resistance welded steel pipe which is manufacture from a steel sheet containing, on mass basis, 0.2% to 0.4% C, 0.05% to 0.5% Si, 0.5% to 2.5% Mn, 0.025% or less P, 0.01% or less S, 0.01% to 0.15% or Al, 0.01% to 2% Cu, 0.05% to 2% Cr, 0.005% to 0.2% Ti, and 0.0002% to 0.005% B, with the remainder being iron and inevitable impurities. The steel pipe has a tensile strength of 1750 N/mm2 or more, a 0.1%-proof stress of 1320 N/mm2 or more, and a Charpy impact value at a testing temperature of minus 40° C. of 50 J/cm2 or more.

Abstract: A high-strength hot-rolled steel sheet containing C: 0.05 to 0.15%, Si: no more than 1.50% (excluding 0%), Mn: 0.5 to 2.5%, P: no more than 0.035% (excluding 0%), S: no more than 0.01% (including 0%), Al: 0.02 to 0.15%, and Ti: 0.05 to 0.2%, which is characterized in that its metallographic structure is composed of 60 to 95 vol % of bainite and solid solution-hardened or precipitation-hardened ferrite (or ferrite and martensite) and its fracture appearance transition temperature (vTrs) is no higher than 0° C. as obtained by impact tests.

Abstract: A high-strength hot-rolled steel sheet containing C: 0.05 to 0.15%, Si: no more than 1.50% (excluding 0%), Mn: 0.5 to 2.5%, P: no more than 0.035% (excluding 0%), S: no more than 0.01% (including 0%), Al: 0.02 to 0.15%, and Ti: 0.05 to 0.2%, which is characterized in that its metallographic structure is composed of 60 to 95 vol % of bainite and solid solution-hardened or precipitation-hardened ferrite (or ferrite and martensite) and its fracture appearance transition temperature (vTrs) is no higher than 0° C. as obtained by impact tests. (% in terms of % by weight).

Abstract: Disclosed herein is a high-strength hot-rolled steel sheet which is characterized by high strength (in terms of tensile strength at 900 MPa level) and excellent combined formability expressed by balance between strength and ductility [tensile strength (TS)×total elongation (El)] and balance between strength and stretch flangeability [tensile strength (TS)×bore expanding ratio (?)]. The hot-rolled steel sheet contains C: no less than 0.02% and no more than 0.15%, Si: no less than 0.2% and no more than 2.0%, Mn: no less than 0.5% and no more than 2.5%, Al: no less than 0.02% and no more than 0.15%, Cu: no less than 1.0% and no more than 3.0%, Ni: no less than 0.5% and no more than 3.0%, and Ti: no less than 0.03% and no more than 0.5%. (% means mass %) It also has a metallographic structure in longitudinal cross section such that the sum of bainitic ferrite and granular bainitic ferrite accounts for no less than 85% by area.

Abstract: A high-strength hot-rolled steel sheet containing C: 0.05 to 0.15%, Si: no more than 1.50% (excluding 0%), Mn: 0.5 to 2.5%, P: no more than 0.035% (excluding 0%), S: no more than 0.01% (including 0%), Al: 0.02 to 0.15%, and Ti: to 0.2%, which is characterized in that its metallographic structure is composed of 60 to 95 vol % of bainite and solid solution-hardened or precipitation-hardened ferrite (or ferrite and martensite) and its fracture appearance transition temperature (vTrs) is no higher than 0° C. as obtained by impact tests.

Abstract: Disclosed is a high-strength electric resistance welded steel pipe which is manufacture from a steel sheet containing, on mass basis, 0.2% to 0.4% C, 0.05% to 0.5% Si, 0.5% to 2.5% Mn, 0.025% or less P, 0.01% or less S, 0.01% to 0.15% or Al, 0.01% to 2% Cu, 0.05% to 2% Cr, 0.005% to 0.2% Ti, and 0.0002% to 0.005% B, with the remainder being iron and inevitable impurities. The steel pipe has a tensile strength of 1750 N/mm2 or more, a 0.1%-proof stress of 1320 N/mm2 or more, and a Charpy impact value at a testing temperature of minus 40° C. of 50 J/cm2 or more.